Low-wool-content multi-component chemical fiber blended fabric

A technology of chemical fibers and blended fabrics, which is applied in the processing of textile materials, continuous processing of textile materials, and weaving. It can solve problems such as low color fastness, wool fiber damage, and large color difference, and achieve excellent wearing comfort and good Moisture absorption, excellent performance effect

Active Publication Date: 2015-06-03
SHANDONG WOYUAN NEWFASHIONED FABRIC
View PDF10 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the dyeing of low-hair and multi-chemical fiber blended fabrics, it is easy to cause wool fiber damage or even damage, and technical problems such as low dyeing fastness and large color difference are insurmountable, making it difficult for beautiful ideas to come true. It was not successfully produced in the industry, and it was even considered impossible at one time

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Low-wool-content multi-component chemical fiber blended fabric
  • Low-wool-content multi-component chemical fiber blended fabric
  • Low-wool-content multi-component chemical fiber blended fabric

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0058] "Polyester / cationic polyester / viscose / tencel / wool / conductive fiber" serge fabric production technology:

[0059] 1. The ratio of spinning raw materials and yarn specifications

[0060] (1) percentage by weight of spinning raw material:

[0061] Polyester staple fiber 39.4%;

[0062] Cationic polyester 30%;

[0063] Viscose 10%;

[0064] Tencel 10%;

[0065] Wool 10%;

[0066]Carbon composite conductive fiber 0.6%.

[0067] 2. Yarn specification:

[0068] ① Yarn 1: 50S / 1, twisted to S twist, used as warp yarn;

[0069] ② Yarn 2: 36S / 1, twisted to Z twist, used as weft yarn.

[0070] 2. Weaving process

[0071] 1. Preparation process before weaving:

[0072] ①Doubling and double twisting:

[0073] Warp yarn: two 50S / 1 single yarns are paralleled with a twisted doubling machine to form a 50S / 2 ply yarn; twisted with a two-for-one twister, the twist is 1050T / m, S twist, and the spindle speed is 9000rpm.

[0074] ②Warp yarn steaming: steaming temperature is 85°C ...

Embodiment 2

[0124] Weight percentage of spinning raw material:

[0125] Polyester staple fiber 30%;

[0126] Cationic polyester 24.9%;

[0127] Viscose 10%;

[0128] Tencel 5%;

[0129] Wool 30%;

[0130] Carbon composite conductive fiber 0.1%.

[0131] The weaving process is as follows:

[0132] 1. Yarn specifications:

[0133] ① Yarn 1: 48S / 1, twisted to S twist, used as warp yarn;

[0134] ② Yarn 2: 40S / 1, twisted to Z twist, used as weft yarn.

[0135] 2. Weaving process

[0136] 1. Preparation process before weaving:

[0137] ①Doubling and double twisting:

[0138] Warp yarn: two 48S / 1 single yarns are paralleled with a twisted doubling machine to form a plied yarn 48S / 2; twisted with a two-for-one twister, the twist is 1000T / m, S twist, and the spindle speed is 8000rpm.

[0139] ②Warp yarn steaming: steaming temperature is 85°C, time is 85 minutes.

[0140] ③Sectional warping process

[0141] The total number of warps is 5900, the number of twists is 15 twists, the warp...

Embodiment 3

[0185] The percentage by weight of spinning raw material is:

[0186] 38% polyester staple fiber;

[0187] Cationic polyester 20.5%;

[0188] Viscose 18%;

[0189] Tencel 15%;

[0190] Wool 8%;

[0191] Carbon composite conductive fiber 0.5%.

[0192] The process is as follows:

[0193] 1. Yarn specifications:

[0194] ① Yarn 1: 55S / 1, twisted to S twist, used as warp yarn;

[0195] ② Yarn 2: 30S / 1, twisted to Z twist, used as weft yarn.

[0196] 2. Weaving process

[0197] 1. Preparation process before weaving:

[0198] ①Doubling and double twisting:

[0199] Warp yarn: two 55S / 1 single yarns are paralleled with a twisted doubling machine to form a 55S / 2 ply yarn; twisted with a two-for-one twister, the twist is 1050T / m, S twist, and the spindle speed is 9000rpm.

[0200] ②Warp yarn steaming: steaming temperature is 90°C, time is 90 minutes.

[0201] ③Sectional warping process

[0202] The total number of warps is 6000, the number of twists is 18 twists, the warp...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Basis weightaaaaaaaaaa
Login to view more

Abstract

The invention provides a low-wool-content multi-component chemical fiber blended fabric and a preparing method of the low-wool-content multi-component chemical fiber blended fabric and belongs to the field of spinning dyeing and finishing. Wool is added to multi-component chemical fibers and the low-wool-content multi-component chemical fiber blended fabric comprises, by weight, 30% to 40% of polyester staple fibers, 20% to 30% of modified polyester fibers, 10% to 20% of mucilage glue, 5% to 15% of Tencel, 8% to 30% of the wool and 0.1% to 0.6% of conductive fibers. The wool content of a traditional product is changed, wool fibers with the content smaller than 30% are blended with the polyester staple fibers, the modified polyester fibers, the mucilage glue, the Tencel and the conductive fibers in the chemical fibers in a combined mode, so that mutual advantage complement of the various fibers is achieved, and multiple colors, the high comfort degree and the easy-maintenance performance of the fabric are achieved with the low wool content. The technology is reasonable, the technical purpose of one bath dyeing of the wool and the multi-component chemical fibers is effectively achieved, and a new path is created for upgrading orientation and the comfort of chemical fiber fabric.

Description

technical field [0001] The invention belongs to the field of textile dyeing and finishing, and relates to a low hair content multi-component chemical fiber blended fabric and a preparation method thereof. Background technique [0002] Wool and polyester fabrics produced in the market generally contain more than 45% wool and other wool. They are made by dyeing tops and dyed polyester yarns. Although they have good comfort, they have been produced and sold for many years, but because of their relatively Single, difficult to care, long production process, and high prices limit the scope of market sales and are not suitable for modern fast-paced life; and blended fabrics mainly made of polyester, viscose, tencel and other chemical fibers, due to the collection It combines the different advantages of a variety of fibers, easy maintenance, bright and diverse colors, and greatly improved comfort. It is more and more favored by clothing manufacturers and consumers, and has gradually...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): D03D15/00D02G3/04D06B21/00D06C27/00D03D15/225D03D15/233D03D15/283D03D15/47D03D15/50D03D15/533
Inventor 武光信唐家瑞唐凯东明洪唐守荣刘文和
Owner SHANDONG WOYUAN NEWFASHIONED FABRIC
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap