Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A resin coating and resin technology, applied in the coating and other directions, can solve the problems of poor adhesion of moisture-proof resin coatings, and achieve the effect of superior moisture-proof ability
Inactive Publication Date: 2015-03-25
SUZHOU MINGXUAN FLOORING COATINGS
View PDF4 Cites 10 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0003] The technical problem mainly solved by the present invention is to provide a kind of moisture-proof resin coating, which solves the problem of poor adhesion of moisture-proof resin coating
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0016] Embodiment 1 of the present invention comprises: a kind of moisture-proof resin coating, comprises the composition of following content ratio:
[0017] Cycloolefin copolymer 3 parts
[0018] Chlorinated polypropylene resin 5 parts
[0019] 3 parts tributyl phosphate
[0020] 8 parts wood glue powder
[0021] Lithium magnesium silicate 2 parts
[0022] Calcium carbonate 12 parts
[0023] Bamboo charcoal powder 0.4 parts
[0024] Dispersant 0.2 parts
[0025] Thickener 0.1 parts.
Embodiment 2
[0026] Embodiment 2 of the present invention comprises: a kind of moisture-proof resin coating, comprises the composition of following content ratio:
[0027] Cycloolefin copolymer 5 parts
[0028] Chlorinated polypropylene resin 8 parts
[0029] 3.5 parts of tributyl phosphate
[0030] 10 parts wood glue powder
[0031] 3 parts lithium magnesium silicate
[0032] Calcium carbonate 24 parts
[0033] Bamboo charcoal powder 0.6 parts
[0034] Dispersant 0.25 parts
[0035] Thickener 0.3 parts.
Embodiment 3
[0036] Embodiment 3 of the present invention comprises: a kind of moisture-proof resin paint, comprises the composition of following content ratio:
[0037] Cycloolefin copolymer 8 parts
[0038] Chlorinated polypropylene resin 12 parts
[0039] 4 parts tributyl phosphate
[0040] 12 parts wood glue powder
[0041] Lithium magnesium silicate 4 parts
[0042] Calcium carbonate 34 parts
[0043] Bamboo charcoal powder 0.7 parts
[0044] Dispersant 0.3 parts
[0045] Thickener 0.5 parts.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention discloses a damp-proof resin coating. The damp-proof resin coating comprises components with the following content proportions: 3-8 parts of a cyclic olefin copolymer, 5-12 parts of chlorinated polypropylene resin, 3-4 parts of tributyl phosphate, 8-12 parts of wood adhesive powder, 2-4 parts of lithium magnesium silicate, 12-34 parts of calcium carbonate, 0.4-0.7 part of bamboo charcoal powder, 0.2-0.3 part of a dispersing agent and 0.1-0.5 part of a thickening agent. By virtue of the mode, the damp-proof resin coating disclosed by the invention can be well adhered to various bottom materials; and moreover, the damp-proof resin coating is excellent in damp-proof ability, and peeling and fading phenomena cannot be caused by other external factors.
Description
technical field [0001] The invention relates to the field of architectural coatings, in particular to a moisture-proof resin coating. Background technique [0002] Moisture-proof coatings are mainly used for materials that are easy to absorb moisture, such as: paper, stones, bricks, cement, ceramics, silica-reinforced quartz fiber composite materials, etc. Negative effects caused by moisture absorption. At present, the main moisture-proof coatings on the market include polyurethane systems, acrylic resin systems, and organic-inorganic composite moisture-proof coatings. However, most moisture-proof coatings have poor adhesion, especially on metal surfaces, and are prone to peeling off. Contents of the invention [0003] The technical problem mainly solved by the invention is to provide a moisture-proof resin coating, which solves the problem of poor adhesion of the moisture-proof resin coating. [0004] In order to solve the above-mentioned technical problems, a technica...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more 
Login to view more