Light-weight reinforced gypsum plaster board and preparation method thereof

A paper surface gypsum board, gypsum board technology, applied in the field of gypsum board for construction, can solve the problems of increasing production, transportation and construction costs, increasing the quality of board per unit area, wasting resources, etc., to improve the strength and bonding performance, improve The effect of damp bonding quality and improving the workability of slurry

Active Publication Date: 2015-04-01
BEIJING NEW BUILDING MATERIALS PLC
View PDF6 Cites 33 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, domestic desulfurized gypsum generally has a concentrated particle size distribution, low grade, and high harmful impurities, resulting in poor workability and water retention of the slurry made in the production process of gypsum boards, which increases the difficulty of controlling the production process of gypsum boards. Seriously affects the strength and bonding quality of gypsum board products
At present, most of the domestic gypsum board production lines solve this problem

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Light-weight reinforced gypsum plaster board and preparation method thereof
  • Light-weight reinforced gypsum plaster board and preparation method thereof
  • Light-weight reinforced gypsum plaster board and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] Weigh each raw material according to the following parts by weight: gypsum clinker: 100 parts; modified starch: 1 part; foaming agent: 0.1 part; rice straw fiber powder: 8 parts; CMC powder: 0.5 part; water: 80 parts .

[0035] Prepare lightweight reinforced gypsum board as follows:

[0036] 1) Add the gypsum clinker and rice straw fiber powder to the mixing reamer and mix thoroughly, then enter the mixer, then add the CMC powder and modified starch to the mixer in turn, and continue to stir evenly;

[0037] 2) The blowing agent is mixed with part of the water, the weight of the blowing agent is 1.2% of the weight of the water, and the blowing agent solution is foamed through the foaming system, and then also enters the mixer;

[0038] 3) The raw materials are fully stirred in the mixer to obtain a uniform slurry, which is continuously poured between two layers of cardboard and extruded to obtain a wet gypsum board;

[0039] 4) The wet gypsum board is solidified, cut,...

Embodiment 2

[0041] Weigh each raw material according to the following parts by weight: gypsum clinker: 100 parts; modified starch: 0.2 part; foaming agent: 0.02 part; rice straw fiber powder: 5 parts; CMC powder: 0.1 part; water: 60 parts .

[0042] Prepare lightweight reinforced gypsum board as follows:

[0043] 1) Add the gypsum clinker and rice straw fiber powder to the mixing reamer and mix thoroughly, then enter the mixer, then add the CMC powder and modified starch to the mixer in turn, and continue to stir evenly;

[0044] 2) The blowing agent is mixed with part of the water, the weight of the blowing agent is 1.2% of the weight of the water, and the blowing agent solution is foamed through the foaming system, and then also enters the mixer;

[0045] 3) The raw materials are fully stirred in the mixer to obtain a uniform slurry, which is continuously poured between two layers of cardboard and extruded to obtain a wet gypsum board;

[0046]4) The wet gypsum board is solidified, cu...

Embodiment 3

[0048] Weigh each raw material according to the following parts by weight: gypsum clinker: 100 parts; modified starch: 0.5 parts; foaming agent: 0.04 parts; rice straw fiber powder: 8 parts; CMC powder: 0.2 parts; water: 75 parts .

[0049] Prepare lightweight reinforced gypsum board as follows:

[0050] 1) Add the gypsum clinker and rice straw fiber powder to the mixing reamer and mix thoroughly, then enter the mixer, then add the CMC powder and modified starch to the mixer in turn, and continue to stir evenly;

[0051] 2) The blowing agent is mixed with part of the water, the weight of the blowing agent is 1.2% of the weight of the water, and the blowing agent solution is foamed through the foaming system, and then also enters the mixer;

[0052] 3) The raw materials are fully stirred in the mixer to obtain a uniform slurry, which is continuously poured between two layers of cardboard and extruded to obtain a wet gypsum board;

[0053] 4) The wet gypsum board is solidified...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a light-weight reinforced gypsum plaster board and a preparation method thereof. The light-weight reinforced gypsum plaster board is prepared from the following raw materials in parts by weight: 100 parts of a gypsum clinker, 0.1-1 part of modified starch, 0.01-0.1 part of a foaming agent, 2-10 parts of rice straw fiber powder, 0.1-0.6 part of CMC (carboxyl methy cellulose) powder and 50-100 parts of water. By adding the rice straw fiber powder and the CMC powder, the workability of slurry is improved, the problems of low grade and low strength of desulfurization gypsum are solved, and particularly the rice straw fiber powder has an adsorption effect on Cl, so that the wetting bond quality of the gypsum plaster board is greatly improved; meanwhile, the consumption of the desulfurization gypsum and the foaming agent is reduced, and the strength and bond performance of the board are improved; the prepared gypsum plaster board is good in wetting bond performance, the mass per unit area of a 9.5mm waterproof board is 6.4kg/m<2> which is far superior to a national standard requirement that the mass per unit area is not less than 9.5kg/m<2>; and the average value of the transverse breaking load is 216.5N, the minimum value of the transverse breaking load is 202.6, the average value of the longitudinal breaking load is 448.0N, the minimum value of the longitudinal breaking load is 423.8N, and the strength is far higher than a national standard requirement.

Description

technical field [0001] The invention relates to a gypsum board for construction, in particular to a light-weight reinforced paper-faced gypsum board and a preparation method thereof. Background technique [0002] Desulfurization gypsum is a by-product of power plant desulfurization industry, and it is also the main raw material for the production of gypsum board. However, domestic desulfurized gypsum generally has a concentrated particle size distribution, low grade, and high harmful impurities, resulting in poor workability and water retention of the slurry made in the production process of gypsum boards, which increases the difficulty of controlling the production process of gypsum boards. It has seriously affected the strength and bonding quality of gypsum board products. At present, the domestic gypsum board production line measures to solve this problem are mostly to increase the mass per unit area of ​​the board, which not only leads to waste of resources, but also ma...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B28/14C04B38/02C04B18/24
CPCY02W30/91
Inventor 唐大勇王永生王波王慧刚辛伟冯亮汪朋裴旭
Owner BEIJING NEW BUILDING MATERIALS PLC
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap