Diatomite ceramic and preparation method thereof

A technology of diatomite and ceramics, applied in the field of ceramics, can solve the problem that the advantages are not widely promoted, and achieve the effects of hard and durable quality, white and clean glaze, and strong adsorption capacity

Active Publication Date: 2014-06-25
青岛泉佳美硅藻泥科技有限公司
View PDF3 Cites 15 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This new type of building material has many advantages, so it is widely used in various decoration projects. Although diatomite is widely used in building material coatings, its advantages have not been widely promoted.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Diatomite ceramic and preparation method thereof
  • Diatomite ceramic and preparation method thereof
  • Diatomite ceramic and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] A kind of diatomite ceramic, is made up of the component of following weight ratio:

[0036] Diatomaceous earth 46%;

[0037] Kaolin 35%;

[0038] Aluminum oxide 2%;

[0039] Boron glass 1%;

[0040] Chromium oxide 1%;

[0041] Feldspar 9%;

[0042] Phosphogypsum 2%;

[0043] Leaf paraffin 1%;

[0044] Silica powder 2%;

[0045] Citrate 1%.

[0046] Above-mentioned diatomite ceramics are made by following method:

[0047] 1. Add water to diatomite, kaolin, alumina, boron glass, chromium oxide, feldspar, phosphogypsum, phylloparaffin, microsilica powder and citrate in the above weight ratio to make a slurry and then make a green body;

[0048] 2. Biscuit the prepared green body, and the bisque firing temperature is 760-830°C;

[0049] 3. Glaze after bisque firing;

[0050] 4. After glazing, fire at 1260-1300°C and keep at 1260-1300°C for 2 hours to make a finished product.

Embodiment 2

[0052] A kind of diatomite ceramic, is made up of the component of following weight ratio:

[0053] Diatomaceous earth 45%;

[0054] Kaolin 33%;

[0055] Aluminum oxide 2%;

[0056] Boron glass 2%;

[0057] Chromium oxide 2%;

[0058] Feldspar 8%;

[0059] Phosphogypsum 3%;

[0060] Leaf paraffin 1%;

[0061] Silica powder 1%;

[0062] Citrate 1%.

[0063] Above-mentioned diatomite ceramics are made by following method:

[0064] 1. Add water to diatomite, kaolin, alumina, boron glass, chromium oxide, feldspar, phosphogypsum, phylloparaffin, microsilica powder and citrate in the above weight ratio to make a slurry and then make a green body;

[0065] 2. Biscuit the prepared green body, and the bisque firing temperature is 760-830°C;

[0066] 3. Glaze after bisque firing;

[0067] 4. After glazing, fire at 1260-1300°C and keep at 1260-1300°C for 2 hours to make a finished product.

[0068] Use two bedrooms A and B which have the same area and have been decorated at t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a diatomite ceramic mud and a diatomite ceramic product thereof. The diatomite ceramic mud is composed of the following components in percentage by weight: 38-53% of diatomite, 30-42% of kaoline, 2-4% of alumium oxide, 1-2% of borax glass, 1-4% of chromic oxide, 7-12% of feldspar, 2-4% of ardealite, 0-3% of pyrophyllite, 0-1% of silica powder and 0-2% of citrate. Compared with the prior art, the formula of the diatomite ceramic mud is obtained by the applicant by virtue of countless tests, the components in the formula function synergistically, and especially, 38-53% of diatomite is added to the formula so that the fired ceramic product is white and clean in glaze, hard and durable in quality, has outstanding adsorption capacity and is capable of effectively absorbing harmful gases in a room, decomposing harmful substances in air, and suppressing bacteria and sterilizing so as to purify the indoor air.

Description

technical field [0001] The invention relates to the field of ceramics, in particular to a diatomite ceramic and a preparation method thereof. Background technique [0002] Nowadays, ceramic products are used in various fields, but most of them are made into utensils for storage or decoration materials or for industrial production. The beauty, high temperature resistance and insulation properties of ceramics are widely used. These existing properties of ceramics can no longer be used. Satisfy people's pursuit of high-quality life now. The main component of diatomaceous earth is silicic acid, with countless pores on the surface, which can absorb and decompose odors in the air, and has the functions of humidity control and deodorization. The building materials produced by using diatomite as raw materials not only have the characteristics of non-combustibility, dehumidification, deodorization and good permeability, but also can purify air, bacteriostasis and disinfection, sound...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B33/00C04B33/13
Inventor 徐连福
Owner 青岛泉佳美硅藻泥科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com