Anticorrosion primer for steel structure and preparation method thereof
An anti-corrosion primer and steel structure technology, applied in anti-corrosion coatings, coatings, etc., can solve the problems of low chemical resistance, low gloss, poor anti-corrosion effect, etc., achieve good protection and decoration, and prevent corrosion , the effect of strong chemical resistance
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0009] The present embodiment provides a kind of anticorrosion primer for steel structure, which contains the following components in parts by mass: 90 parts of high chlorinated polyethylene resin, 30 parts of polyvinyl acetate, 90 parts of chlorinated paraffin, 185 parts of turpentine, di 5 parts of iron, 8 parts of carbon fiber powder, 6 parts of bentonite, 0.5 parts of iron oxide red, 1.2 parts of dodecyl dimethyl tertiary amine.
[0010] The preparation steps of a kind of anticorrosion primer for steel structure are as follows: firstly mix high-chlorinated polyethylene resin, polyvinyl acetate and turpentine evenly, after the high-chlorinated polyethylene resin is dissolved, then mix with chlorinated paraffin, dioxygen trioxide Mix iron, carbon fiber powder, bentonite, iron oxide red and dodecyl dimethyl tertiary amine evenly to get the finished product.
Embodiment 2
[0012] The present embodiment provides a kind of anticorrosion primer for steel structure, which contains the following components in parts by mass: 100 parts of high chlorinated polyethylene resin, 35 parts of polyvinyl acetate, 100 parts of chlorinated paraffin, 200 parts of turpentine, dihydrogen trioxide 7 parts of iron, 10 parts of carbon fiber powder, 7 parts of bentonite, 1.5 parts of iron oxide red, 1.8 parts of dodecyl dimethyl tertiary amine.
[0013] The preparation steps of a kind of anticorrosion primer for steel structure are as follows: firstly mix high-chlorinated polyethylene resin, polyvinyl acetate and turpentine evenly, after the high-chlorinated polyethylene resin is dissolved, then mix with chlorinated paraffin, dioxygen trioxide Mix iron, carbon fiber powder, bentonite, iron oxide red and dodecyl dimethyl tertiary amine evenly to get the finished product.
Embodiment 3
[0015] The present embodiment provides a kind of anticorrosion primer for steel structure, which contains the following components in parts by mass: 110 parts of high chlorinated polyethylene resin, 45 parts of polyvinyl acetate, 105 parts of chlorinated paraffin, 210 parts of turpentine, 9 parts of iron, 13 parts of carbon fiber powder, 9 parts of bentonite, 2 parts of iron oxide red, 2.2 parts of dodecyl dimethyl tertiary amine.
[0016] The preparation steps of a kind of anticorrosion primer for steel structure are as follows: firstly mix high-chlorinated polyethylene resin, polyvinyl acetate and turpentine evenly, after the high-chlorinated polyethylene resin is dissolved, then mix with chlorinated paraffin, dioxygen trioxide Mix iron, carbon fiber powder, bentonite, iron oxide red and dodecyl dimethyl tertiary amine evenly to get the finished product.