Shape memory method based on order-disorder phase transition and used for semiconductor materials

A technology of semiconductors and ordered phases, applied in chemical instruments and methods, inorganic chemistry, silver compounds, etc., can solve problems that limit the application of shape memory materials

Active Publication Date: 2019-10-25
ZHEJIANG UNIV
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This also greatly limits the application of shape memory materials in the fields of microelectronics and electronic information.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Shape memory method based on order-disorder phase transition and used for semiconductor materials
  • Shape memory method based on order-disorder phase transition and used for semiconductor materials
  • Shape memory method based on order-disorder phase transition and used for semiconductor materials

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] Embodiment 1: the shape memory effect of nanowire section sample:

[0035] The first step is to prepare Ag by using focused ion beam micro-nano processing instrument 2 S nanowire cross-section sample and transferred to the heating chip, as figure 2 shown.

[0036] In the second step, the sample is heated to 10-20°C below the phase transition point of the sample (due to the nanoscale Ag 2 The α-β phase transition point of S decreases as its size decreases. At the same time, considering the convenience of rapid temperature rise across its phase transition point, the low-temperature phase holding temperature is usually 130-160 ° C. The preferred temperature for nanomaterials with a size of 45 nm is 155°C).

[0037] In the third step, the sample is rapidly heated until the phase transition is completed and becomes the BCC phase (due to the nanoscale Ag 2 The β-α phase transition point of S decreases as its size decreases. At the same time, considering the convenience o...

Embodiment 2

[0041] Embodiment 2: Shape regulation of nanowire cross section sample:

[0042] The first step is to prepare Ag by using focused ion beam micro-nano processing instrument 2 S nanowire cross-section samples and transferred to a heated chip.

[0043] In the second step, the sample is heated to 10-20°C lower than the phase transition point of the sample.

[0044] In the third step, the sample is rapidly heated until the phase changes to the BCC phase. Samples along [-101] α The direction is elongated by 1%-2%, and the shape changes.

[0045] The fourth step is to keep warm for more than 30 minutes. At this point the residual order is already at the noise level.

[0046] In the fifth step, the temperature is lowered so that the sample turns back to the monoclinic phase. At this time, the sample will no longer have the shape of the initial low-temperature phase, and the [-101] of the sample α The directions will be distributed in three equivalent directions with certain pro...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Phase transition pointaaaaaaaaaa
Login to view more

Abstract

The invention discloses a shape memory method based on order-disorder phase transition and used for semiconductor materials. According to the method, shape memory and shape control in the phase transition process are realized by controlling the heat preservation time of the disorder phase (high-temperature phase). In a temperature increasing-decreasing phase transition cycle of order-disorder phase transition, the shortest axis of the monoclinic phase can be remembered in the quick temperature increasing-decreasing cycle during order-disorder phase transition of monocrystal Ag2S from the low-temperature monoclinic phase to the high-temperature body-centered cubic phase, and therefore shape memory of the monoclinic phase is achieved. By prolonging the heat preservation time of the high-temperature phase, quasi-control over the position of the shortest axis can be achieved, and thus shape quasi-control is achieved. The method provides a feasible thought for shape memory of semiconductorswith order-disorder phase transition.

Description

technical field [0001] The invention belongs to the intersection field of shape memory effect and semiconductor, and relates to a shape memory semiconductor with order-disorder phase transition and a method for realizing its shape memory and shape control. Background technique [0002] In the Ag-S binary system, only Ag 2 S a compound. Between room temperature and melting point 842°C, Ag 2 S has three isomers: monoclinic α-Ag 2 S, body centered cubic phase β-Ag 2 S and face centered cubic phase γ-Ag 2 S. where α-Ag 2 S and β-Ag 2 The equilibrium phase transition point between S is 177°C. α-Ag 2 S is also called spiral pyrite, which belongs to the monoclinic crystal system. in α-Ag 2 S atoms in S have a distorted BCC (Body Centered Cubic) structure, and the plane formed by S atoms is perpendicular to the b-axis. in α-Ag 2 There are two types of Ag atoms in S, Ag I Occupying a position slightly off the plane, the Ag II Occupies between two planes. β-Ag 2 S is ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C01G5/00H01L45/00
CPCC01G5/00C01P2004/16C01P2004/04C01P2004/20H10N70/231H10N70/8822
Inventor 王勇刘军陈陆杨杭生张泽
Owner ZHEJIANG UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products