Anti-oxidation glass film-on and preparation method thereof
A glass film, oxidation-resistant technology, applied in the preparation of oxidation-resistant glass film installation solution, in the field of oxidation-resistant glass film installation solution, can solve problems such as inability to adapt, and achieve extended service life, improved oxidation resistance, and good oxidation resistance technology. effect of effect
Active Publication Date: 2014-08-20
宁波申山新材料科技有限公司
View PDF1 Cites 2 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
However, with the rapid development of science and technology, glass film has highlighted the function of heat insulation and energy saving while being safe and beautiful. A large number of functional films combined with metal and metal media are available, and barrier elements are added to product structure design. Therefore, the original The installation fluid can no longer meet the existing technical requirements
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreImage
Smart Image Click on the blue labels to locate them in the text.
Smart ImageViewing Examples
Examples
Experimental program
Comparison scheme
Effect test
Embodiment Construction
[0022] Below in conjunction with embodiment the present invention is further described.
[0023] Case 1:
[0024] Take 1000g of ultrapure water (resistance value greater than 15 megohms), add 2g of chelating agent (disodium ethylenediaminetetraacetate) to the ultrapure water, stir and heat up to 50C°, after completely dissolving, add antioxidant (benzene And triazole) 1g, stir while adding, until completely dissolving, then add surfactant (fatty alcohol polyoxyethylene ether) 8g, stir for 30 minutes, the above-mentioned solution is rapidly cooled to below 40C °, the pH value of test solution If the pH value is 7, select an appropriate amount of pH regulator (a mixture of citric acid and tartaric acid), and test it while dropping it until the solution pH = 7.5 to 8. After adding 1 g of preservatives (triazine compounds) and stirring evenly, then add Stir 1 g of antifungal agent (2-methyl-4-isothiazolin-3-one) evenly, and the preparation is completed to obtain the installation ...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More PUM
Login to View More Abstract
The invention relates to the technical field of a glass film-on and in particular relates to an anti-oxidation glass film-on. The anti-oxidation glass film-on comprises 1000 parts by weight of ultrapure water, and 2 parts by weight of chelating agent, 1 part by weight of anti-oxidant, 8 parts by weight of surfactant, 1 part by weight of preservative, 1 part by weight of mildew-proof agent and a proper amount of PH value regulator which are all added to the ultrapure water. The invention also discloses a preparation method of the anti-oxidation glass film-on. The anti-oxidation glass film-on obtained according to the formula and the process has an excellent anti-oxidation technical effect and is applied to the construction of a glass film containing an easily oxidizing noble metal layer, and a film glued by the anti-oxidation glass film-on is greatly improved in anti-oxidation performance and increased in service life.
Description
technical field [0001] The invention relates to the technical field of glass film-attaching installation liquid, in particular to an oxidation-resistant glass film-attaching installation liquid. At the same time, the invention also discloses a preparation method of the oxidation-resistant glass film-attaching installation liquid. Background technique [0002] The application of glass film in safety and energy saving can be traced back to the 1960s. It has been more than 40 years since 3M Company applied for the first glass film. Glass film can be divided into safety film, heat insulation film according to its function. Film, decorative film, widely used in automobiles, construction, electronic products, household appliances and other fields. [0003] At present, the glass film is installed by spraying installation liquid between the glass and the film pressure-sensitive adhesive during construction. This installation liquid is mainly composed of water, and an appropriate amo...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More Application Information
Patent Timeline
Login to View More Patent Type & Authority Applications(China)
IPC IPC(8): C03C23/00
Inventor 张虎寅郭继光
Owner 宁波申山新材料科技有限公司