Matt black plasticized ink

A kind of ink, environmental protection technology, applied in the field of printing ink, can solve the problem of ink use restriction, etc., achieve the effect of reducing surface tension, reducing dispersion time, and good film formation

Active Publication Date: 2016-02-24
SUZHOU ANJIE TECH
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the use of these inks is increasingly restricted due to environmental, health and safety concerns

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Matt black plasticized ink
  • Matt black plasticized ink
  • Matt black plasticized ink

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] The matte black environmentally friendly plasticizing ink described in this embodiment contains the following components by weight:

[0027]

[0028] The preparation method of the matt black environmentally friendly plasticizing ink in this embodiment includes the following steps:

[0029] (1) Mix 4.0 parts by weight of silver powder and 12.5 parts by weight of Seiko 1000-800 varnish uniformly to obtain a conditioning material;

[0030] (2) 35.0 parts by weight of trimethylolpropane triacrylate and 30 parts by weight of mixed solvent are thoroughly mixed and dissolved in a stirring manner to obtain a dispersion solution;

[0031] (3) 70 parts by weight of pigment black, 10.5 parts of pigment transparent red, 13.0 parts by weight of pigment transparent blue and the dispersion solution prepared in step (2) are thoroughly mixed and wetted by stirring to obtain the first mixture liquid;

[0032] (4) 35.0 parts by weight of polymethyl methacrylate and 35 parts by weight of mixed solv...

Embodiment 2

[0036] The matt black environmentally friendly plasticizing ink described in this embodiment contains the following components in parts by weight:

[0037]

[0038] The preparation method of the matt black environmentally friendly plasticizing ink described in this embodiment includes the following steps:

[0039] (1) 4.8 parts by weight of silver powder and 15.2 parts by weight of Seiko 1000-800 varnish are mixed uniformly to obtain a conditioning material;

[0040] (2) 39.0 parts by weight of trimethylolpropane triacrylate and 32 parts by weight of mixed solvent are thoroughly mixed and dissolved in a stirring manner to obtain a dispersion solution;

[0041] (3) 71.2 parts by weight of pigment black, 10.6 parts of pigment transparent red, 13.2 parts by weight of pigment transparent blue and the dispersion solution prepared in step (2) are thoroughly mixed and moistened by stirring to obtain the first mixture liquid;

[0042] (4) 38.0 parts by weight of polymethyl methacrylate and 39 ...

Embodiment 3

[0046] The matte black environmentally friendly plasticizing ink described in this embodiment contains the following components by weight:

[0047]

[0048]

[0049] The preparation method of the matt black environmentally friendly plasticizing ink in this embodiment includes the following steps:

[0050] (1) 4.8 parts by weight of silver powder and 15.2 parts by weight of Seiko 1000-800 varnish are mixed uniformly to obtain a conditioning material;

[0051] (2) 39.0 parts by weight of trimethylolpropane triacrylate and 32 parts by weight of mixed solvent are thoroughly mixed and dissolved in a stirring manner to obtain a dispersion solution;

[0052] (3) 70.0 parts by weight of pigment black, 10.2 parts of pigment transparent red, 12.8 parts by weight of pigment transparent blue and the dispersion solution prepared in step (2) are thoroughly mixed and moistened by stirring to obtain the first mixture liquid;

[0053] (4) 38.0 parts by weight of polymethyl methacrylate and 39 parts by ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a matte black environment-friendly plasticizing ink which contains the following components in parts by weight: 3-5 parts of silver powder, 10-16.5 parts of Seiko 1000-800 gloss oil, 70-72 parts of black pigment, 10.0-10.8 parts of transparent red pigment, 12.8-13.2 parts of transparent blue pigment, 32.0-40.0 parts of polymethyl methacrylate, 35.0-42.0 parts of trimethylolpropane triacrylate, 8.0-10.0 parts of stearin citrate and 65-75 parts of mixed solvent. The environment-friendly plasticizing ink is free of any phthalate or polyvinyl chloride resin plasticizer; and however, the environment-friendly plasticizing ink has equivalent flowing property to the prior art, and has favorable storage stability and favorable film-forming property.

Description

Technical field [0001] The invention belongs to the technical field of printing inks. More specifically, the invention relates to a matt black environmentally friendly plasticizing ink and a preparation method thereof. Background technique [0002] Ink is an important material used for printing packaging materials. It displays patterns and words on the substrate through printing. The ink includes the main and auxiliary components, which are uniformly mixed and repeatedly rolled to form a viscous colloidal fluid. Printing ink is a paste-like colloid formed by uniformly dispersing and mixing materials such as pigments, binders, additives and solvents. The binder of solvent-based ink is composed of solid resin and a large amount of volatile organic solvent. After the solid resin is dissolved in the solvent, the colorant is evenly dispersed in the binder. After the ink is printed on the printing medium, the solvent quickly evaporates to dry the conjunctiva. [0003] For inks, it is g...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C09D11/02C09D11/03C09D11/037
Inventor 王春生
Owner SUZHOU ANJIE TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap