Vessel for preventing solute and molten state salt and alkali in salt and alkali solutions from climbing out

A molten state, alkaline solution technology, applied in the direction of chemical instruments and methods, synthetic resin layered products, layered products, etc., can solve problems affecting normal production, salt stains, alkali stains are difficult to clean, waste resources, etc., to achieve convenience Large-scale production, excellent chemical stability, and low cost effects

Active Publication Date: 2014-04-30
SHANGHAI APPLIED TECHNOLOGIES COLLEGE
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

For salt, alkali solution and molten salt and alkali, in an open system, if left for a period of time, the crystals will climb out along the container wall, and climb outside the container mouth to form salt and alkali stains, making the concentration of the prepared solution Reduce or cause the loss of salt and alkali in molten state, and it is difficult to clean up salt and alkali stains, which not only affects the normal production of experiments and factories, but also wastes resources

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] A container for preventing solutes in salt and alkali solutions and molten salt and alkali from creeping out, including the container, and sintering on the inner wall of the container mouth from the edge of the container mouth down to 0.5-1.5cm from the edge of the container mouth Has a non-adhesive film;

[0031] The non-adhesive film is polytetrafluoroethylene with a thickness of 0.05-0.075mm;

[0032] The container is an open glass container, i.e. a glass beaker.

[0033] A kind of above-mentioned preparation method of the container that prevents the solute in the salt and alkali solution and the salt in the molten state and the alkali to climb out, specifically comprises the following steps:

[0034] (1) Take a glass beaker and wash it with deionized water to get a clean glass beaker;

[0035] (2) On the inner wall of the mouth of a clean glass beaker, apply a layer of polytetrafluoroethylene emulsion dispersion liquid from the edge of the container mouth down to ...

Embodiment 2

[0040] A container for preventing solutes in salt and alkali solutions and molten salt and alkali from creeping out, including the container, and sintering on the inner wall of the container mouth from the edge of the container mouth down to 0.5-1.5cm from the edge of the container mouth Has a non-adhesive film;

[0041] The non-adhesive film is polytetrafluoroethylene with a thickness of 0.05-0.075mm;

[0042] The container is an open ceramic container, that is, a crucible.

[0043] A kind of above-mentioned preparation method of the container that prevents the solute in the salt and alkali solution and the salt in the molten state and the alkali to climb out, specifically comprises the following steps:

[0044] (1) Take the crucible, and get a clean crucible after being treated with deionized water;

[0045] (2) On the inner wall of the clean crucible mouth, from the edge of the container mouth down to 0.5-1.5cm away from the edge of the container mouth, apply a layer of p...

Embodiment 3

[0050] A container for preventing solutes in salt and alkali solutions and molten salt and alkali from creeping out, including the container, and sintering on the inner wall of the container mouth from the edge of the container mouth down to 0.5-1.5cm from the edge of the container mouth Has a non-adhesive film;

[0051] The non-adhesive film is polyvinylidene fluoride with a thickness of 0.05-0.075 mm;

[0052] The container is an open metal container, that is, a stainless steel container.

[0053] A kind of above-mentioned preparation method of the container that prevents the solute in the salt and alkali solution and the salt in the molten state and the alkali to climb out, specifically comprises the following steps:

[0054] (1) Take a stainless steel container and clean it with deionized water;

[0055] (2) On the inner wall of a clean stainless steel container mouth, spray a layer of polyvinylidene fluoride swelling solution from the edge of the container mouth down to...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Sintering temperatureaaaaaaaaaa
Sintering temperatureaaaaaaaaaa
Login to View More

Abstract

The invention discloses a vessel for preventing solute and molten state salt and alkali in salt and alkali solutions from climbing out and a preparation method thereof. According to the vessel, a layer of non-adhesive membrane is sintered at the position, 0.5-1.5cm down below the edge of the vessel mouth, on the inner wall of the vessel mouth, and the non-adhesive membrane is teflon or polyvinylidene fluoride with thickness of 0.05-0.075mm. The vessel can effectively prevent salt and alkali from climbing out without affecting the use of the salt and alkali. The preparation method is simple, has low cost and is convenient for large scale production.

Description

technical field [0001] The invention belongs to the field of energy saving and consumption reduction, in particular to a container from which the solute in the salt and alkali solution and the salt and alkali in the molten state creep out. Background technique [0002] The phenomenon that salt and alkali climb out along with the container wall is classified as "alkali climbing" phenomenon. For salt, alkali solution and molten salt and alkali, in an open system, if left for a period of time, the crystals will climb out along the container wall, and climb outside the container mouth, forming salt and alkali stains, making the concentration of the prepared solution Reduce or cause the loss of salt and alkali in the molten state, and the salt stains and alkali stains are difficult to clean up, which not only affects the normal production of experiments and factories, but also wastes resources. This method is simple and convenient, and can effectively improve the phenomenon of "...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B32B1/02B32B27/30B32B33/00
Inventor 张全生王淼党国举王昭勍李海燕闵凡奇李硕李细方张伟黄海军
Owner SHANGHAI APPLIED TECHNOLOGIES COLLEGE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products