Water-based normal-temperature rust-removal rust-proof liquid and preparation method thereof

A kind of anti-rust liquid, normal temperature technology, applied in the direction of metal material coating process, etc., can solve the problems of few types of colorless and transparent resins, no long-term anti-rust, carcinogenicity, etc., achieve good corrosion and anti-rust effect, easy to remove Effect

Active Publication Date: 2014-06-25
ANHUI PUYUAN SEPARATION MACHINERY MFG CO LTD
View PDF5 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Ordinary anti-rust water contains a large amount of sodium nitrite, which is carcinogenic and is not conducive to environmental protection and human health. However, the use of humectants to prolong the life of anti-rust water brings the disadvantages of sticking hands and dust, and cannot prevent rust for a long time; Although the general dura-film anti-rust oil is suitable for long-term anti-rust, and the film is transparent and beautiful, there are few types of colorless and transparent resins, which are unstable and easy to oxidize and change color. They also need organic solvents to dissolve, which brings the danger of flammability and explosion. It is not conducive to environmental protection and health; the general anti-rust oil uses mineral oil, which is difficult to degrade, and it will also cause the problem of difficult degreasing when used for short-term anti-rust

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0009] A water-based room-temperature rust-removing and anti-rust solution is made of the following raw materials in parts by weight (kg): 1.5 parts by weight of zinc oxide, 2.5 parts of manganese dioxide, 2.5 parts of citric acid, 23 parts of E-12 epoxy resin, 7 parts by weight of sodium hexametaphosphate, Dimethylformamide 1.5, catechol 2.5, sodium dodecylbenzene sulfonate 1.5, bisphenol A epoxy acrylate 14, EDTA disodium 1.5, additive 4.5, water 300. The auxiliary agent is made of the following raw materials in parts by weight (kg): polyoxyethylene sorbitan monooleate 3, nano-titanium dioxide 0.1, sodium tripolyphosphate 1, sodium silicate 2, urotropine 2 , hydroquinone 1, borax 3, urea 3, ammonium persulfate 1, peach gum 2, water 20; the preparation method is to dissolve ammonium persulfate in water, then add other remaining materials, stir for 10-15 minutes, and heat To 70-80 ℃, stirring reaction for 1-2 hours, that is.

[0010] The preparation method of the water-based ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a water-based normal-temperature rust-removal rust-proof liquid, which is prepared from the following active ingredients in parts by weight: 1-2 parts of zinc oxide, 2-3 parts of manganese dioxide, 2-3 parts of citric acid, 22-24 parts of E-12 epoxy resin, 6-8 parts of sodium hexametaphosphate, 1-2 parts of dimethyl formamide, 2-3 parts of catechol, 1-2 parts of sodium dodecyl benzene sulfonate, 13-15 parts of bisphenol A epoxy acrylate, 1-2 parts of disodium edetate dihydrate, 4-5 parts of auxiliaries and 300 parts of water. The rust-proof liquid can fast remove oil and rust at normal temperature, and can be corrosion-resistant and antibacterial, a thin film can be formed on a metal surface by using organic polymer resin and a chelating agent so as to isolate air and achieve the oxidization prevention effect, and the corrosion-inhibition and rust-proof effects are better, the thin film is easy to remove with water, thus being energy-saving and environment-friendly.

Description

technical field [0001] The invention relates to the technical field of rust prevention, in particular to a water-based room temperature rust removal and rust prevention liquid and a preparation method thereof. Background technique [0002] Rust prevention on metal surfaces is an important subject in industrial production. Traditional antirust liquids and antirust oils have both advantages and disadvantages. Ordinary anti-rust water contains a large amount of sodium nitrite, which is carcinogenic and is not conducive to environmental protection and human health. However, the use of humectants to prolong the life of anti-rust water brings the disadvantages of sticking hands and dust, and cannot prevent rust for a long time; Although the general dura-film anti-rust oil is suitable for long-term anti-rust, and the film is transparent and beautiful, there are few types of colorless and transparent resins, which are unstable and easy to oxidize and change color. They also need org...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C23G1/06C23C22/18
Inventor 沈泽文黄帅彭哲
Owner ANHUI PUYUAN SEPARATION MACHINERY MFG CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products