A kind of foam ceramic insulation material and preparation method thereof

A foamed ceramic and thermal insulation material technology, applied in the field of thermal insulation materials, can solve the problems of poor flame retardant performance, poor thermal insulation performance, good thermal insulation performance, etc., and achieve good thermal insulation effect, excellent thermal insulation and fire performance, and high strength. Effect

Inactive Publication Date: 2016-08-24
SHANGHAI INST OF TECH
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] One of the purposes of the present invention is to solve the problem that the above-mentioned thermal insulation material has good fireproof performance but poor thermal insulation performance; Performance and insulation properties of ceramic foam insulation

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] A ceramic foam insulation material, which is obtained by injecting the filling medium used in the ceramic foam insulation material into the ceramic foam filter with a vacuum device until it completely fills the internal space, and then drying it in a drying oven at a controlled temperature of 90-110°C. ;

[0035] The ceramic foam filter has a mesh number of 300-400 mesh / inch, a filtration accuracy of 50-80ppi, and a thickness of 40-60mm;

[0036] The filling medium used in the foamed ceramic insulation material is calculated by weight percentage, and the composition and content of the raw materials used in the preparation process are as follows:

[0037] Sodium Carboxymethyl Cellulose 2.1%

[0038] Glass beads 56.0%;

[0039] The balance is water.

[0040] The above-mentioned preparation method of a ceramic foam insulation material specifically comprises the following steps:

[0041] (1) Mix sodium carboxymethyl cellulose and water to obtain viscous liquid;

[0042...

Embodiment 2

[0046]A ceramic foam insulation material, which is obtained by injecting the filling medium used in the ceramic foam insulation material into the ceramic foam filter with vacuum equipment until it completely fills the internal space, and then drying it in a drying oven at a controlled temperature of 90-110°C ;

[0047] The ceramic foam filter has a mesh number of 300-400 mesh / inch, a filtration accuracy of 50-80ppi, and a thickness of 40-60mm;

[0048] The filling medium used in the foamed ceramic insulation material is calculated by weight percentage, and the composition and content of the raw materials used in the preparation process are as follows:

[0049] Sodium Carboxymethyl Cellulose 2.7%

[0050] Glass beads 43.2%;

[0051] The balance is water.

[0052] The above-mentioned preparation method of a ceramic foam insulation material specifically comprises the following steps:

[0053] (1) Mix sodium carboxymethyl cellulose and water to obtain viscous liquid;

[0054]...

Embodiment 3

[0058] A ceramic foam insulation material, which is obtained by injecting the filling medium used in the ceramic foam insulation material into the ceramic foam filter with vacuum equipment until it completely fills the internal space, and then drying it in a drying oven at a controlled temperature of 90-110°C ;

[0059] The ceramic foam filter has a mesh number of 300-400 mesh / inch, a filtration accuracy of 50-80ppi, and a thickness of 40-60mm;

[0060] The filling medium used in the foamed ceramic insulation material is calculated by weight percentage, and the composition and content of the raw materials used in the preparation process are as follows:

[0061] Sodium Carboxymethyl Cellulose 2.9%

[0062] Glass beads 38.8%;

[0063] The balance is water.

[0064] The above-mentioned preparation method of a ceramic foam insulation material specifically comprises the following steps:

[0065] (1) Mix sodium carboxymethyl cellulose and water to obtain viscous liquid;

[0066...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
porosityaaaaaaaaaa
dimensional stabilityaaaaaaaaaa
Login to view more

Abstract

The invention discloses a foam ceramic insulation material and a preparation method thereof. The preparation method comprises the steps of injecting a filling medium for a foam ceramic insulation material into a foam ceramic filter by virtue of vacuum equipment until gaps inside the filter are filled with the filling medium, and drying in a drying oven at 90-110 DEG C, wherein the foam ceramic filter has a mesh number of 300-400mesh / inch, a filter accuracy of 50-80ppi and a thickness of 40-60mm; the filling medium for the foam ceramic insulation material is prepared from the following raw materials in percentage by weight: 2-3 percent of sodium carboxymethyl cellulose, 38.8-56.0 percent of glass microspheres and the balance of water. The foam ceramic insulation material has excellent insulation performance, excellent compression strength, relatively high size accuracy, good flame retardance, good thermal shock resistance, low hot-shrinkage rate, low heat expansion coefficient, low production cost, simple preparation process and no special equipment, and is suitable for industrial production.

Description

technical field [0001] The invention relates to a foam ceramic thermal insulation material and a preparation method thereof, belonging to the field of thermal insulation materials. Background technique [0002] With the depletion of the traditional three major fossil energy sources, energy conservation and environmental protection have become an increasingly hot topic. At present, my country's building energy consumption has risen sharply year by year, reaching 45% of the country's total energy consumption, which has caused a huge burden on the development of the national economy. Therefore, building energy saving is imminent. Maintaining the temperature inside the building and reducing its heat loss is an effective way to improve the energy efficiency of the building. At present, the insulation materials used in more than 80% of domestic buildings are mainly organic materials such as expanded polystyrene board (EPS), extruded polystyrene board (XPS), sprayed polyurethane ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C04B41/80
Inventor 吴桢干张骋吴健郁雷张栋马昕迪
Owner SHANGHAI INST OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap