A mud and material preparation technology, which is applied in the field of preparation of mud hanging images, can solve the problems of small thickness, large area to thickness ratio, and large area, and achieve the effect of controllable color, beautiful hanging images, and simple and generous colors

Inactive Publication Date: 2016-08-24
闫吉平
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The present invention is aimed at the deficiencies in the prior art. The inventor of this patent tries to use muddy materials to make hanging images. Traditional clear mud is generally made into smaller clear mud inkstone products, but hanging images generally require a relatively small thickness and relatively small area. Large, the thickness is generally 2-10cm, and the area is greater than 800cm 2 , due to the large ratio of area to thickness, there will be a large proportion of cracking and deformation when firing large-area and low-thickness hanging images made of clay materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0034] What the inventor's embodiment made is the holy image of Jesus, the thickness of the statue is 2-5cm, and the area is 800-10000cm 2 Variety, the method of preparation of the clay statue of Jesus,

[0035] The first step is to prepare materials

[0036] Select the following materials in parts by mass:

[0037] 10-20 parts of cement

[0038] Kaolin 40-40 parts,

[0039] Bauxite 20-30 parts

[0040] 5-10 parts of ferric oxide,

[0041] 2-5 parts of chromium oxide

[0042] The second step and mud

[0043] Select the deep well iron-rich molten iron and the raw materials and mud prepared in the first step of the step, and use a high-strength vacuum mud mixer to refine the mud, and the mud is evenly removed from the air bubbles. The advantage of using deep well rich iron-rich water is that the hardness of the water is high, and the color of the finished product after subsequent firing is good;

[0044] The third step embryo making

[0045] Put the mud ball into the mol...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
areaaaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method of an argillaceous hung image. The argillaceous hung image is prepared by selecting raw materials including plaster, kaolin, bauxite, iron trioxide and chromic oxide in a proper proportion, mixing, making a blank, firing, post-processing and the like. After being verified, the yield of a fired product can be above 85%; the argillaceous hung image can be made into a Jesus icon, a leader hung image and the like; and the argillaceous hung image is primitive, simple and generous in colour and is applied to being used as a hung image.

Description

technical field [0001] The invention belongs to the technical field of clay product preparation, and in particular relates to a method for preparing a clay hanging image. Background technique [0002] Statues of Jesus, hanging images of leaders, etc. are generally made of paper or plaster. Paper hanging images cannot be made into three-dimensional relief shapes. Large-area and low-thickness hanging images made of plaster products, if they are white and single in color, if they are processed into other colors It needs to be dyed, and it is not solemn enough. Contents of the invention [0003] The present invention is aimed at the deficiencies in the prior art. The inventor of this patent tries to use muddy materials to make hanging images. Traditional clear mud is generally made into smaller clear mud inkstone products, but hanging images generally require a relatively small thickness and relatively small area. Large, the thickness is generally 2-10cm, and the area is grea...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine