Lead-carbon storage battery cathode material and preparation method thereof

A negative electrode material, battery technology, applied in lead-acid battery electrodes, lead-acid batteries, battery electrodes, etc., can solve the problems of easy thermal runaway, low specific energy, easy failure, etc., achieve good rate performance, high rate performance, improve adhesive effect

Active Publication Date: 2015-05-06
HENGYANG RITAR POWER CO LTD
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the disadvantages of lead-acid batteries are also obvious, such as: low specific energy, short cycle life, easy thermal runaway, bulky batteries, low discharge efficiency at high rates, and low temperature has a great impact on battery performance (low temperature of minus 30 degrees loses charging and discharge capacity), high temperature is easy to fail, etc.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Lead-carbon storage battery cathode material and preparation method thereof
  • Lead-carbon storage battery cathode material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0047] The following clearly and completely describes the technical solutions in the embodiments of the present invention. Obviously, the described embodiments are only some of the embodiments of the present invention, but not all of them. Based on the embodiments of the present invention, all other embodiments obtained by persons of ordinary skill in the art without making creative efforts belong to the protection scope of the present invention.

[0048] An embodiment of the present invention provides a negative electrode material for a lead-carbon storage battery, which is formed by mixing and stirring the first component and the second component;

[0049] The first component is composed of the following components according to the mass ratio:

[0050] Lead powder 32~35%;

[0051] Phosphoric acid 0.6~1.0%;

[0052] Carbon nanotubes 0.3~0.5%;

[0053] Activated carbon 1.6~2.2%;

[0054] Magnesium sulfate 0.3~0.5%;

[0055] Paraffin oil 0.3~0.6%;

[0056] Deionized water...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a lead-carbon storage battery cathode material and a preparation method thereof. The material is prepared by mixing and stirring a first component and a second component, wherein the first component is prepared from the following components in percentage by mass: 32%-35% of lead powder, 0.6%-1.0% of phosphoric acid, 0.3-0.5% of a carbon nano tube, 1.6%-2.2% of activated carbon, 0.3%-0.5% of magnesium sulfate, 0.3%-0.6% of paroline oil and 60.2%-64.5% of deionized water; and the second component is prepared from the following raw materials in percentage by weight: 50%-55% of silicon dioxide, 1.3%-2.5% of a carbon nano tube, 7.8%-9.6% of citric acid and 33.2%-39% of deionized water. According to the lead-carbon storage battery cathode material and the preparation method thereof, the lead-carbon storage battery cathode material has good high-rate capability, long service life and high capacity.

Description

technical field [0001] The invention relates to a negative electrode material of a lead-carbon storage battery and a preparation method thereof, belonging to the field of storage batteries. Background technique [0002] Lead-acid battery refers to a battery whose electrodes are mainly made of lead and its oxides, and the electrolyte is a sulfuric acid solution. Lead-acid batteries have been widely used due to their advantages of stable voltage and low price. However, the disadvantages of lead-acid batteries are also obvious, such as: low specific energy, short cycle life, easy thermal runaway, bulky batteries, low discharge efficiency at high rates, and low temperature has a great impact on battery performance (low temperature of minus 30 degrees loses charging and discharge capacity), high temperature is easy to fail, etc. [0003] Therefore, it is necessary to design a lead-carbon battery negative electrode material and a preparation method thereof to overcome the above ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): H01M4/36H01M4/56H01M4/583H01M4/20
CPCH01M4/57H01M4/587H01M4/621H01M10/06Y02E60/10
Inventor 刘兆勇夏朝阳
Owner HENGYANG RITAR POWER CO LTD