Preparation method of a high-barrier fireproof and high temperature resistant composite material

A composite material and high-temperature-resistant technology, applied in chemical instruments and methods, layered products, lamination devices, etc., can solve problems such as difficulty in obtaining production technical parameters, thin materials and poor ductility, and failure to meet new requirements. Achieve the effects of green production process, outstanding technical advantages, excellent ductility and softness

Active Publication Date: 2016-08-17
江苏东浦精细陶瓷科技股份有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, few domestic manufacturers can produce high-barrier fireproof products. Some foreign companies purchase and sell to China and other countries in Malaysia and other countries. Many domestic companies can only produce two-layer products of aluminum foil and glass fiber cloth. The overall material It is thin and has poor ductility, which cannot meet the new requirements of the current market for packaging.
[0003] Foreign companies use high-barrier, fire-proof and high-temperature-resistant materials as their core technology to protect, and it is difficult to obtain technical cores such as production technical parameters, while domestic manufacturers have not yet developed similar products and production processes that can compete with them

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of a high-barrier fireproof and high temperature resistant composite material
  • Preparation method of a high-barrier fireproof and high temperature resistant composite material
  • Preparation method of a high-barrier fireproof and high temperature resistant composite material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] A method for preparing a high-barrier fire-proof and high-temperature-resistant composite material, comprising the following steps:

[0025] Step 1. Print patterns or characters on the surface of the aluminum foil, and apply a high temperature resistant protective layer;

[0026] Step 2: Glue the aluminum foil, dry it in a high-temperature oven, and compound it with glass fiber cloth at the heat-sealing part. In this step, the amount of glue applied to the aluminum foil is 2.2g / m 2 , the temperature of the high-temperature oven is controlled at 148°C, the time is 3.0 seconds, and the heat sealing pressure is 1.95kg to achieve appropriate strength and flexibility.

[0027] Step 3: After winding into rolls, mature in a constant temperature room at 42°C for 38 hours to obtain the first intermediate product. In this step, the winding tension is 19N, and the winding speed is 100m / min;

[0028] Step 4: Apply gluing on the second layer of aluminum foil, heat-seal and roll the...

Embodiment 2

[0034] A method for preparing a high-barrier fire-proof and high-temperature-resistant composite material, comprising the following steps:

[0035] Step 1. Print patterns or characters on the surface of the aluminum foil, and apply a high temperature resistant protective layer;

[0036] Step 2: Glue the aluminum foil, dry it in a high-temperature oven, and compound it with glass fiber cloth at the heat-sealing part. In this step, the amount of glue applied to the aluminum foil is 3.3g / m 2 , the temperature of the high-temperature oven is controlled at 153°C, the time is 2.8 seconds, and the heat sealing pressure is 2.15kg, so as to achieve appropriate strength and flexibility. ;

[0037] Step 3. After winding into rolls, mature in a constant temperature room at 48°C for 50 hours to obtain the first intermediate product. In this step, the winding tension is 20N, and the winding speed is 105m / min;

[0038] Step 4: Apply gluing on the second layer of aluminum foil, heat-seal an...

Embodiment 3

[0044] A method for preparing a high-barrier fire-proof and high-temperature-resistant composite material, comprising the following steps:

[0045] Step 1. Print patterns or characters on the surface of the aluminum foil, and apply a high temperature resistant protective layer;

[0046] Step 2: Glue the aluminum foil, dry it in a high-temperature oven, and compound it with glass fiber cloth at the heat-sealing part. In this step, the amount of glue applied to the aluminum foil is 2.5g / m 2 , the temperature of the high-temperature oven is controlled at 145°C, the time is 2.5 seconds, and the heat sealing pressure is 2.0kg, so as to achieve appropriate strength and flexibility. ;

[0047] Step 3: After winding into rolls, mature in a constant temperature room at 45°C for 55 hours to obtain the first intermediate product. In this step, the winding tension is 21N, and the winding speed is 110m / min;

[0048] Step 4: Apply gluing on the second layer of aluminum foil, heat-seal and...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a high-barrier, fireproof and high temperature resistant composite material and a preparation method thereof. The high temperature resistant composite material comprises a polyester layer, a polyvinyl chloride soft cloth layer, an adhesive sticker layer and a paper centrifugal film layer which are composited sequentially. The preparation method of the composite material comprises steps as follows: patterns are printed on a polyester film in a preset mode; a dry compound machine is used for gluing, the polyester film and polyvinyl chloride soft cloth are heat-sealed and rolled at certain temperature and pressure, and an intermediate product is obtained; the rolled intermediate product is cured at a certain temperature; after a rolled film is cooled, the dry compound machine is used for gluing, and the film is composited and rolled with a paper centrifugal film at certain pressure; and slitting and packaging are performed according to preset specifications. The composite material has excellent ductility and softness, breaks the technological monopoly of foreign companies, fills the technological blank and the product blank at home and has a wide market prospect; and the production process is green, environment-friendly and energy-saving, meets requirements of the national high technology industry and has outstanding technological advantages.

Description

technical field [0001] The invention relates to a composite material, especially a preparation method of a high-barrier, fire-proof and high-temperature-resistant composite material. Background technique [0002] At present, few domestic manufacturers can produce high-barrier fireproof products. Some foreign companies purchase and sell to China and other countries in Malaysia and other countries. Many domestic companies can only produce two-layer products of aluminum foil and glass fiber cloth. The overall material It is thin and has poor ductility, which cannot meet the new requirements of the current market for packaging. [0003] Foreign companies use high-barrier, fire-resistant and high-temperature-resistant materials as their core technology to protect, and it is difficult to obtain technical cores such as production technical parameters, while domestic manufacturers have not yet developed similar products and production processes that can compete with them. [0004] ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B32B15/14B32B17/02B32B15/09B32B7/12B32B37/12B32B37/06B32B37/10
Inventor 颜成林颜成贵韩永洪
Owner 江苏东浦精细陶瓷科技股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com