Mould-prevention polyethylene water supply tubular product and preparation method thereof
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A technology for water supply pipes and polyethylene, which is applied in the field of PE pipes and its preparation, can solve problems such as limiting the scope of application and reducing the service life of PE pipes, and achieves the effects of broad application prospects, prevention of mold adhesion and growth, and excellent mechanical properties
Inactive Publication Date: 2014-10-15
ANHUI DINGYUAN ZHENYUN PLASTIC
View PDF4 Cites 7 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
In recent years, with the rapid development of science and technology and the continuous improvement of people's living standards, the performance requirements of PE water supply pipes are getting higher and higher. Currently, PE water supply pipes on the market are easily damaged by mold erosion in humid environments. Greatly reduces the service life of the PE pipe and limits its application range
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment Construction
[0013] A anti-mold polyethylene water supply pipe, made of the following raw materials in weight (kg): medium density polyethylene 60, metallocene linear low density polyethylene 35, nylon 12 25, dimethyl fumarate 16, fluorine resin 6. Liquid paraffin 4, ethyl protocatechuate 1.5, propylparaben 2.5, dichlorovinyl salicylamide 2, antimony sulfate 3.5, jade powder 8, calcined loess 18 polyglycerol monolaurate 2.5, ten Zinc monoenoate 1.5, epoxy soybean oil 7, calcium stearate 1.5, barium stearate 1, filler masterbatch 22, dicyclohexyl phthalate 12, N,N'-di-sec-butyl-p-phenylene Diamine 2.5, tributyltin chloride 2;
[0014] The preparation method of the filler masterbatch is as follows: a. Weigh the raw materials with the following weight (kg): serpentine 42, diatomite 33, pyrophyllite 18, olivine 14, behenyloxypolydimethylsiloxane 2. Distearyloxy isopropyl aluminate 2.5, di-n-octyl phthalate 10, diisodecyl adipate 15, decyl tetradecyl cetyl stearate 2, di Polyoxypropylene ...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Property
Measurement
Unit
yield strength
aaaaa
aaaaa
compressive strength
aaaaa
aaaaa
Vicat softening point
aaaaa
aaaaa
Login to view more
Abstract
The invention discloses a mould-prevention polyethylene water supply tubular product and a preparation method thereof. The mould-prevention polyethylene water supply tubular product is prepared from the following raw materials in parts by weight: 50-70 parts of medium density polyethylene, 25-45 parts of metallocene linear low density polyethylene, 20-30 parts of nylon 12, 15-20 parts of dimethyl fumarate, 4-8 parts of perfluorinated polyether lubricating grease, 3-6 parts of liquid paraffin, 1-2 parts of protocatechuic acid ethyl ester, 2-3 parts of propylparaben, 1.5-2.5 parts of trichlamide, 2.5-4.5 parts of antimony sulfate, 5-10 parts of jade powder, 15-20 parts of calcining loess, 2-3 parts of dodecanoic acid monoester with triglycerol, 1-2 parts of zinc undecylenate, 5-10 parts of epoxidized soybean oil, 1-2 parts of calcium stearate, 1-2 parts of barium stearate, 20-25 parts of filling master batch, 10-15 parts of dicyclohexyl phthalate, 2-3 parts of N,N'-Bis(1-methylpropyl)-1,4-phenylenediamine and 1.5-2.5 parts of chlorotributyltin. The mould-prevention polyethylene water supply tubular product has excellent antibacterial property, can effectively restrain and prevent attachment and breeding of mould, prevents mould from corroding the tubular product, has excellent mechanical property, ageing resistance, heat resistance and processability, and is long in service life and wide in application prospect.
Description
technical field [0001] The invention relates to a PE pipe material and a preparation method thereof, in particular to a mildew-proof polyethylene water supply pipe material and a preparation method thereof. Background technique [0002] PE pipes are widely used in the field of water supply manufacturing because of their high strength, high temperature resistance, corrosion resistance, non-toxicity, and wear resistance. They are replacement products for traditional steel pipes and PVC drinking water pipes. In recent years, with the rapid development of science and technology and the continuous improvement of people's living standards, the performance requirements of PE water supply pipes are getting higher and higher. Currently, PE water supply pipes on the market are easily damaged by mold erosion in humid environments. The service life of the PE pipe is greatly reduced and its application range is limited. Therefore, be badly in need of developing a kind of mold-resistant ...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.