A kind of processing method of far-infrared hollow thermal insulation yarn

A processing method, far-infrared technology, applied in the field of textile fabrics, can solve the problems of heavy thermal clothing, inconvenient wearing activities, lack of aesthetic feeling, etc., achieve good thermal performance, high practical value, and reduce the effect of winding speed

Active Publication Date: 2016-08-17
浙江春江轻纺集团有限责任公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The object of the present invention is to solve the problems of the prior art thermal clothing that are heavy, poor in air permeability, inconvenient to wear and lack of aesthetic feeling, and provide a woven clothing fabric that not only has good thermal performance, but also wears light, breathable and comfortable far-infrared hollow clothing. Thermal yarn and processing method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of processing method of far-infrared hollow thermal insulation yarn
  • A kind of processing method of far-infrared hollow thermal insulation yarn
  • A kind of processing method of far-infrared hollow thermal insulation yarn

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] A far-infrared hollow warm-keeping yarn, the far-infrared hollow warm-keeping yarn is composed of far-infrared hollow polyester fibers with a weight ratio of 80% and viscose fiber blended with 20%, and the specification of the far-infrared hollow polyester fibers is 1.56 dtex×38mm, the specification of the viscose fiber is 1.33dtex×38mm.

[0030] The processing method of far-infrared hollow thermal yarn includes cleaning, carding, drawing, roving, spun yarn and winding processes. Because the two fibers are chemical fibers, they have good uniformity and do not contain impurities, so thermal insulation fibers and Viscose fiber is directly mixed with raw materials in the blowing process according to the yarn forming ratio, and made into laps for production in the subsequent process. Its basic process flow is:

[0031] Far-infrared hollow polyester fiber / viscose fiber: A002C catching machine→A035A mixed cotton opener→A036 cotton opener→A092A cotton box feeder→A076C lapping...

Embodiment 2

[0066] The far-infrared hollow warm-keeping yarn of embodiment 2 is made of the far-infrared hollow polyester fiber of 80% by weight and the viscose fiber blend of 20%. The far-infrared material in the described far-infrared hollow polyester fiber is far-infrared ceramic powder, far The content of infrared ceramic powder is 10% of the total weight of the fiber, and the far-infrared radiation wavelength of the far-infrared ceramic powder is 4 μm-14 μm; the far-infrared hollow polyester fiber is a single-hole hollow polyester fiber, and the average value of the single-hole hollow polyester fiber is Hollow rate is 30%-40%, all the other are identical with embodiment 1. This embodiment adopts hollow polyester fiber, its heat retention performance and service life are significantly improved compared with Embodiment 1, and its heat retention rate reaches 31.2% in actual measurement, which is slightly improved compared with Embodiment 1.

Embodiment 3

[0068] Both ends of the single hole in the hollow polyester fiber in Example 3 are closed structures, and the length of the closed section is 0.5mm-1mm, and the rest are the same as in Example 2. This embodiment adopts hollow polyester fibers with a single hole and closed ends structure, and its heat retention performance and service life are significantly improved compared with Embodiment 2. The measured heat retention rate reaches 33.6%, which is significantly improved compared with Embodiment 2.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses far infrared hollow thermal yarns and a processing method. The far infrared hollow thermal yarns are processed by blending 75 to 85 weight percent of far infrared hollow polyester fibers and 15 to 25 weight percent of viscose fibers. The processing method comprises procedures of blowing, carding, drawing, roving, spinning and spooling. According to the far infrared hollow thermal yarns and the processing method, the problems of heaviness, poor air permeability, inconvenience for movement and lack of beauty of thermal garments in the prior art are effectively solved; a garment fabric woven from the yarns is high in thermal insulation property, light, air-permeable, comfortable and long in service life, and has high practical value.

Description

technical field [0001] The invention relates to the technical field of textile fabrics, in particular to a far-infrared hollow thermal yarn and a processing method thereof. Background technique [0002] Traditional winter cold clothing is mostly cotton-padded clothes, cotton-padded overcoats or sweaters plus down jackets and the like, which have the defects of bulkiness, bulkiness, inconvenient movement, and lack of aesthetic feeling. Along with the raising of social development and people's living standard, only relying on the thickness of adding and subtracting clothes to obtain warming effect, can't satisfy people's demand. In the 1990s, the emergence of "thermal underwear" made thermal clothing develop from outerwear to underwear, from the traditional "warm, thick, heavy, and swollen" to "warm, light, thin, and healthy". The warmth of textile and clothing is to block the conduction and convection of human body heat and the outside world. Early thermal underwear mostly ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D02G3/44D02G3/04
Inventor 蒋建清章水龙汪子鹏
Owner 浙江春江轻纺集团有限责任公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com