A cement grinding aid and reinforced technology, applied in the field of reinforced cement grinding aid, can solve the problems of macromolecular polydispersity, non-uniformity of physical and chemical properties, underutilization, and structural complexity, etc. The effect of increasing the output per hour, improving the gradation and increasing the fluidity of the material

Active Publication Date: 2015-03-11
GUILIN HUAYUE ENVIRONMENTAL PROTECTION TECH CO LTD
View PDF6 Cites 22 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Lignin, a natural high-molecular compound with huge yield, renewable and biodegradable, has not been fully and effectively utilized due to its complex structure, polydispersity of macromolecules and heterogeneity of physical and chemical properties.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Reinforced cement grinding aid

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] The following raw materials are weighed according to the weight ratio: diethanol monoisopropanolamine 10kg, triethanolamine 5kg, sodium acetate 4kg, sodium thiosulfate 10kg, sodium chloride 12kg, sodium carboxymethylcellulose 4kg, papermaking black liquor 18kg , Mix and stir for 30 minutes to obtain the enhanced cement grinding aid product.

Embodiment 2

[0016] The following raw materials are weighed according to the weight ratio: 15kg of diethanol monoisopropanolamine, 3kg of triethanolamine, 6kg of sodium acetate, 6kg of sodium thiosulfate, 10kg of sodium chloride, 5kg of sodium carboxymethylcellulose, and 15kg of papermaking black liquor , Mix and stir for 30 minutes to obtain the enhanced cement grinding aid product.

Embodiment 3

[0018] The following raw materials are weighed according to the weight ratio: diethanol monoisopropanolamine 12kg, triethanolamine 4kg, sodium acetate 5kg, sodium thiosulfate 8kg, sodium chloride 11kg, sodium carboxymethylcellulose 6kg, papermaking black liquor 16kg , Mix and stir for 30 minutes to obtain the enhanced cement grinding aid product.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a reinforced cement grinding aid which comprises the following ingredients in parts by weight: 10-15 parts of diethanolisopropanolamine, 3-5 parts of triethanolamine, 4-6 parts of sodium acetate, 6-10 parts of sodium thiosulfate, 10-12 parts of sodium chloride, 4-6 parts of sodium carboxymethylcellulose and 15-18 parts of papermaking black liquid. The reinforced cement grinding aid is low in mixing amount, good in reinforcement effect and low in cost.

Description

technical field [0001] The invention belongs to the technical field of cement production and processing, and in particular relates to an enhanced cement grinding aid. Background technique [0002] Cement grinding aid is a chemical admixture to improve the grinding efficiency of the mill and improve the performance of cement. It is generally added directly to the cement mill or added to the cement clinker into the grinding belt, and mixed with cement clinker or other materials together into the cement mill for grinding. After the grinding aid enters the mill with the cement clinker, it is adsorbed on the surface and cracks of the material particles. Due to the polar molecular structure of the grinding aid, the foreign ions provided by it neutralize the electrostatic charge generated by the friction of the cement clinker during the grinding process, reducing the ability of fine particles to aggregate and making the clinker The particles are separated from the grinding medium...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B24/38
Inventor 尹丹黄煌陈威王恒阮长泰
Owner GUILIN HUAYUE ENVIRONMENTAL PROTECTION TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap