An economical high-strength hot-rolled galvanized sheet and its manufacturing method

A manufacturing method and high-strength technology, applied in hot-dip plating process, metal material coating process, coating and other directions, can solve the problems of low strength and low resource utilization rate of hot-rolled substrate galvanized sheet

Active Publication Date: 2016-11-30
ANGANG STEEL CO LTD
View PDF8 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The technical problem to be solved by the present invention is to provide an economical high-strength hot-rolled galvanized base plate and its manufacturing method to solve the problems of low strength and low resource utilization of the hot-rolled galvanized base plate

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] Chemical composition of steel: C0.15%, Si0.55%, Mn1.60%, P≤0.020%, S≤0.020%, Al0.02%, Ti0.02%, the rest is Fe and some unavoidable impurity elements . Manufacturing process: After smelting, casting, hot-rolling, and pickling of the steel of the above composition, the steel plate is hot-dip galvanized in a continuous hot-dip galvanizing production line to obtain an ultra-high-strength hot-rolled substrate galvanized sheet. Hot rolling finish temperature: 850°C, start and cool temperature: 730°C, cooling rate ≥ 30°C / s, crimping temperature: 240°C, thickness specification: 3.0mm; hot-dip galvanizing heating and holding temperature: 460°C, The holding time is: 120s, and the composition of the plating solution is: zinc solution (containing 0.3% Al).

[0026] The organization is: 50% F+45% tempered M+5% residual A.

[0027] Finished product performance: Yield strength 620MPa, tensile strength 1030MPa, elongation 19%, coating adhesion is good, surface quality meets FB surfac...

Embodiment 2

[0029] Chemical composition of steel: C0.15%, Si0.01%, Mn1.10%, P≤0.020%, S≤0.020%, Al0.90%, V0.10%, the rest is Fe and some unavoidable impurities element.

[0030] Manufacturing process: After smelting, casting, hot-rolling, and pickling of the steel of the above composition, the steel plate is hot-dip galvanized in a continuous hot-dip galvanizing production line to obtain an ultra-high-strength hot-rolled substrate galvanized sheet. Hot rolling finish temperature: 880°C, start and cool temperature: 700°C, cooling rate ≥ 15°C / s, crimping temperature: 300°C, thickness specification: 5.0mm; hot-dip galvanizing heating and holding temperature: 460°C, The holding time is: 120s, and the composition of the plating solution is: zinc solution (containing 0.3% Al).

[0031] The structure is: 60% F+35% tempered M+5% residual A.

[0032] Finished product performance: Yield strength 580MPa, tensile strength 1010MPa, elongation 21%, coating adhesion is good, surface quality meets FB s...

Embodiment 3

[0034] Chemical composition of steel: C0.65%, Si1.70%, Mn5.00%, P≤0.020%, S≤0.020%, Al0.02%, Nb0.05%, the rest is Fe and some unavoidable impurities element.

[0035] Manufacturing process: After smelting, casting, hot-rolling, and pickling of the steel of the above composition, the steel plate is hot-dip galvanized in a continuous hot-dip galvanizing production line to obtain an ultra-high-strength hot-rolled substrate galvanized sheet. Hot rolling finish temperature: 900°C, start and cool temperature: 850°C, cooling rate ≥ 30°C / s, crimping temperature: 200°C, thickness specification: 4.0mm; hot-dip galvanizing heating and holding temperature: 480°C, The holding time is: 160s, and the composition of the plating solution is: zinc solution (containing 0.5% Al).

[0036] The organization is: 88% tempered M+12% residual A.

[0037] Finished product performance: Yield strength 980MPa, tensile strength 1220MPa, elongation 12%, coating adhesion is good, surface quality meets FA le...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
yield strengthaaaaaaaaaa
yield strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses an economical high-strength hot-rolled substrate galvanized sheet, C0.15%-0.65%, Si0.01%-3.50%, Mn1.10-5.00%, P≤0.50%, S≤0.030%, Al0 .02%~3.00%, V≤0.50%, Ti≤0.20%, Nb≤0.20%. The finishing temperature of hot rolling is controlled in the austenite zone, the cooling start temperature is controlled in the austenite zone or the two-phase zone of austenite and ferrite, and the M of the steel at the end of cooling is s Point and M f The temperature between the points, and then coiled; the hot-rolled sheet is immediately hot-dip galvanized after pickling, and the steel sheet is heated to 450-600°C in the continuous hot-dip galvanizing production line, and the holding temperature is 450-600°C, and then hot-dip galvanized.

Description

technical field [0001] The invention belongs to the field of continuous production and manufacture of hot-rolled substrate galvanized steel sheets, in particular to an economical high-strength hot-rolled substrate galvanized sheet and a manufacturing method thereof. Background technique [0002] Due to the progress of hot rolling process technology, especially the commissioning of a batch of thin slab continuous casting and rolling production lines, the production quantity of thin gauge (<2.5mm thick) hot rolled strip steel has greatly increased. At present, the thinnest can reach 0.8mm. Thin gauge hot-rolled pickled galvanized sheet provides the raw material to replace hot-dip galvanized or organically coated cold-rolled strip in a wide range of applications. In addition, thin-gauge hot-rolled pickled galvanized sheet is also used in its traditional application fields, such as construction industry, cold-formed steel structural parts, etc.; Highway guardrail board and a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C22C38/14C22C38/12C22C38/06C21D8/02C23C2/40
Inventor 吕家舜李锋杨洪刚周芳刘仁东黄秋菊
Owner ANGANG STEEL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap