A kind of wear-resistant polypropylene composite material and preparation method thereof

A technology of composite material and polypropylene, which is applied in the field of wear-resistant polypropylene composite materials and its preparation, can solve the problem that the wear resistance of polypropylene materials cannot be fundamentally solved, and achieve the effect of low production cost and good wear resistance

Active Publication Date: 2016-09-21
CHONGQNG PRET NEW MATERIAL +2
View PDF12 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although the above methods have solved a certain wear resistance in specific components and systems, they cannot fundamentally solve the wear resistance of polypropylene materials.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of wear-resistant polypropylene composite material and preparation method thereof
  • A kind of wear-resistant polypropylene composite material and preparation method thereof
  • A kind of wear-resistant polypropylene composite material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0028] Below in conjunction with embodiment, the present invention is described in further detail:

[0029] In the material formulations of the examples and comparative examples, the polypropylene used is a copolymerized polypropylene produced by Shanghai Petrochemical, and the trade name is M2600R. The inorganic filler is 5000-mesh talc powder with an average particle size of 2.5 microns. The toughening agent POE used is a linear ethylene-octene copolymer produced by Dupont Company of the United States, the brand name is Engage8180, the density is 0.863g / cm3, and the melt flow rate is 0.5g / 10min. The nucleating agent used is the nucleating agent NA-21 produced by Japan Asahi Denka Co., Ltd. , which is a colorless powder, and its added amount is 0.1-0.5% by weight. The anti-wear agent used is LUBDE305 produced by Shanghai Dirun Chemical Co., Ltd., a white fine particle of high molecular weight siloxane, its molecular weight is between 2w and 6w, the average particle size is ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
densityaaaaaaaaaa
melt flow indexaaaaaaaaaa
Login to View More

Abstract

The invention discloses a wear-resisting polypropylene composite material and a preparation method thereof. The wear-resisting polypropylene composite material is composed of the following raw materials in percentage by weight: 46-95 parts of polypropylene, 0-25 parts of inorganic fillers, 0-15 parts of a toughening agent POE (Polyoxyethylene), 1-10 parts of a wear-resisting agent, 0.1-0.5 part of a nucleating agent, 0.1-1 part of an antioxidant, 0.1-1 part of a light stabilizing agent and 0-2 parts of color toner or color master batch. The raw materials are put into a high-speed mixer to be mixed for 3-5 minutes; the mixed raw materials are put into a double-screw extruder; then mixed raw materials are subjected to melt extrusion and granulation. The process is as follows: the temperature of a first zone is 190-200 DEG C, the temperature of a second zone is 200-210 DEG C, the temperature of a third zone is 210-220 DEG C and the temperature of a fourth zone is 205-215 DEG C; the staying time of a whole extruding process is 1-2 minutes and the pressure is 12-18MPa. According to the wear-resisting polypropylene composite material and the preparation method thereof, the wear-resisting agent and the nucleating agent are added in a basic formula of the polypropylene composite material so as to prepare the polypropylene material with a good wear-resisting performance. The wear-resisting polypropylene composite material has the advantages that the wear-resisting performance of the material is guaranteed and physical and mechanical properties of the materials are basically not influenced; the preparation process is simple and the production cost is low.

Description

technical field [0001] The invention relates to a wear-resistant polypropylene composite material and a preparation method thereof, which can be used for interior and exterior trim parts of automobiles and belongs to the technical field of polymer modification and processing. Background technique [0002] Polypropylene has good physical, mechanical, chemical properties and easy processing properties. At the same time, it is light, cheap and easy to recycle, so it is widely used in interior and exterior parts of automobiles. However, the wear resistance of polypropylene material is poor. Some parts that are susceptible to constant friction from the outside, such as brake light housings, horn covers, etc., will be damaged due to friction, which directly affects the appearance of the car and seriously affects its quality. In the application of automotive trims, polypropylene materials need to be improved to meet the requirements of product wear resistance. [0003] There have ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L23/12C08L53/00C08L23/08C08L83/04C08K3/34C08K3/26C08K3/30B29C47/92B29C48/92
CPCB29B9/06B29C48/92B29C2948/92514B29C2948/92561B29C2948/92704C08L23/12C08L53/00C08L2205/03C08L2205/24C08L23/0815C08L83/04C08K13/02C08K3/34C08K5/523B29C48/40B29C48/875B29C2948/92895
Inventor 康兴宾张鹰张祥福周文
Owner CHONGQNG PRET NEW MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com