Polishing wheel piece and production method

A polishing wheel and accelerator technology, which is used in grinding/polishing equipment, abrasives, metal processing equipment, etc., to achieve the effect of reducing costs, fewer repairs, and shorter grinding time

Active Publication Date: 2014-01-08
江苏好帮手砂轮有限公司
View PDF7 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Due to the strict requirements on the production process of good nylon wheels, they generally rely on imports. At present, there is no polishing wheel that can effectively replace imported nylon wheels and resin fine-grained polishing wheels with good shape retention, low price, and fast grinding speed without burning the workpiece. piece

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] 1. Weigh the materials, weigh the following materials in proportion, and put them into the rubber mixer: 100 parts of styrene-butadiene rubber, 5 parts of pine tar, 5 parts of stearic acid, 8 parts of aluminum oxide, 15 parts of resin powder, 1.5 parts of zinc oxide, 1 part of accelerator DM, 0.5 part of accelerator M, and three times the amount of abrasives of the aforementioned components;

[0021] 2. Mixing, the materials are mixed evenly by mixing;

[0022] 3. Forming, the mixed material is evenly distributed on the base material by rolling, and laminated according to the diameter and thickness of the polishing wheel to be produced, cut and processed into the required shape after standing still, and processed by heat treatment after

[0023] 4. Vulcanization: heat the material to 175°C and keep this temperature for 20 hours for vulcanization.

Embodiment 2

[0025] 1. Weigh the materials, weigh the following materials in proportion, and put them into the reaction kettle: 100 parts of styrene-butadiene rubber, 10 parts of pine tar, 10 parts of stearic acid, 10 parts of aluminum oxide, 20 parts of resin powder, 2.5 parts of zinc oxide, 2 parts of agent DM, 0.5 parts of accelerator M, and three times the amount of abrasives of the aforementioned components;

[0026] 2. Mixing, the materials are mixed evenly by mixing;

[0027] 3. Forming, the mixed material is evenly distributed on the base material by rolling, and laminated according to the diameter and thickness of the polishing wheel to be produced, cut and processed into the required shape after standing still, and processed by heat treatment after

[0028] 4. Vulcanization: heat the material to 175°C and keep this temperature for 25 hours for vulcanization.

Embodiment 3

[0030] 1. Weigh the materials, weigh the following materials in proportion, and put them into the rubber mixer: 100 parts of styrene-butadiene rubber, 10 parts of pine tar, 10 parts of stearic acid, 10 parts of aluminum oxide, 20 parts of resin powder, 2.5 parts of zinc oxide, 2 parts of accelerator DM, 0.5 parts of accelerator M, and three times the amount of abrasives of the aforementioned components;

[0031] 2. Mixing, the materials are mixed evenly by mixing;

[0032] 3. Forming, the mixed material is evenly distributed on the base material by rolling, and laminated according to the diameter and thickness of the polishing wheel to be produced, cut and processed into the required shape after standing still, and processed by heat treatment after

[0033] 4. Vulcanization: heat the material to 175°C and keep this temperature for 23 hours for vulcanization.

[0034] The abrasive material of the polishing wheel sheet produced by the present invention is below 280#, and is us...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a polishing wheel piece. The polishing wheel piece comprises butadiene styrene rubber, pine tar, stearic acid, alumina, resin powder, zinc oxide, an accelerant DM and an accelerant M. Meanwhile, the invention further provides a production method of the polishing wheel piece. The method includes the steps of weighing materials, mixing the materials, conducting forming and conducting vulcanization. A polishing wheel sheet abrasive produced through the production method is under 280 meshes and used for polishing automobile connecting rods and shock absorber pipes, the surface roughness Ra can be less than or equal to 0.05, the polishing wheel piece can effectively replace a resin fine-granularity polishing grinding wheel and has the advantages of having a high shape protection property, less in the number of maintenance times, short in grinding time, low in cost and the like, and the polishing wheel piece can not burn a workpiece in the use process. The polishing wheel piece can partly replace a nylon polishing wheel imported from Japan. Cost is effectively reduced.

Description

technical field [0001] The invention relates to a formula for replacing imported polishing wheels and a production method thereof, belonging to the field of mechanical accessories. Background technique [0002] The polishing wheel is a press-fit flat wheel, which is formed by pressing several polishing wheel pieces, and the outer surface of each polishing wheel piece is evenly coated with a layer of polishing oil. No separate oiling is required during polishing. It is simple in structure and easy to use. [0003] Nylon wheel is a kind of polishing wheel, also known as (Anlong grinding wheel, non-woven wheel, fiber wheel), strong cutting force, can partially replace the traditional cloth grinding wheel, sponge cloth wheel and rubber abrasive cloth wheel, and can cover the abrasive cloth belt. The left thick lines are very effective for fine removal and continuous repair of larger burrs of castings, and the lines are fine and beautiful after grinding, which can be used for m...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B24D18/00B24D3/22B24D3/28
Inventor 曹杰
Owner 江苏好帮手砂轮有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com