Floating beads and method for preparing modified floating beads

A technology of floating beads and modification, applied in chemical instruments and methods, inorganic pigment treatment, fibrous fillers, etc., can solve the problems of high energy consumption in the production process, cumbersome preparation process, and low quality stability

Active Publication Date: 2014-06-18
HUZHOU GREEN BUILDING MATERIALS DEV
View PDF10 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the preparation process of this kind of chemical coating method is cumbersome, the quali

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0128] Example one

[0129] In method C, the additives described in steps ① and ④ consist of the following components, calculated in parts by mass:

[0130] Film forming aid 0.8

[0131] Leveling agent 0.1

[0132] Thickener 0.1

[0133] Antifreeze 1.0

[0134] Dispersant 0.5

[0135] Defoamer 0.2.

[0136] The formula of the reflective paint is as follows, in parts by mass:

[0137] Silicone modified acrylate emulsion 26.0

[0138] Elastic acrylic emulsion 16.0

[0139] Titanium dioxide 13.0

[0140] Barium sulfate 2.0

[0141] Mica powder 0.8

[0142] Water 16.0

[0143] Film forming aid 0.8

[0144] Leveling agent 0.1

[0145] Thickener 0.1

[0146] Antifreeze 1.0

[0147] Dispersant 0.5

[0148] Defoamer 0.2

[0149] Cellulose ether 0.05.

[0150] The formula of the heat insulation reflective coating is as follows, in parts by mass:

[0151] Silicone modified acrylate emulsion 26.0

[0152] Elastic acrylic emulsion 16.0

[0153] Modified floating beads 16.0

[0154] T...

Example Embodiment

[0165] Example two

[0166] In method C, the additives described in steps ① and ④ consist of the following components, calculated in parts by mass:

[0167] Film forming aid 0.9

[0168] Leveling agent 0.2

[0169] Thickener 0.12

[0170] Antifreeze 1.2

[0171] Dispersant 0.56

[0172] Defoamer 0.22

[0173] The formula of reflective paint is as follows:

[0174] Silicone modified acrylate emulsion 27.0

[0175] Elastic acrylic emulsion 17.0

[0176] Titanium dioxide 14.0

[0177] Barium sulfate 2.0

[0178] Mica powder 0.84

[0179] Water 16.5

[0180] Film forming aid 0.9

[0181] Leveling agent 0.2

[0182] Thickener 0.12

[0183] Antifreeze 1.2

[0184] Dispersant 0.56

[0185] Defoamer 0.22

[0186] Cellulose ether 0.05.

[0187] The formula of the heat insulation reflective coating is as follows:

[0188] Silicone modified acrylate emulsion 27.0

[0189] Elastic acrylic emulsion 17.0

[0190] Modified floating beads 17.0

[0191] Titanium dioxide 14.0

[0192] B...

Example Embodiment

[0202] Example three

[0203] In method C, the additives described in steps ① and ④ consist of the following components, calculated in parts by mass:

[0204] Film forming aid 1.0

[0205] Leveling agent 0.3

[0206] Thickener 0.15

[0207] Antifreeze 1.2

[0208] Dispersant 0.6

[0209] Defoamer 0.25

[0210] The formula of reflective paint is as follows:

[0211] Silicone modified acrylate emulsion 28.0

[0212] Elastic acrylic emulsion 18.0

[0213] Titanium dioxide 15.0

[0214] Barium sulfate 2.5

[0215] Mica powder 0.88

[0216] Water 16.5

[0217] Film forming aid 1.0

[0218] Leveling agent 0.3

[0219] Thickener 0.15

[0220] Antifreeze 1.2

[0221] Dispersant 0.56

[0222] Defoamer 0.26

[0223] Cellulose ether 0.05.

[0224] The formula of the heat insulation reflective coating is as follows:

[0225] Silicone modified acrylate emulsion 28.0

[0226] Elastic acrylic emulsion 18.0

[0227] Modified floating beads 18.0

[0228] Titanium dioxide 15.0

[0229] ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to coating materials for reflecting and insulating light and heat, particularly relates to floating beads and a method for preparing modified floating beads and belongs to the technical field of architectural coatings. A reflective and insulating coating material comprises a reflective coating material and the modified floating beads, wherein the modified floating beads are uniformly dispersed into the reflective coating material. According to the floating beads and the method for preparing the modified floating beads, from economic considerations, ceramic hollow microbeads are replaced with flyash floating beads, then, a good technical effect is obtained; the price of the flyash floating beads is far lower than that of the ceramic hollow microbeads, and although the heat insulating capability of the flyash floating beads is strong, the color of the flyash floating beads is not white enough, thus, the light and heat reflecting properties of the coating material are affected; the color problem of the floating beads is solved by adopting a titanium white spraying process, and the wall adhesion of the floating beads is far greater than that of the ceramic hollow microbeads, so that the floating beads have technical advantages; the reflective coating material can be used separately, can also be used in a manner of being matched with the modified floating beads, has a light and heat reflecting effect during separate use and has a heat reflecting and insulating effect during matched use.

Description

technical field [0001] The invention relates to a coating for reflecting light and heat and isolating light and heat, in particular to a preparation method of modified floating beads and the floating beads, which belong to the technical field of architectural coatings. Background technique [0002] At present, reflective heat insulation coatings have been more and more widely used in buildings. Generally speaking, under the same base material conditions, pigments and fillers play a leading role in the reflective heat insulation effect of reflective heat insulation coatings. One of the keys. Ceramic hollow microspheres are a kind of white powder. The particles are hollow inside, with low density and small thermal conductivity. They can well reflect incident waves such as light and heat, and prevent heat from being transmitted to the interior of the object. These properties make it a reflective barrier. First choice filler for thermal coatings. At present, most of the p...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09C1/40C09C3/06C09D133/00C09D5/33C09D7/12
Inventor 朱士荣朱维梁徐敏张海棠黄宝军
Owner HUZHOU GREEN BUILDING MATERIALS DEV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap