A kind of densifier and ultra-high density cement slurry based on the densifier

A technology of ultra-high density and densifier, which is applied in the direction of drilling compositions, chemical instruments and methods, and can solve the problem of insufficient cement slurry density

Active Publication Date: 2016-03-30
四川川庆井下科技有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In view of the above-mentioned prior art, the technical problem to be solved by the present invention is to provide a densifier and an ultra-high-density cement slurry based on the densifier, so as to solve the problem that the density of the existing cement slurry is not high enough

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] Density at 90°C is 2.50g / cm 3 The ultra-high-density cement slurry is composed of a base formula and additives: the weight of the base formula consists of 100 parts of cement, 180 parts of ilmenite, 20 parts of a densifier, and a water-cement ratio of 0.27; In terms of percentage, the weight percentage of additives is composed of: 0.6% of fluid loss reducer, 0.2% of drag reducer, and 0.05% of retarder. The weight of said densifier consists of: 80-90 parts of iron ore powder, 5 parts of manganese ore powder -10 parts, G grade superfine cement 5-10 parts, micro silica fume 5-10 parts.

Embodiment 2

[0027] Density at 120°C is 2.50g / cm 3 The ultra-high-density cement slurry is composed of a base formula and additives: the weight of the base formula is 75 parts of cement, 25 parts of quartz sand, 170 parts of ilmenite, 30 parts of densifier, and a water-cement ratio of 0.26; In terms of the percentage of the total weight of the square, the weight percentage of additives is composed of: 0.8% of high temperature fluid loss reducer, 0.4% of drag reducer, and 0.1% of retarder, and the weight of said densifier is composed of: iron ore powder 80-90% 5-10 parts of manganese ore powder, 5-10 parts of G grade superfine cement, and 5-10 parts of microsilica fume.

Embodiment 3

[0029] Density at 90°C is 2.90g / cm 3 The ultra-high-density cement slurry is composed of a base formula and additives: the weight of the base formula consists of 100 parts of cement, 125 parts of a densifier, and a water-cement ratio of 0.2; in terms of the percentage of the total weight of the base formula, the weight of the additive The percentage composition is: 0.5% fluid loss reducer, 0.7% drag reducer, 0.05% retarder, and the weight composition of the densifier is: 80-90 parts of iron ore powder, 5-10 parts of manganese ore powder, G grade 5-10 parts of superfine cement, 5-10 parts of microsilica fume.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
densityaaaaaaaaaa
Login to View More

Abstract

The invention discloses a densifier and an ultra-high-density cement slurry based on the densifier. The weight composition of the densifier is: 80-90 parts of iron ore powder, 5-10 parts of manganese ore powder, and 5 parts of G-grade superfine cement. -10 parts, microsilica fume 5-10 parts. The ultra-high-density cement slurry provided by the invention has stable performance, low water loss, certain anti-air channeling ability, relatively ideal thickening transition time and can form cement stone with strong strength. It can effectively control high-pressure oil and gas layers, avoid oil and gas escape, and better improve the quality of cementing.

Description

technical field [0001] The invention belongs to the technical field of oil testing engineering, and in particular relates to a method for preparing an ultra-high-density cement slurry system in petroleum exploration and development. Background technique [0002] With the increasing drilling footage of deep wells and ultra-deep wells in complex formations, ordinary high-density cement slurry can no longer meet the needs of deep wells, ultra-deep wells and ultra-high pressure cementing operations. It is imperative to study ultra-high-density cement slurry systems. Therefore, the research on ultra-high-density cement slurry system is not only to meet the urgent needs of production, but also has very important practical significance. [0003] Domestic oil fields have basically formed 2.40g / cm 3 Using ordinary high-density cement slurry technology, but higher than 2.50g / cm 3 The density of ultra-high density cement slurry technology is limited by materials and basic theory, and...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09K8/48C09K8/467
CPCC04B28/00C09K8/48C09K8/487C09K2208/28C04B18/12
Inventor 吴家明张作宏曾科许桂莉向娴武超常超杨国良刘华治
Owner 四川川庆井下科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com