A kind of extra-thick specification x70 pipeline steel and its manufacturing method

A pipeline steel and specification technology, applied in the field of X70 submarine pipeline steel and its manufacturing, can solve the problems of shortened service period of pipeline steel, increase of cost, decline of pipeline steel, etc., to save straightening cost, improve production efficiency and stabilize production process Effect

Active Publication Date: 2016-08-17
JIANGYIN XINGCHENG SPECIAL STEEL WORKS CO LTD
View PDF5 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In addition, due to the harsh service environment of submarine steel, the strength, toughness, and plasticity of pipeline steel will decrease after a certain period of time, resulting in shortened service period and increased cost of pipeline steel. Therefore, improving the strain aging performance of submarine pipeline steel is also It is an urgent subject for those skilled in the art to explore

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of extra-thick specification x70 pipeline steel and its manufacturing method
  • A kind of extra-thick specification x70 pipeline steel and its manufacturing method
  • A kind of extra-thick specification x70 pipeline steel and its manufacturing method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] The thickness of the extra-thick X70 pipeline steel involved in this example is 31.8mm, and its chemical composition is calculated by mass percentage: C: 0.04%, Si: 0.2%, Mn: 1.44%, P: 0.009%, S: 0.002% , Nb: 0.045%, Ti: 0.017%, Ni: 0.2%, Cr: 0.10%, Cu: 0.16%, and the balance is Fe and unavoidable impurity elements.

[0033] The 31.8mm thick extra-thick X70 pipeline steel corresponds to the production furnace number S21104062. The manufacturing process is to configure the smelting raw materials according to the chemical composition of the above-mentioned extra-thick X70 pipeline steel, and then perform KR molten iron pretreatment in sequence to control the S content to 0.002%. , enter the converter after slag removal; double slag method is used in converter smelting to remove P, the content of P is 0.009%, and the content of C at the end of converter smelting is controlled to be 0.04%; blow argon for 10 minutes; then carry out LF refining and RH vacuum degassing, RH vac...

Embodiment 2

[0036] The thickness of the extra-thick specification X70 pipeline steel involved in this example is 31.8mm, and its chemical composition is calculated by mass percentage: C: 0.04%, Si: 0.15%, Mn: 1.44%, P: 0.007%, S: 0.002% , Nb: 0.045%, Ti: 0.017%, Ni: 0.2%, Cr: 0.10%, Cu: 0.16%, and the balance is Fe and unavoidable impurity elements.

[0037] The 31.8mm thick extra-thick X70 pipeline steel corresponds to the production furnace number S21104062. The manufacturing process is to configure the smelting raw materials according to the chemical composition of the above-mentioned extra-thick X70 pipeline steel, and then perform KR molten iron pretreatment in sequence to control the S content to 0.002%. , enter the converter after slag removal; double slag method is used in converter smelting to remove P, the content of P is 0.007%, and the content of C at the end of converter smelting is controlled to be 0.04%; blow argon for 15 minutes; then carry out LF refining and RH vacuum deg...

Embodiment 3

[0040] The thickness of the extra-thick specification X70 pipeline steel involved in this embodiment is 32 mm, and its chemical composition is calculated by mass percentage: C: 0.03%, Si: 0.24%, Mn: 1.43%, P: 0.009%, S: 0.0015%, Nb: 0.044%, Ti: 0.015%, Ni: 0.19%, Cr: 0.10%, Cu: 0.13%, and the balance is Fe and unavoidable impurity elements.

[0041] The 32mm thick extra-thick X70 pipeline steel corresponds to the production furnace number S21104060. Its manufacturing process is to configure the smelting raw materials according to the chemical composition of the above-mentioned extra-thick X70 pipeline steel, and then perform KR molten iron pretreatment in sequence to control the S content to 0.0015%. After slag removal, it enters the converter; the double slag method is used to remove P in the converter smelting, the content of P is 0.009%, and the content of C is controlled at the end of the converter smelting to 0.03%; blowing argon for 10 minutes; followed by LF refining and...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
yield strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses an extra-thick specification X70 pipeline steel and a manufacturing method thereof. The thickness of the pipeline steel is 30-32 mm, and its chemical components are C: 0.03-0.06%, Si: 0.1-0.30%, Mn in terms of mass percentage. : 1.30~1.60%, P: ≤0.010%, S: ≤0.0050%, Nb: 0.030~0.050%, Ti: 0.008~0.020%, Ni: 0.10~0.30%, Cr: 0.10~0.30%, Cu: 0.10~ 0.30%, the balance is Fe and inevitable impurity elements. The smelting raw materials are sequentially subjected to KR molten iron pretreatment, converter smelting, LF refining, and RH vacuum degassing to obtain molten steel with high purity. Pipeline steel with excellent toughness, low temperature aging resistance and HIC resistance.

Description

technical field [0001] The invention relates to X70 submarine pipeline steel and a manufacturing method thereof, in particular to an X70 pipeline steel with a thickness of more than 30 mm, a narrow strength range, excellent low-temperature toughness, HIC resistance, and low-temperature strain aging resistance and a manufacturing method thereof . Background technique [0002] With the rapid development of the world economy and the depletion of energy resources, the focus of oil and gas development has shifted from land to sea. Subsea oil and gas pipelines are the main components of offshore oil and gas field development and production systems. It is the fastest, safest and most efficient way to continuously transport large amounts of oil and gas An economical and reliable transportation method, it has been widely used in offshore oil transportation. For example, a 37,000Km ocean pipeline has been built in the US Gulf of Mexico, and the deepest gas pipeline reaches 2,900m. T...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C38/58C22C38/50C22C33/04C21D8/02B22D11/00
Inventor 李经涛刘朝霞林涛孙宪进蒋昌林方寿玉
Owner JIANGYIN XINGCHENG SPECIAL STEEL WORKS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com