A flame-retardant polyethylene cable material with anti-mold function
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A technology of flame-retardant polyethylene and cable materials, which is applied in the direction of circuits, electrical components, insulators, etc., can solve the problems affecting the physical and mechanical properties and processing of cable materials, achieve good flame-retardant performance, inhibit growth, and avoid losses.
Active Publication Date: 2016-04-13
蚌埠尚维知识产权运营有限公司
View PDF2 Cites 0 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
Among them, the demand for non-halogen and low-smoke flame-retardant polyethylene cable materials with anti-mold function is increasing. At present, the production of non-halogen and low-smoke flame-retardant polyethylene cable materials with anti-mold function is mostly in polyolefin substrates. Add a large amount of acetylene carbon black or acetylene carbon black to achieve the flame retardant effect, however, the addition of a large amount of inorganic materials affects the physical and mechanical properties and processing of cable materials
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment Construction
[0017] A flame-retardant polyethylene cable material with anti-mold function, prepared from the following component raw materials in weight (kg):
[0019] Among them, the modified filler is prepared by the following method: a. Take the following raw materials by weight (kg): kaolin 200, diatomite 125, sepiolite 11, nano-carbon 2, zirconium fluoride 1, alum 2.5, Tibetan Fennel essential oil 2, ascorbic acid 1.5, sodium alginate 2.5, precipitated silica 32, tea polyphenol 3, acrylate-2-hydroxypro...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention provides a flame-retardant polyethylene cable material capable of preventing mould. The flame-retardant polyethylene cable material is prepared with the following components and raw materials by weight: 50-60 parts of high-density polyethylene, 30-45 parts of linear low-density polyethylene, 10-15 parts of polyester resin, 8-10 parts of organic silicon resin, 2-3 parts of simethicone, 1-2 parts of zinc oxide, 5-10 parts of wollastonite powder, 1-2 parts of barium sulfate, 5-6 parts of dolomite, 6-8 parts of attapulgite, 4-6 parts of celestite, 10-12 parts of zinc hydroxide, 10-15 parts of triammonium phosphate, 10-12 parts of tricresyl phosphate (TCP), 6-8 parts of poly(1,2-propylene glycol adipate), 1-2 parts of sophora flavescens alcohol extract, 0.5-0.6 parts of zanthoxylum oil, 1-2 parts of OBPA (10,10'-oxybisphenoxarsine) mould inhibitor, 1-1.5 parts of PVC (polyvinyl chloride) processing agent ACR-401 (acrylate plastic modifier), and 10-15 parts of modified filler. The cable wire has good antibacterial property, and the characteristics of weather resistance, low smoke, ageing resistance, flame retardation and so on.
Description
technical field [0001] The invention relates to the field of cable materials, in particular to a flame-retardant polyethylene cable material with anti-mold function. Background technique [0002] Wire and cable are indispensable and important materials in industrial and agricultural production and modern life. my country is the world's largest producer of wire and cable. The wire and cable industry occupies a very important position in my country's national economy. However, at present, the market The cable material is not resistant to high temperature and aging, and the material turns yellow and becomes brittle after the aging test. There are more and more fires caused by aging wires. How to reduce the incidence of fire and the death rate in the event of fire, low smoke, halogen-free, flame retardant, and environmental protection have also become the development direction of the wire and cable industry. Among them, the demand for non-halogen and low-smoke flame-retardant po...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.