A kind of preparation method of aluminum oxide dry glue

A technology of alumina dry glue and alumina, applied in chemical instruments and methods, alumina/aluminum hydroxide, catalyst carrier, etc., can solve the problems of unfavorable heavy oil hydrodesulfurization and hydroconversion reaction, small specific surface area, etc. , to achieve the effects of accelerated molecular movement, uniform stacking, and improved utilization

Active Publication Date: 2015-09-30
CHINA PETROLEUM & CHEM CORP +1
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although the alumina carrier prepared by this gelling method has a large average pore size, it has a small specific surface area, and using it as a catalyst carrier is not conducive to heavy oil hydrodesulfurization and hydroconversion reactions.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of aluminum oxide dry glue
  • A kind of preparation method of aluminum oxide dry glue

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] Preparation of sodium metaaluminate solution concentration is 140gAl 2 o 3 / L, a total of 2.5L; the concentration of aluminum sulfate solution is 40gAl 2 o 3 / L, a total of 5.0L; in the mixed solution of ethanol and hydroxypropyl methylcellulose (HPMC), the concentration of ethanol is 1.0g / L, and the concentration of HPMC is 1.0g / L, a total of 1.0L.

[0028] Pre-add bottom water to the reaction tank, set the temperature of the reaction tank to 75°C, and start stirring. In the process of adding the prepared sodium metaaluminate solution and aluminum sulfate solution into the reaction tank, the mixed solution of ethanol and hydroxypropyl methylcellulose (HPMC) is added in parallel to adjust the pH value to 6.5, and the reaction time is 40min. After the materials were added, sodium hydroxide solution was added to the obtained product to adjust the pH value to 8.8, the reaction temperature was 90° C., and the reaction time was 30 minutes. After the reaction is finished...

Embodiment 2

[0030] Other conditions were the same as in Example 1, except that ethanol was replaced by isopropanol, the concentration of the prepared isopropanol was changed to 35g / L, HPMC was replaced by MC, and the concentration of the prepared MC was changed to 20g / L to prepare alumina B.

Embodiment 3

[0032] Other conditions were the same as in Example 1, except that the concentration of ethanol was changed to 55g / L, and the concentration of HPMC was changed to 50g / L to prepare alumina C.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
specific surface areaaaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method for alumina dry gel. The method comprises the following steps: in the process of gel formation by cocurrent flow of an alkaline solution containing aluminum and an acidic solution containing aluminum, adding an additive and an organic template agent in the manner of cocurrent flow at the same time, controlling proper reaction conditions and carrying out gel formation; then adding an alkaline solution to adjust a pH value; and then carrying out filtering, washing and drying so as to obtain the alumina dry gel. The alumina dry gel prepared by using the method has the advantages of a large specific surface area, a great pore volume and a reasonable pore structure and is particularly applicable as a carrier component for a heavy oil hydrotreating catalyst, especially applicable as a carrier component for a residual oil hydrodesulfurization or hydro-conversion catalyst.

Description

technical field [0001] The invention relates to a preparation method of alumina dry glue, in particular to a carrier component used for heavy residue oil hydrotreating catalysts. Background technique [0002] Alumina is one of the most commonly used industrial raw materials, and plays an important role in the fields of catalysts, ceramics, and refractory materials. Due to its good mechanical strength, thermal stability, adjustable acid properties and pore structure, alumina is widely used as a catalyst carrier in the field of catalysis. At present, the world's emphasis on hydrogenation technology makes the demand for hydrogenation catalysts in the catalyst market continue to increase. At present, the most widely used hydrogenation catalysts are usually supported catalysts, and their supports are generally alumina and composite supports derived from it, such as TiO 2 -Al 2 o 3 , SiO 2 -Al 2 o 3 etc., or add some additives to the alumina carrier for modification...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B01J32/00C01F7/02B01J21/04
Inventor 张成刘立军王永林杨刚袁胜华
Owner CHINA PETROLEUM & CHEM CORP