Interior wall paint for construction
A technology for interior wall coatings and construction, applied in the field of coatings, can solve the problems of poor heat resistance, crack resistance, easy foaming, etc., and achieve good heat resistance and stability
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0015] A kind of interior wall paint for building, its raw material ratio is as follows by weight: 100 parts of polyvinyl alcohol resin; 20 parts of rosin; 45 parts of water glass; 30 parts of turpentine; 80 parts of water; 10 parts of ethanol; 20 parts of titanium dioxide ; 5 parts of wax; 40 parts of lithopone; 5 parts of tetrahydrofuran; 60 parts of light calcium carbonate; 1 part of silicon dioxide powder; 40 parts of talcum powder; 50 parts of toluene.
[0016] Put polyvinyl alcohol resin and water into the reactor, stir while heating to 90°C, add rosin, turpentine, ethanol, silica powder and toluene after the polyvinyl alcohol resin is completely dissolved, cool down to 30°C, add water glass After reacting for 0.8h, add titanium dioxide, light calcium carbonate and the remaining raw materials, and mix to obtain the finished product.
[0017] The solid content of the product is 30%, and the fineness is 60 μm; the surface is dry for 0.8 hours, and there is no foaming or sh...
Embodiment 2
[0019] A kind of interior wall paint for building, its raw material ratio is as follows by weight: 100 parts of polyvinyl alcohol resin; 30 parts of rosin; 55 parts of water glass; 40 parts of turpentine; 100 parts of water; 20 parts of ethanol; 10 parts of wax; 50 parts of lithopone; 10 parts of tetrahydrofuran; 80 parts of light calcium carbonate; 1 part of silicon dioxide powder; 60 parts of talcum powder; 60 parts of toluene.
[0020] Put polyvinyl alcohol resin and water into the reactor, stir while heating to 100°C, add rosin, turpentine, ethanol, silica powder and toluene after the polyvinyl alcohol resin is completely dissolved, cool down to 40°C, add water glass After reacting for 1.2 hours, add titanium dioxide, light calcium carbonate and the remaining raw materials, and mix to obtain the finished product.
[0021] The solid content of the product is 40%, and the fineness is 80 μm; the surface is dry for 0.5 hours, and there is no foaming or shedding after soaking i...
Embodiment 3
[0023] A kind of interior wall paint for building, its raw material ratio is as follows by weight: 100 parts of polyvinyl alcohol resin; 25 parts of rosin; 50 parts of water glass; 35 parts of turpentine; 90 parts of water; 15 parts of ethanol; 30 parts of titanium dioxide ; 7.5 parts of wax; 45 parts of lithopone; 8 parts of tetrahydrofuran; 70 parts of light calcium carbonate; 1 part of silicon dioxide powder; 50 parts of talcum powder; 55 parts of toluene.
[0024] Put polyvinyl alcohol resin and water into the reactor, stir while heating to 95°C, add rosin, turpentine, ethanol, silica powder and toluene after the polyvinyl alcohol resin is completely dissolved, cool down to 35°C, add water glass React for 1 hour, add titanium dioxide, light calcium carbonate and remaining raw materials, and mix to obtain the finished product.
[0025] The solid content of the product is 35%, and the fineness is 70μm; the surface is dry for 0.1h, and there is no foaming or shedding after so...
PUM
Property | Measurement | Unit |
---|---|---|
Fineness | aaaaa | aaaaa |
Fineness | aaaaa | aaaaa |
Fineness | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap