Formula of compound ceramic simulating coating

A porcelain-like coating and composite technology, applied in the direction of coating, etc., can solve the problems of weak adhesion, easy to fall off, lack of decorative and protective effects, etc., and achieve a good overall effect

Inactive Publication Date: 2015-04-22
EURONAVY NANTONG HEAVY ANTICORROSION COATINGS
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the water-based imitation porcelain coatings on the market have weak adhesion ability, and they are easy to fall off after long-term use, and cannot achieve effective decoration and protection effects.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0008] A composite imitation porcelain paint formula, including the following raw materials in mass proportions: 40 parts of styrene-acrylic emulsion, 35 parts of water-soluble polyvinyl alcohol emulsion, 5 parts of calcium carbonate, 5 parts of methyl cellulose, 2 parts of titanium dioxide, 1 part of whitening agent, 1 part of film-forming aid, 1 part of dispersant, 10 parts of distilled water.

Embodiment 2

[0010] A composite imitation porcelain paint formula, including the following raw materials in proportion by mass: 35 parts of styrene-acrylic emulsion, 30 parts of water-soluble polyvinyl alcohol emulsion, 8 parts of calcium carbonate, 5 parts of methyl cellulose, 3 parts of titanium dioxide, 2 parts of whitening agent, 2 parts of coalescent, 2 parts of dispersant, 13 parts of distilled water.

Embodiment 3

[0012] A composite enamel-like paint formula, including the following raw materials in proportion by mass: 35 parts of styrene-acrylic emulsion, 35 parts of water-soluble polyvinyl alcohol emulsion, 5 parts of calcium carbonate, 5 parts of methyl cellulose, and 2 parts of titanium dioxide , 2 parts of whitening agent, 2 parts of film-forming aid, 2 parts of dispersant, 12 parts of distilled water.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a formula of compound ceramic simulating coating, which comprises the following raw materials in parts by mass: 35-40 parts of styrene-acrylic emulsion, 30-35 parts of water-soluble polyvinyl alcohol emulsion, 5-8 parts of calcium carbonate, 5-8 parts of methylcellulose, 2-3 parts of titanium dioxide, 1-2 parts of brightener, 1-2 parts of coalescing agent, 1-2 parts of dispersing agent and 10-15 parts of distilled water. The compound ceramic simulating coating disclosed by the invention is a high-gloss coating, no brickwork joint occurs after the coating is applied, and the overall effect is good; and the compound ceramic simulating coating has the characteristics of water resistance, alkali resistance, washing resistance and the like as ceramic tiles.

Description

technical field [0001] The invention relates to a coating formula, in particular to a porcelain-like coating formula, which belongs to the technical field of chemical coatings. Background technique [0002] Porcelain-like paint is not only used in home decoration and wall art, but also can achieve good results in handicrafts. The imitation porcelain effect of products sprayed with this kind of paint can reach a realistic level. Some of the water-based imitation porcelain paints on the market have weak adhesion, and are easy to fall off after long-term use, and cannot achieve effective decoration and protection effects. Contents of the invention [0003] Purpose of the invention: The purpose of the invention is to solve the deficiencies in the prior art, and provide a composite imitation porcelain coating with water resistance, alkali resistance, washing resistance and overall effect. [0004] Technical solution: A composite imitation porcelain paint formula according ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D125/14C09D129/04
CPCC08K2003/2241C09D125/14C08L2205/03C09D7/61C08L29/04C08L1/28C08K13/02C08K2003/265
Inventor 郭永和
Owner EURONAVY NANTONG HEAVY ANTICORROSION COATINGS
Features
  • Generate Ideas
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com