Rust treatment solution applicable to high-humidity region and preparation method of rust treatment solution

A treatment liquid and high humidity technology, applied in the direction of metal material coating process, etc., can solve the problems of slow drying, incompleteness, and rust conversion of the rusted treatment liquid, so as to improve the heat release rate, reduce the possibility, and ensure complete The effect of conversion

Active Publication Date: 2015-04-29
GUIZHOU POWER GRID CO LTD
View PDF5 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to provide a rusty treatment liquid suitable for high humidity areas and its preparation method, so as to solve the problems that the existing rusty treatment liquid dries slowly in humid climates, easily causes rust return or incomplete conversion, etc.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Rust treatment solution applicable to high-humidity region and preparation method of rust treatment solution

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] This embodiment provides a rust treatment solution, which is composed of the following raw materials (mass parts):

[0019] Mixed acid 20-25 parts

[0020] Mixed alcohol 30-50 parts

[0021] 0.5-1 parts of tannic acid

[0022] Zinc layer passivator 0.5-1 part

[0023] Rust layer passivator 2-3 parts

[0024] 1-2 parts of rust conversion agent

[0025] Film-forming accelerator 0.1-0.5 parts

[0026] Catalyst 0.1-0.3 parts

[0027] Penetrant 0.5-1 part

[0028] Surfactant 0.1 parts

[0029] Corrosion inhibitor 0.5-2 parts

[0030] Anti-flash rust agent 0.1-1 parts

[0031] The balance is water.

[0032] Among them, mixed acid is mixed acid, which is made by mixing 97.5 parts of phosphoric acid, 2 parts of oxalic acid and 0.5 part of hydrochloric acid; mixed alcohol is mixed alcohol, which is made by mixing tert-butanol, isopropanol and propylene glycol in a mass ratio of 1:1:1 ; The zinc layer passivator is a fast and efficient passivator, and the passivation o...

Embodiment 2

[0034] This embodiment provides a rust treatment solution, which consists of the following raw materials (parts by mass, subject to a total of 100 parts):

[0035] Mixed acid 20 parts

[0036] Mixed alcohol 30 parts

[0037] 0.5 parts of tannic acid

[0038] Zinc layer passivator 0.5 parts

[0039] Rust passivator 2 parts

[0040] 1 piece of rust conversion agent

[0041] Film-forming accelerator 0.1 part

[0042] Catalyst 0.1 parts

[0043] Penetrant 0.5 parts

[0044] Surfactant 0.1 parts

[0045] Corrosion inhibitor 0.5 parts

[0046] Anti-flash rust agent 0.1 parts

[0047] The balance is water.

[0048] Among them, mixed acid is mixed acid, which is made by mixing 97.5 parts of phosphoric acid, 2 parts of oxalic acid and 0.5 part of hydrochloric acid; mixed alcohol is mixed alcohol, which is made by mixing tert-butanol, isopropanol and propylene glycol in a mass ratio of 1:1:1 ; The zinc layer passivator is a fast and efficient passivator, and the passivation o...

Embodiment 3

[0050] This embodiment provides a rust treatment solution, which consists of the following raw materials (parts by mass, subject to a total of 100 parts):

[0051] Mixed acid 22 parts

[0052] Mixed alcohol 35 parts

[0053] 1 part tannic acid

[0054] Zinc layer passivator 0.7 parts

[0055] Rust passivator 2 parts

[0056] 1 piece of rust conversion agent

[0057] Film-forming accelerator 0.1 part

[0058] Catalyst 0.1 part

[0059] Penetrant 0.5 parts

[0060] Surfactant 0.1 parts

[0061] Corrosion inhibitor 0.5 parts

[0062] Anti-flash rust agent 0.1 parts

[0063] The balance is water.

[0064] Among them, the mixed acid is 97.5 parts of phosphoric acid, 2 parts of oxalic acid and 0.5 part of hydrochloric acid; High-efficiency passivator, the passivation of the zinc layer can be completed within 1 second after brushing. The passivating agent for the zinc layer is chromic anhydride, chromium trichloride, and silver nitrate mixed at a mass ratio of 6:4:1; the ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a rust treatment solution applicable to a high-humidity region and a preparation method of the rust treatment solution. The rust treatment solution comprises the following components in mass percentage: 20-25% of mixed acid, 30-50% of mixed alcohol, 0.5-1% of tannic acid, 0.5-1% of a zinc layer passivation agent, 2-3% of a rust layer passivation agent, 1-2% of a rust layer conversion agent, 0.1-0.5% of a film formation promoting agent, 0.1-0.3% of a catalyst, 0.5-1% of a permeating agent, 0.1% of a surfactant, 0.5-2% of a corrosion inhibitor, 0.1-1% of an anti-flash rust agent and the balance of water. The rust treatment solution is used for solving the problems that the existing rust treatment solution is slow in drying in a humid climate, liable to causing re-rusting or incomplete conversion and the like. The rust treatment solution provided by the invention belongs to the field of metal rust protection.

Description

technical field [0001] The invention relates to a rust treatment solution, which belongs to the field of metal rust prevention. Background technique [0002] According to statistics, the direct economic loss caused by metal corrosion accounts for about 4% of the gross national product in my country every year. Therefore, the corrosion protection of metals has attracted more and more attention. In the previous metal anti-corrosion coating technology, the pretreatment of the metal surface before painting accounts for about 45% of the total price of the entire coating project. If the surface treatment processes such as rust removal, oil removal, and water removal can be reduced or omitted, the coating cost can be significantly reduced, and the painting process can be greatly simplified at the same time, thereby reducing labor intensity and reducing the harm of rust dust to the human body. Based on the above purposes, a water-based rust treatment solution has been developed, w...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C23C22/47
CPCC23C22/47
Inventor 虢韬王伟杨恒李欣
Owner GUIZHOU POWER GRID CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap