Matte black environment-friendly plasticizing ink

A kind of ink, environmental protection technology, applied in the field of printing ink, can solve the problem of ink usage limitation, and achieve the effect of reducing surface tension, good film formation, good bright effect

Active Publication Date: 2014-07-09
SUZHOU ANJIE TECH
View PDF2 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the use of these inks is increasingly restricted due to environmental, health and safety concerns

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Matte black environment-friendly plasticizing ink
  • Matte black environment-friendly plasticizing ink
  • Matte black environment-friendly plasticizing ink

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] The dumb black environment-friendly plasticizing ink described in the present embodiment contains the following components in parts by weight:

[0027]

[0028] The preparation method of the dumb black environment-friendly plasticized ink described in the present embodiment comprises the following steps:

[0029] (1) the silver powder of 4.0 parts by weight, the Seiko 1000-800 varnish of 12.5 parts by weight are mixed in a stirring mode to obtain the regulating material;

[0030] (2) 35.0 parts by weight of trimethylolpropane triacrylate and 30 parts by weight of mixed solvent are fully mixed and dissolved in a stirring manner to prepare a dispersion solution;

[0031] (3) 70 parts by weight of pigment black, 10.5 parts of pigment transparent red, 13.0 parts by weight of pigment transparent blue and the dispersion solution prepared in step (2) are fully mixed and moistened by stirring to obtain the first mixed liquid;

[0032] (4) 35.0 parts by weight of polymethyl...

Embodiment 2

[0036] The dumb black environment-friendly plasticizing ink described in the present embodiment contains the following components in parts by weight:

[0037]

[0038] The preparation method of the dumb black environment-friendly plasticized ink described in the present embodiment comprises the following steps:

[0039] (1) the silver powder of 4.8 parts by weight, the Seiko 1000-800 varnish of 15.2 parts by weight are mixed in a stirring mode to obtain the regulating material;

[0040] (2) 39.0 parts by weight of trimethylolpropane triacrylate and 32 parts by weight of mixed solvent are fully mixed and dissolved in a stirring manner to prepare a dispersion solution;

[0041] (3) 71.2 parts by weight of pigment black, 10.6 parts of pigment transparent red, 13.2 parts by weight of pigment transparent blue and the dispersion solution prepared in step (2) are fully mixed and wetted by stirring to obtain the first mixed liquid;

[0042] (4) Fully mix and dissolve 38.0 parts b...

Embodiment 3

[0046] The dumb black environment-friendly plasticizing ink described in the present embodiment contains the following components in parts by weight:

[0047]

[0048]

[0049] The preparation method of the dumb black environment-friendly plasticized ink described in the present embodiment comprises the following steps:

[0050] (1) the silver powder of 4.8 parts by weight, the Seiko 1000-800 varnish of 15.2 parts by weight are mixed in a stirring mode to obtain the regulating material;

[0051](2) 39.0 parts by weight of trimethylolpropane triacrylate and 32 parts by weight of mixed solvent are fully mixed and dissolved in a stirring manner to prepare a dispersion solution;

[0052] (3) 70.0 parts by weight of pigment black, 10.2 parts of pigment transparent red, 12.8 parts by weight of pigment transparent blue and the dispersion solution prepared in step (2) are fully mixed and moistened by stirring to obtain the first mixed liquid;

[0053] (4) Fully mix and dissolv...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a matte black environment-friendly plasticizing ink which contains the following components in parts by weight: 3-5 parts of silver powder, 10-16.5 parts of Seiko 1000-800 gloss oil, 70-72 parts of black pigment, 10.0-10.8 parts of transparent red pigment, 12.8-13.2 parts of transparent blue pigment, 32.0-40.0 parts of polymethyl methacrylate, 35.0-42.0 parts of trimethylolpropane triacrylate, 8.0-10.0 parts of stearin citrate and 65-75 parts of mixed solvent. The environment-friendly plasticizing ink is free of any phthalate or polyvinyl chloride resin plasticizer; and however, the environment-friendly plasticizing ink has equivalent flowing property to the prior art, and has favorable storage stability and favorable film-forming property.

Description

technical field [0001] The invention belongs to the technical field of printing ink, and more specifically, the invention relates to a kind of dumb black environment-friendly plasticized ink and a preparation method thereof. Background technique [0002] Ink is an important material for printing packaging materials. It expresses patterns and characters on the substrate through printing. The ink includes main components and auxiliary components. They are evenly mixed and rolled repeatedly to form a viscous colloidal fluid. Printing ink is a paste-like colloid formed by uniformly dispersing and mixing materials such as colorants, linking materials, additives, and solvents. The binder of solvent-based ink is composed of solid resin and a large amount of volatile organic solvent. After the solid resin is dissolved in the solvent, the coloring material is evenly dispersed in the binder, and after the ink is printed on the printing medium, the solvent quickly evaporates and dries...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D11/02C09D11/03C09D11/037
Inventor 王春生
Owner SUZHOU ANJIE TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More