A technology of semi-melting and microporous tubes, which is applied in the technical field of semi-melting continuous extrusion of polymer powder to prepare microporous tubes, to achieve the effects of weakening the melting shear effect, saving costs, and facilitating continuous extrusion molding

Active Publication Date: 2013-12-18
SUZHOU KAHO POLYMER TECH CO LTD +1
View PDF3 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In addition, polymer resin tubular products made by ordinary extrusion methods are closed-cell products

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Technology for preparing micropore pipe through semi-molten continuous extrusion of high molecular powder

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0031] The present invention will now be further described in detail in conjunction with the accompanying drawings and embodiments, and these accompanying drawings are simplified schematic diagrams.

[0032] Such as figure 1 Shown, a kind of technology that polymer powder semi-melt continuous extrusion prepares microporous tube comprises the following steps:

[0033] (1) The solid powder material is fed into the screw extrusion device through the hopper;

[0034] (2) The material enters the barrel of the screw extrusion device for heating, and at the same time, it is initially compacted by the screw of the screw extrusion device, and the material becomes a semi-molten state;

[0035] (3) The material enters the head 2 of the screw extrusion device and is further compacted by the compression of the head 2;

[0036] (4) The material enters the cavity of the die 4 of the screw extrusion device and is formed into a tubular shape, and the inner and outer diameters are determined ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a technology for preparing a micropore pipe through semi-molten continuous extrusion of high molecular powder. The technology is characterized by comprising the following steps: (1) feeding solid powdered material in a screw extruding device through a hopper; (2) heating a barrel entering the screw extruding device, and performing initial compaction by a threaded rod at the same time so as to enable materials to be in a semi-molten state; (3) feeding the material in a handpiece for further compaction; (4) feeding the materials in a mould cavity of a neck mould of the screw extruding device to be tubular, determining inner and outer diameters under the effect of a vacuum cooling forming sleeve, and initially cooling; (5) cutting through a cutting device to obtain the micropore pipe. According to the technology, the high molecular powder is continuously extruded and formed when being in semi-molten state and the produced product does not need to be subjected to aftertreatment simultaneously when production of micropore pipes is realized, so that the production efficiency is greatly improved. According to the technology, a solvent is not used, and thus the micropore pipe is beneficial to environmental protection and health of operators.

Description

technical field [0001] The invention relates to a molding process of polymer microporous materials, in particular to a molding process of polymer microporous tubes. Background technique [0002] At present, the molding methods of microporous materials at home and abroad include: polymer particle sintering method, thermal phase separation method, inorganic particle filling method and melt extrusion stretching method, etc. Among them, the polymer particle sintering method is a method in which particles of a certain particle size are loaded into corresponding molds and sintered at high temperature to obtain microporous materials. It is a discontinuous production method with low production efficiency; thermally induced phase separation method is to The polymer dissolves in a specific solvent at high temperature to form a homogeneous solution. When the temperature decreases, the solid-liquid phase separation occurs in the homogeneous system. After the solvent is removed, the spac...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B29C47/38B29C47/88B29C47/92B29C47/78B29C47/08B29C48/09B29C48/39B29C48/395B29C48/92
CPCB29C48/92B29C48/09B29C48/39B29C48/395B29C48/832B29C48/911B29C48/913B29C48/914B29C48/916B29C48/919B29C48/904B29C2948/92428B29C2948/92619B29C2948/92933
Inventor 王秋玲
Owner SUZHOU KAHO POLYMER TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap