Flavor celluloses and injection molding method

A scented cellulose, injection molding technology, applied in the direction of coating, etc., can solve the problems of short scent persistence and poor compatibility of cellulose, and achieve the effect of strong scent persistence, good compatibility, and no electrostatic adsorption

Active Publication Date: 2013-12-11
东莞冠狄塑胶有限公司
View PDF5 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] But the compatibility of the flavoring agent of the existing cellulose plate and cellulose is poor, and after using for a period of time, the fragrance is completely released, resulting in a short duration of fragrance that cannot meet people's requirements

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0042] A kind of injection molding method of scented cellulose, it comprises the steps:

[0043] a. Put 90 parts of cellulose acetate and 30 parts of diethyl phthalate into a high-speed mixer and mix for 20 hours to prepare mixture I;

[0044] b. Add 0.01 part of lily flavoring agent to mixture I, mix and stir evenly, and let it stand for 20 hours to prepare mixture II;

[0045] c. Put the mixture II into a twin-screw extruder to melt and extrude, the extrusion temperature is 165°C, the extrusion speed is 20r / min, cool to 30°C and then pelletize to obtain colorless flavor cellulose;

[0046] d. Put the prepared flavored cellulose into an injection molding machine, and make a cellulose plate under the condition of 150-200°C.

[0047] A cellulose plate prepared by applying the method of this embodiment.

Embodiment 2

[0049] A kind of injection molding method of scented cellulose, it comprises the steps:

[0050] a. Put 92 parts of cellulose acetate propionate and 35 parts of glyceryl diacetate into a high-speed mixer and mix for 21 hours to prepare mixture I;

[0051] b. Add 0.03 parts of rose flavoring agent to mixture I, mix and stir evenly, and let it stand for 21 hours to prepare mixture II;

[0052] c. Put the mixture II into a twin-screw extruder for melt extrusion, the extrusion temperature is 170°C, the extrusion speed is 22r / min, cool to 35°C and then pelletize to obtain colorless flavor cellulose;

[0053] c1. Add 1 part of Lithor red pigment powder to the prepared colorless flavor cellulose to obtain colored flavor cellulose;

[0054] d. Put the prepared colored and flavored cellulose into an injection molding machine, and make a cellulose plate under the condition of 150-200°C.

[0055] A multi-color cellulose plate with rose fragrance prepared by applying the method of this ...

Embodiment 3

[0057] A kind of injection molding method of scented cellulose, it comprises the steps:

[0058] a. Put 95 parts of cellulose acetate butyrate and 37 parts of glyceryl triacetate into a high-speed mixer and mix for 22 hours to prepare mixture I;

[0059] b. Add 0.04 parts of lavender flavoring agent to mixture I, mix and stir evenly, and let it stand for 22 hours to prepare mixture II;

[0060] c. Put the mixture II into a twin-screw extruder to melt and extrude, the extrusion temperature is 175°C, the extrusion speed is 24r / min, cool to 40°C and then pelletize to obtain colorless flavor cellulose;

[0061] c1. Add 1.5 parts of permanent orange pigment powder to the obtained colorless flavor cellulose to obtain colored flavor cellulose;

[0062] d. Put the prepared colored and flavored cellulose into an injection molding machine, and make a cellulose plate under the condition of 150-200°C.

[0063] A multi-color cellulose board with lavender fragrance prepared by applying th...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melting pointaaaaaaaaaa
densityaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention relates to flavor celluloses and an injection molding method. The flavor celluloses comprise the following raw materials: 60-90 parts of celluloses, 20-30 parts of plasticizer, 0-3 parts of pigment powder and 0.01-0.1 part of flavoring agent, wherein the plasticizer added to the celluloses is conductive to the transfer of the flavoring agent in the celluloses, so that the durability of flavor can be remarkably enhanced without the addition of other compatilizers. The prepared flavor celluloses have high flavor strength and strong flavor durability; the problem of short time of duration of the flavor of conventional celluloses is solved; multicolor cellulose boards manufactured by the flavor celluloses have high elasticity, good air permeability, no electrostatic adherence, no toxicity, very good liquid permeability, good adsorptivity and wide application range, is anallergic after being in contact with skin for a long term, can be dry-cleaned or washed with water and can be manufactured into multiple products such as tool handles and hair pins. The injection molding method of the flavor celluloses is simple in process and low in production cost.

Description

technical field [0001] The invention relates to the technical field of cellulose plates, in particular to a scented cellulose and an injection molding method thereof. Background technique [0002] Cellulose is the oldest and most abundant natural polymer on the earth. It is inexhaustible and the most precious natural renewable resource for human beings. The cellulose sheet made of it has low thermal conductivity and can be produced flexibly. , a variety of visual effects, excellent fluidity, good surface gloss, good electrical insulation, anti-static, self-brightness, high transparency, strong pressure resistance, unique surface vision, has been widely used in tool handles, hair clips, Toys, goggles, helmets, glasses frames, toothbrushes, tableware handles, combs and photo negatives, etc., as people's requirements for cellulose products continue to increase, people add flavoring agents to them, so that the prepared cellulose can Exudes a pleasant or appropriate fragrance, i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L1/12C08L1/14C08K13/02B29B9/06B29C45/00
Inventor 黄炳坚
Owner 东莞冠狄塑胶有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com