Thermosetting shape memory resin capable of memorizing various shapes and preparation method thereof

A thermosetting and memory technology, applied in the application field of shape memory functionalization of high-performance resin-based composite materials, it can solve the problems of limited application scope and inability to achieve multi-stage deformation, and achieve high mechanical properties, high mechanical properties and temperature resistance. Effect

Active Publication Date: 2017-07-28
HARBIN INST OF TECH
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to solve the problem that the current thermosetting shape memory resin can only memorize a single shape, and cannot realize multi-stage deformation, so that its application range as a resin matrix for high-performance shape memory composite structural parts is limited. Shaped thermosetting shape memory resin and preparation method thereof

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Thermosetting shape memory resin capable of memorizing various shapes and preparation method thereof
  • Thermosetting shape memory resin capable of memorizing various shapes and preparation method thereof
  • Thermosetting shape memory resin capable of memorizing various shapes and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] In a three-necked flask equipped with mechanical stirring and a thermometer, add 1 mole of 4,4'bismaleimidodiphenylmethane and 0.5 mole of polyetheramine D400 into an appropriate amount of tetrahydrofuran, so that the polymer mass accounts for 20% of the total system mass. %, that is, the mass ratio of the total mass of bismaleimide and polyetheramine to tetrahydrofuran is 1:4, then stir and start heating to 65°C. After 24 hours of reaction, a homogeneous amber solution formed. Then the solution was cooled to room temperature, 0.5 mole of bisphenol A cyanate was added, and the stirring was accelerated until the bisphenol A cyanate was completely dissolved. The mixed solution is poured into a mold with a flat surface, placed in a vacuum oven, and vacuumed to remove air bubbles. After 5 minutes, the mold was taken out from the vacuum oven, and placed at room temperature to evaporate excess solvent in the solution. After 24 hours, put the mold in the oven, and make the r...

Embodiment 2

[0023] Add 1 mole of 4,4'bismaleimidodiphenylmethane and 1 mole of polyetheramine D400 into tetrahydrofuran in a three-necked flask equipped with mechanical stirring and a thermometer, so that the polymer mass accounts for 20% of the total system mass , then stir and begin heating to 65°C. After 24 hours of reaction, a homogeneous amber solution formed. Then the solution was cooled to room temperature, 1 mole of bisphenol A cyanate was added, and the stirring was accelerated until the bisphenol A cyanate was completely dissolved. The mixed solution is poured into a mold with a flat surface, placed in a vacuum oven, and vacuumed to remove air bubbles. After 5 minutes, the mold was taken out from the vacuum oven, and placed at room temperature to evaporate excess solvent in the solution. After 24 hours, put the mold in the oven, and make the resin fully react according to the curing conditions of 120°C / 0.5h, 150°C / 1h, 180°C / 1h, and 200°C / 2h. After the reaction is over, the ma...

Embodiment 3

[0025] Add 1 mole of 4,4'bismaleimidodiphenylmethane and 2 moles of polyetheramine D400 into tetrahydrofuran in a three-necked flask equipped with mechanical stirring and a thermometer, so that the polymer mass accounts for 20% of the total system mass , then stir and begin heating to 65°C. After 24 hours of reaction, a homogeneous amber solution formed. Then the solution was cooled to room temperature, 2 moles of bisphenol A cyanate was added, and the stirring was accelerated until the bisphenol A cyanate was completely dissolved. The mixed solution is poured into a mold with a flat surface, placed in a vacuum oven, and vacuumed to remove air bubbles. After 5 minutes, the mold was taken out from the vacuum oven, and placed at room temperature to evaporate excess solvent in the solution. After 24 hours, put the mold in the oven, and make the resin fully react according to the curing conditions of 120°C / 0.5h, 150°C / 1h, 180°C / 1h, and 200°C / 2h. After the reaction is over, the ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
glass transition temperatureaaaaaaaaaa
glass transition temperatureaaaaaaaaaa
glass transition temperatureaaaaaaaaaa
Login to view more

Abstract

The invention relates to a thermosetting shape memory resin capable of memorizing various shapes and a preparation method thereof. The method is as follows: first mix bismaleimide and polyetheramine and dissolve in tetrahydrofuran, and react at 65°C for 24 hours; when the solution is amber, add bisphenol A cyanate; Process parameters for the preparation of resin castings or shape memory composites. Polyetheramine can react with bismaleimide resin monomer to form a linear molecular skeleton and act as a reversible phase for resin deformation and recovery, which can not only realize the shape memory effect of the resin, but also improve its mechanical properties. Due to the existence of multiple cross-linking structures, the resin has a wide glass transition temperature range, so that the resin system can memorize different shapes at different temperatures, and can also maintain its high mechanical properties and temperature resistance level.

Description

technical field [0001] The invention belongs to the technical field of shape-memory functional application of high-performance resin-based composite materials, and relates to a thermosetting shape-memory resin capable of memorizing various shapes and a preparation method thereof. Background technique [0002] Smart material is a kind of material that can change its shape, mechanical properties, phase separation, surface morphology, permeability, etc. , optical properties and electrical properties of stress-sensitive materials. Smart materials make materials adapt to the external environment by changing their own composition or structure. Today, with the rapid development of aerospace technology, materials have a great role in promoting the development of aircraft. In this case, smart materials, as "new materials in the 21st century", have broad development space and play a significant role in promoting the progress of human civilization and the improvement of living standa...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C08J3/24C08L79/08C08K5/29C08G73/10
Inventor 冷劲松刘彦菊张启伟
Owner HARBIN INST OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka