The preparation method of rosin emulsifier
A technology of emulsifier and rosin, applied in chemical instruments and methods, chemical/physical process, chemical modification of natural resin, etc., can solve the problem of high production cost of rosin emulsifier, achieve good hydrophilic and lipophilic properties, small particle size , the effect of high emulsification and dispersion performance
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0013] Add 1 kg of rosin, 0.2 kg of ethanol and 0.5 kg of acrylic acid to the reaction kettle in sequence, heat and melt, raise the temperature to 150°C, stir and react for 3 hours to obtain acrylic modified rosin ester, cool to room temperature; add to acrylic modified rosin ester Heat and melt 0.15 kg of deionized water, heat up to 150°C, slowly add 48 g of octoxynol dropwise while stirring, and cool to room temperature at a stirring speed of 400 rpm to obtain a rosin emulsifier product.
Embodiment 2
[0015] Add 10 kg of rosin, 3 kg of ethanol and 5 kg of acrylic acid into the reaction kettle in turn, heat and melt, raise the temperature to 160°C, stir and react for 2 hours to obtain acrylic modified rosin ester, cool to room temperature; add to the acrylic modified rosin ester 2.4 kg of deionized water was heated and melted, and the temperature was raised to 160° C., 0.64 kg of octoxynol was slowly added dropwise while stirring, and cooled to room temperature at a stirring speed of 600 rpm to obtain a rosin emulsifier product.
Embodiment 3
[0017] Add 100 kg of rosin, 20 kg of ethanol and 40 kg of acrylic acid into the reaction kettle in sequence, heat and melt, raise the temperature to 155°C, stir and react for 2.5 hours to obtain acrylic modified rosin ester, cool to room temperature; add to acrylic modified rosin ester 0.15 kg of deionized water was heated and melted, and the temperature was raised to 155° C., and 6.6 kg of octoxynol was slowly added dropwise while stirring, and cooled to room temperature at a stirring speed of 500 rpm to obtain a rosin emulsifier product.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com