Rosin-containing geogrid

A technology of geogrid and rosin, which is applied in the field of construction, can solve problems affecting on-site construction and later effects, and achieve the effects of overcoming uneven settlement, enhancing bearing capacity, and low elongation

Inactive Publication Date: 2015-01-07
ANHUI JIEAOMAKE SYNTHETIC MATERIAL TECH
View PDF3 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, the preparation of geogrid materials is relatively simple. Most of them are directly extruded with reinforcing agents such as high molecular polymers and carbon black. With the continuous development and progress of society, the research on soil environment, climate environment, etc. Or indirectly affect the on-site construction and post-effects, therefore, it is necessary to further improve the performance of the traditional simple geogrid;

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] A geogrid containing rosin, which is composed of the following raw materials in parts by weight:

[0024] High-density polypropylene 120, carboxylated graphene powder 10, cadmium stearate 0.2, maleic anhydride grafted polypropylene 10, rosin 2, lanolin 2, potassium bromate 0.3, sodium methylene dinaphthalene sulfonate 1.6, antioxidant Agent BHT0.4, Bamboo Charcoal Powder 2, Hexafluoroacetylacetone 0.4, Blast Furnace Slag 10, Rare Earth Additive 3, Paodium 1;

[0025] Described rare earth additive is made up of the following raw materials of weight part:

[0026] Boron carbide 40, rare earth chloride 6, attapulgite 18, silicic acid 15, aluminum tripolyphosphate 3, calcium acetate 2, phosphite 0.8, potassium carbonate 3, polyvinylpyrrolidone 0.4, silane coupling agent KH560 0.2,

[0027] Mix calcium acetate with attapulgite, ball mill evenly, add phosphite, keep stirring at 50°C for 10 minutes to obtain a mixture;

[0028] Add aluminum tripolyphosphate to 30 times of wa...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile yield strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a rosin-containing geogrid. The rosin-containing geogrid consists of the following raw materials in parts by weight: 107-120 parts of high-density polypropylene, 8-10 parts of carboxyl graphene powder, 0.1-0.2 part of cadmium stearate, 6-10 parts of maleic anhydride grafted polypropylene, 2-3 parts of rosin, 1-2 parts of lanolin, 0.1-0.3 part of potassium bromoflouride, 1-1.6 parts of dispersing agent NNO, 0.1-0.4 part of antioxidant BHT, 2-3 parts of bamboo carbon powder, 0.2-0.4 part of hexafluoro-acetylacetone, 7-10 parts of blast furnace slag, 2-3 parts of rare earth auxiliary and 1-2 parts of sodium silicate. The rare earth auxiliary added into the rosin containing geogrid is formed through the full mixing of high-strength boron carbide, attapulgite and rare earth elements, the cooperation of a calcium acetate antiseptic and a polyvinylpyrrolidone stabilizer and the surface treatment action of a silane coupling agent, so that the formed auxiliary is high in not only surface strength, tenacity, weatherability and corrosion resistance, but also stability. The comprehensive quality of the finished product can be effectively improved by the auxiliary, and the adaptability to soil and the resistance to external pressure are improved.

Description

technical field [0001] The invention mainly relates to the construction field, in particular to a geogrid containing rosin. Background technique [0002] At present, the preparation of geogrid materials is relatively simple. Most of them are directly extruded with reinforcing agents such as high molecular polymers and carbon black. With the continuous development and progress of society, the research on soil environment, climate environment, etc. Or indirectly affect the on-site construction and post-effects, therefore, it is necessary to further improve the performance of the traditional simple geogrid; [0003] Blast furnace slag is the waste discharged from the blast furnace when smelting pig iron. The main components are CaO, SiO2 and Al2O3. A lot of blast furnace slag waste is produced every year in my country. At present, it is widely used in roads, airports, foundation projects, railway ballast, Concrete aggregate and asphalt pavement, etc., but no blast furnace s...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/12C08L51/06C08L93/04C08K13/06C08K9/00C08K3/04C08K3/38C08K3/16C08K3/34C08K3/32C08K5/098C08K5/524C08K3/26
CPCC08L23/12C08L2205/035C08L51/06C08L93/04C08L39/06C08K13/06C08K9/06C08K3/38C08K3/346C08K3/04C08K5/098C08K3/16
Inventor 叶磊
Owner ANHUI JIEAOMAKE SYNTHETIC MATERIAL TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products