A kind of water-based antirust agent and its preparation method and application

A water-based rust inhibitor and rolling line technology, applied in the field of steel surface treatment, can solve the problems that the rust prevention requirements cannot be fully met, require several hours or even a day, and have no high-temperature rust prevention method, and achieve good economical efficiency and use. The method is simple and the effect of delaying the surface corrosion

Active Publication Date: 2016-04-13
WUKUN STEEL
View PDF6 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The normal temperature anti-rust agent is mainly used to process the finished steel at normal temperature. The steel bars need to be cleaned, degreased, soaked, passivated, and dried. There are still many occasions that require high-temperature anti-rust technology to achieve the purpose of anti-corrosion, that is, to directly treat the surface of high-temperature steel to improve the corrosion resistance of steel bars at room temperature
At present, high temperature antirust is difficult, therefore, there is no effective high temperature antirust method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of water-based antirust agent and its preparation method and application
  • A kind of water-based antirust agent and its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0025] The preparation method of water-based antirust agent of the present invention comprises following concrete steps:

[0026] (1) Determine the dosage of each component;

[0027] (2) Add gelatin to water and stir until it dissolves completely. The mass-to-volume ratio of gelatin to water (g:L) is 1:8~15; add alum to water and stir until it is completely dissolved. L) is 1:20~40; sodium dodecyl sulfonate is added to water and stirred until it is completely dissolved, and the mass-volume ratio of solid to liquid (g:L) is 1:6~15;

[0028] (3) Mix the above three solutions with water-soluble silicone oil evenly;

[0029] (4) Add water to constant volume to obtain the water-based antirust agent.

[0030] Gelatin is difficult to dissolve in water at normal temperature and pressure. The dissolution method adopted in this technical solution is to soak gelatin at room temperature for 10-30 minutes, and then fully stir in a constant temperature water bath at 65-70°C until it is co...

Embodiment 1

[0038] The formula of water-based antirust agent is: 30g / L gelatin, 3g / L alum, 20g / L sodium dodecylsulfonate, 20g / L water-soluble silicone oil, and the balance is water.

[0039] First soak 30g of gelatin at room temperature for 10min, add it into 250mL of water, and stir in a constant temperature water bath at 65°C until completely dissolved. Add 3g of alum into 120mL of water and stir until it is completely dissolved, add 20g of sodium dodecylsulfonate into 200mL of water and stir until it is completely dissolved. Thoroughly mix the above three solutions with 20 g of water-soluble silicone oil, add water to make the volume to 1 L, and obtain the water-based antirust agent.

[0040] The hot-rolled ribbed steel bar with a surface temperature of 200 ° C is completely immersed in the anti-rust agent for 10 seconds. After the anti-rust agent dries, a bright anti-rust film is formed on the surface of the steel bar.

Embodiment 2

[0042] The formula of water-based antirust agent is: 30g / L gelatin, 3g / L alum, 20g / L sodium dodecylsulfonate, 20g / L water-soluble silicone oil, and the balance is water.

[0043] Soak 30g of gelatin at room temperature for 20min, add 300mL of water, and stir in a constant temperature water bath at 65°C until completely dissolved; add 3g of alum in 100mL of water and stir until completely dissolved; add 20g of sodium dodecylsulfonate into 300mL of water Stir well until completely dissolved. Thoroughly mix the above three solutions with 20 g of water-soluble silicone oil, add water to make the volume to 1 L, and obtain the water-based antirust agent.

[0044] The hot-rolled ribbed steel bar with a surface temperature of 200 ° C is completely immersed in the anti-rust agent for 10 seconds. After the anti-rust agent dries, a bright anti-rust film is formed on the surface of the steel bar.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a water-based rust preventer and a preparation method and application thereof. The water-based rust preventer disclosed by the invention contains 30-50g / L of gelatin, 3-5g / L of alum, 20-30g / L of sodium dodecyl sulfonate, 20-30g / L of water-soluble silicone oil and the balance of water. The invention further discloses the preparation method of the water-based rust preventer and application of the water-based rust preventer in the rust prevention of hot-rolled ribbed steel bars. The rust preventer disclosed by the invention is convenient in use, good in rust prevention effect and low in cost, the condition that rusting cannot occur in an open-air environment under the conditions of being exposed to the wind, rain and sun can be maintained for 2-3 months, and the mechanical properties and welding performance of steel bars are not affected, so that the problem that the bearing capacity, durability and the like of reinforced concrete members are affected due to the fact that the existing hot-rolled ribbed steel bars severely rust is fundamentally solved.

Description

technical field [0001] The invention belongs to the technical field of steel surface treatment, and in particular relates to an environment-friendly high-temperature water-based antirust agent capable of delaying the corrosion of hot-rolled ribbed steel bars in an atmospheric environment, and a preparation method and application thereof. Background technique [0002] As construction steel, hot-rolled ribbed steel has always occupied a large proportion of my country's steel production and plays a vital role in the national economy. In recent years, in order to produce low-cost high-strength steel bars, the main method adopted by major iron and steel enterprises is the water cooling process after final rolling. This process can improve the structure to a certain extent and improve the mechanical properties of steel bars, but there is a big disadvantage in this process, that is, the hot-rolled ribbed steel bars cooled by water are easy to rust during storage and transportation,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C23F11/173
Inventor 陶俊赵宇张卫强苏宁陈涛孙肖媛郑玲
Owner WUKUN STEEL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com