A health-care bamboo and bamboo fiber technology, applied in the field of textiles, can solve the problems of softness and antibacterial properties of fiber materials to be improved, and achieve the effects of comfortable mood, high stability and dispersion performance, and high reactivity

Active Publication Date: 2016-06-01
FUJIAN KAISHIDA SPORTS APPL CO LTD
View PDF11 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

CN103556263A (2014-2-5) discloses a hollow bamboo charcoal viscose fiber and its production process, but the softness and bacteriostasis of the fiber material prepared by this method still need to be improved

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of health-care bamboo fiber fabric
  • A kind of health-care bamboo fiber fabric
  • A kind of health-care bamboo fiber fabric

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0045] Preparation of nano silver:

[0046] A. Add sodium dodecylsulfonate solution, water-based polyacrylate and hydrazine hydrate solution to silver nitrate aqueous solution to obtain a mixed solution, the molar ratio of sodium dodecylsulfonate to silver nitrate is 4:1; The molar ratio of acrylate to silver nitrate is 0.4:1; the molar ratio of hydrazine hydrate to silver nitrate is 0.2:1;

[0047] B. Add dicyclohexyl-18-crown-6 and sodium metaphosphate to the mixture, the molar ratio of dicyclohexyl-18-crown-6 to silver nitrate is 3:1; sodium metaphosphate and nitric acid The molar ratio of silver is 0.8:1, and the pH value is controlled to be 8-9 to obtain nano silver.

[0048] The composition proportioning of the antibacterial solution that is used for health care bamboo fiber fabric:

[0049] 25 parts of phthalic anhydride, 7 parts of furfuryl alcohol extracted from corncob residue, 10 parts of triethylene glycol, 15 parts of glutaric acid, 8 parts of butanetriol, 5 par...

Embodiment 2

[0067] Preparation of nano silver:

[0068] A. Add sodium dodecylsulfonate solution, water-based polyacrylate and hydrazine hydrate solution to silver nitrate aqueous solution to obtain a mixed solution, the molar ratio of sodium dodecylsulfonate to silver nitrate is 6:1; The molar ratio of acrylate to silver nitrate is 0.6:1; the molar ratio of hydrazine hydrate to silver nitrate is 0.3:1;

[0069] B. Add dicyclohexyl-18-crown-6 and sodium metaphosphate to the mixture, the molar ratio of dicyclohexyl-18-crown-6 to silver nitrate is 5:1; sodium metaphosphate and nitric acid The molar ratio of silver is 1.3:1, and the pH value is controlled to be 8-9 to obtain nano silver.

[0070] The composition proportioning of the antibacterial solution that is used for health care bamboo fiber fabric:

[0071] 35 parts of phthalic anhydride, 11 parts of furfuryl alcohol extracted from oat or wheat bran, 12 parts of triethylene glycol, 18 parts of glutaric acid, 10 parts of butanetriol, 7...

Embodiment 3

[0088] Preparation of nano silver:

[0089] A. Add sodium dodecylsulfonate solution, water-based polyacrylate and hydrazine hydrate solution to silver nitrate aqueous solution to obtain a mixed solution, the molar ratio of sodium dodecylsulfonate to silver nitrate is 5:1; The molar ratio of acrylate to silver nitrate is 0.5:1; the molar ratio of hydrazine hydrate to silver nitrate is 0.25:1;

[0090] B. Add dicyclohexyl-18-crown-6 and sodium metaphosphate to the mixture, the molar ratio of dicyclohexyl-18-crown-6 to silver nitrate is 4:1; sodium metaphosphate and nitric acid The molar ratio of silver is 1:1, and the pH value is controlled to be 8-9 to obtain nano silver.

[0091] The composition proportioning that is used for the antibacterial solution of bamboo fiber fabric:

[0092] 30 parts of phthalic anhydride, 7-11 parts of furfuryl alcohol extracted from bamboo sawdust, 11 parts of triethylene glycol, 16 parts of glutaric acid, 9 parts of butanetriol, 6 parts of zinc ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention relates to a textile, in particular to a health care bamboo fiber fabric. The health care bamboo fiber fabric is prepared by the following steps: antibacterial bamboo fiber preparation: electrostatically spraying antibacterial solution onto a bamboo fiber surface and then carrying out microwave treatment; dyeing; color spinning processing; jacquard; printing. The antibacterial solution comprises the following raw materials in parts by weight: 25-35 parts of phthalic anhydride, 7-11 parts of furfuryl alcohol extracted from natural plants, 10-12 parts of triethylene glycol, 15-18 parts of glutaric acid, 8-10 parts of butantriol, 5-7 parts of zinc oxide, 3-5 parts of magnesium oxide, 15-25 parts of chloroprene rubber, 70-95 parts of elastic rubber, 2-3 parts of softening oil, 15-20 parts of dimethyl carbonate, 1-3 parts of benzoyl peroxide, 4-8 parts of ethyl acetate, 1-4 parts of emulsifying agent, 20-30 parts of chitosan, 0.3-0.7 part of tourmaline particle, 0.2-0.6 part of negative ion powder, 0.1-0.4 parts of flexible magnet massage bead, 5*10-5-9*10-5 parts of nano silver, 1-3 parts of fire retardant, 10-14 parts of methylcellulose and 20-40 parts of deionized water. The health care bamboo fiber fabric for home textile, which is prepared, is good in softness, antibacterial activity and health care effect.

Description

technical field [0001] The invention relates to a textile, in particular to a health-care bamboo fiber fabric. Background technique [0002] Bamboo charcoal has good deodorizing, anti-corrosion, and odor-absorbing functions. Nano-scale bamboo charcoal powder also has antibacterial and bactericidal effects, as well as far-infrared and negative ion properties. CN103556263A (2014-2-5) discloses a hollow bamboo charcoal viscose fiber and its production process, but the softness and bacteriostasis of the fiber material prepared by this method still need to be improved. Contents of the invention [0003] The purpose of the invention is to provide a kind of health-care bamboo fiber fabric with good softness and antibacterial property. [0004] Above-mentioned technical purpose of the present invention is achieved through the following technical solutions: [0005] A health-care bamboo fiber fabric is characterized in that it is prepared through the following steps: [0006] (...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): D06M10/08D06M10/10D06M13/11D06M15/693D06M15/03D06M11/80D06M11/83D06M11/74D06M15/263D06M15/564D06M15/333D06M15/227D06M13/188D06M11/79D06M11/46D06M11/71D06M13/175D06P3/60D06P1/22D06P1/16B41M1/26D06M101/04
Inventor 丁建中
Owner FUJIAN KAISHIDA SPORTS APPL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap