Warm-mixing high-elastoplasticity bridge expansion joint sealing material and preparation method thereof
A high-elasticity, warm-mixing type technology, applied in building insulation materials, building components, climate change adaptation, etc., can solve the problems of insufficient material elasticity, difficult bridge coordination deformation, high construction requirements, etc., and achieve good high temperature and anti-rutting Ability, viscosity reduction effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0024] Example 1
[0025] A warm-mix high-elasticity modified asphalt, including the following components:
[0026] 70# Road petroleum asphalt: styrene-butadiene block polymer (SBS): styrene butadiene rubber (SBR): resin: stabilizer: warm mixing agent = 100:9:4:4:3:3. The styrene-butadiene block polymer is star-shaped. The resin is petroleum resin. The stabilizer is a mixture of sulfur and TOR rubber stabilizer, and the ratio is: sulfur:TOR=4:1. Said warm mixing agent is Sasobit viscosity reducing agent.
[0027] 1. Put the asphalt in 120℃ for 1 hour and wait until the asphalt is in a liquid state.
[0028] 2. Use electric furnace to heat, set the temperature to 175~180℃, add the weighed styrene-butadiene block polymer (SBS) into the asphalt, and use a high-speed shearing machine for high-speed shearing at a speed of 1500~ 3000r / min, shearing time is 30~45min, then adding SBR for high-speed shearing for 30~60min, adding resin and TOR rubber stabilizer for shearing for 20~30min.
[...
Example Embodiment
[0038] Example 2
[0039] A warm-mix high-elasticity modified asphalt, including the following components:
[0040] 70# Road petroleum asphalt: styrene-butadiene block polymer (SBS): styrene butadiene rubber (SBR): resin: stabilizer: warm mixing agent = 100:5:4:4:3:3. The styrene-butadiene block polymer is star-shaped. The resin is petroleum resin. The stabilizer is a mixture of sulfur and TOR rubber stabilizer, and the ratio is: sulfur:TOR=4:1. Said warm mixing agent is Sasobit viscosity reducing agent.
[0041] 1. Put the asphalt in 120℃ for 1 hour and wait until the asphalt is in a liquid state.
[0042] 2. Use electric furnace to heat, set the temperature to 175~180℃, add the weighed styrene-butadiene block polymer (SBS) into the asphalt, and use a high-speed shearing machine for high-speed shearing at a speed of 1500~ 3000r / min, shearing time is 30~45min, then adding SBR for high-speed shearing for 30~60min, adding resin and TOR rubber stabilizer for shearing for 20~30min.
[...
PUM
Property | Measurement | Unit |
---|---|---|
Softening point | aaaaa | aaaaa |
Extensibility | aaaaa | aaaaa |
Softening point | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap