Preparation method of single fired glass ceramic composite board

A technology of glass-ceramic and glass-ceramic frit, which is applied in the field of architectural ceramics, can solve the problems of poor flatness, easy damage, deformation, and deformation of products, and achieve the effect of increasing the rate of qualified products and improving the flatness

Active Publication Date: 2015-01-21
金湖县综合检验检测中心
View PDF2 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In the one-time firing process, the solvent in the adhesive will penetrate into the adobe, and the adobe will deform when more solvent is absorbed, and it will be easily damaged and deformed in the subsequent transportation, and the flatness of the fired product will also deteriorate. affect product quality

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of single fired glass ceramic composite board
  • Preparation method of single fired glass ceramic composite board
  • Preparation method of single fired glass ceramic composite board

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0027] Preparation of the bottom glaze: kaolin, quartz, potassium feldspar, albite, calcite, talc, dolomite, zinc oxide, zircon powder, pyrophyllite with a thickness of less than 100 meshes are mixed by ball milling as raw materials for the bottom glaze, and an appropriate amount of water and 0.5 % sodium tripolyphosphate, 0.3% methyl cellulose, the chemical composition of the bottom glaze is SiO2: 50%, Al2O3: 20%, CaO: 9%, MgO: 2%, K2O: 2%, Na2O: 3%, ZnO: 4%, ZrO2: 10%, and the slurry bottom glaze whose fineness is 0.5% of the 10,000-hole sieve is for use.

[0028] The pyrophyllite in the bottom glaze has good water absorption, which can alleviate the deformation of the green body caused by the solvent in the suspension liquid penetrating into the green body. Usually, the pyrophyllite is 3-5% of the mass of the dry material of the bottom glaze.

[0029] It should be noted that the preparation of green body powder, micropowder formula components and bottom glaze given here can...

Embodiment 1-1

[0034] The glass-ceramic frit particle of 375kg silver-white ice crystal effect (purchase from Quincy Caroby Glaze Company, fineness 70 orders) is added in the frit particle binder of 125kg that embodiment group 1 makes, mix homogeneously , to obtain glass-ceramic frit particle suspension, the solid content of glass-ceramic frit particles is 75%, no visible bubbles, the flow rate is 45.3s (30 ℃, coated with -4 cups), and there is still no stratification after the suspension is placed for 5 days , it can be seen that the frit particle binder of the present invention still has good stability after mixing with the glass-ceramic frit particles. It should be noted that the glass-ceramic frit particles with silver-white ice crystal effect selected in Example 1-1 spread during the sintering process, forming the effect of silver-white ice crystal flowers on the glaze layer, and the glass-ceramic frit particles It can be purchased through the color glaze company, and similar frit produ...

Embodiment 2

[0045] Components of every 100kg frit particle binder: nonionic polyurethane associative thickener (Nae Woi Korea., Ltd. company, model HIRESOL85) content is added as shown in Table 1, attapulgite clay 2.0kg, polyether Type GPE defoamer (purchased from Hangzhou Phil Chemical Industry Co., Ltd.) 1kg, sodium tripolyphosphate 1.6kg, and the balance is water.

[0046] 350kg has the glass-ceramic frit particle of milky white ice crystal effect (purchasing from Quincy Carroby Glaze Company, fineness 110 orders) is added in the frit particle binder of 150kg that embodiment 2 makes, mix homogeneously, A glass-ceramic frit particle suspension was obtained. The solid content of the glass-ceramic frit particles was 70%, and there were no visible bubbles. The suspension was left for 5 days. See Table 2 for the flow rate and stratification.

[0047] Table 2 Research on the amount of nonionic polyurethane associative thickener added

[0048]

[0049] From Table 2, the addition amount of...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention provides a preparation method of a single fired glass ceramic composite board. The preparation method comprises the following steps: A, green body punch forming; B, glazing and printing, wherein the glaze contains 3-5% of pyrophyllite by mass; C, spraying of a layer of glass ceramic frit suspension, and spraying a layer of glass ceramic frit suspension onto the surface of the green body in the step B, wherein the glass ceramic frit suspension is prepared by mixing glass ceramic frits with polyurethane binders and the polyurethane binders are prepared from the following components by mass fraction: 3.8-4.8% of nonionic polyurethane associative thickening agent, 1.8-2.4% of attapulgite clay, 0.6-1% of defoaming agent, 0.6-1.6% of dispersing agents and the balance of solvents; D, firing, namely feeding the green body into a kiln and firing at a temperature of 1150-1250 DEG C; and E, polishing and edging processing, thus obtaining the finished product of the glass ceramic composite board. The preparation method has the beneficial effects that the adverse effects of a preheating zone of the kiln on the adsorption effects of the glass ceramic frits can be avoided and the product yield can be increased.

Description

technical field [0001] The invention relates to the technical field of building ceramics, in particular to a preparation method of a once-firing glass-ceramic composite plate. Background technique [0002] The glass-ceramic composite board is a new type of composite board that combines a layer of glass-ceramic on the surface of the ceramic tile. Because the surface is a glass-ceramic layer, it is completely antifouling and easy to clean and maintain. At present, glass-ceramics frits are mainly covered with a certain thickness of glass-ceramics frits (particle size is 15-150 mesh) on the body surface or glaze surface by means of cloth, and a layer of adhesive is sprayed to fix the particles. On the surface of the green body, after firing, the glazed surface is reprocessed. The quality of the glass-ceramic frit directly determines the flatness of the brick and the decorative effect of the brick. The binder used in the prior art is only ordinary glue and The water is mixed acc...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B41/89
Inventor 朱培祺朱丽萍岑永炽张远强刘丹
Owner 金湖县综合检验检测中心
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com