A technology of composite thermal insulation and dibutyl phthalate, which is applied in the field of composite thermal insulation boards, can solve the problems of thermal insulation board toughness, fire resistance performance, waterproof and thermal insulation effect, etc., and achieve good waterproof thermal insulation effect and excellent fire resistance performance , the effect of high toughness
Inactive Publication Date: 2014-12-17
SUZHOU CHANGXING CONSTR SCI TECH
View PDF4 Cites 1 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0002] Insulation board is a widely used building material, the current insulation boar
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0044] The composite insulation board consists of the following components by weight:
[0045] 3.4 parts whiskers calcium sulfate,
[0046] 8.9 parts polystyrene,
[0047] 3.4 parts low-alkali glass fiber,
[0048] 1.2 parts of aminopropyltriethoxysilane,
[0049] 8.9 parts of asbestos,
[0050] 1.2 parts of isomeric decanol polyoxyethylene ether,
[0051] 8.9 parts of sulphoaluminate cement,
[0052] 2.3 parts dibutyl phthalate.
Embodiment 2
[0054] The composite insulation board consists of the following components by weight:
[0055] 4 parts whiskers calcium sulfate,
[0056] 9 parts polystyrene,
[0057] 4 parts low-alkali fiberglass,
[0058] 2 parts aminopropyltriethoxysilane,
[0059] 9 parts asbestos,
[0060] 2 parts isomerized decanol ethoxylates,
[0061] 9 parts sulphoaluminate cement,
[0062] 3 parts dibutyl phthalate.
Embodiment 3
[0064] The composite insulation board consists of the following components by weight:
[0065] 3 parts whiskers calcium sulfate,
[0066] 8 parts polystyrene,
[0067] 3 parts low-alkali fiberglass,
[0068] 1 part aminopropyltriethoxysilane,
[0069] 8 parts asbestos,
[0070] 1 part Isodecanol Ethoxylates,
[0071] 8 parts sulphoaluminate cement,
[0072] 2 parts dibutyl phthalate.
[0073]
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention discloses a composite thermal insulation board. The composite thermal insulation board consists of the following components in parts by weight: 3-4 parts of crystal whisker calcium sulfate, 8-9 parts of polystyrene, 3-4 parts of low-alkaline glass fibers, 1-2 parts of aminopropyl triethoxysilane, 8-9 parts of asbestos, 1-2 parts of isodesyl alcohol polyoxyethylene ether, 8-9 parts of sulfate aluminum cement and 2-3 parts of dibutyl phthalate. The composite thermal insulation board is high in strength of thermal insulation core material, great in toughness, free of slag, excellent in flame resistance and good in waterproof thermal-insulation effect.
Description
technical field [0001] The invention relates to a composite thermal insulation board. Background technique [0002] Insulation boards are widely used building materials, but the current insulation boards are not ideal in toughness, fire resistance, waterproof and heat preservation. Contents of the invention [0003] The object of the present invention is to provide a composite thermal insulation board, the thermal insulation core material of which has high strength, high toughness, no slag drop, excellent fire resistance performance, and good waterproof and thermal insulation effect. [0004] In order to achieve the above object, the technical solution of the present invention is to design a composite insulation board, which consists of the following components in parts by weight: [0005] 3-4 parts whiskers calcium sulfate, [0006] 8 to 9 parts of polystyrene, [0007] 3 to 4 parts of low-alkali glass fiber, [0008] 1-2 parts of aminopropyltriethoxysilane, [0009]...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more 
Login to view more