Repairing method for damaged polyurethane material

A polyurethane material and repair method technology, which is applied in the field of self-repair of damaged polyurethane materials, can solve problems such as affecting normal use and increasing thickness, and achieve the effect of recovery performance, good performance and high healing rate

Inactive Publication Date: 2015-06-24
CHANGAN UNIV
View PDF3 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

After the repair, the bonding position is obvious, and the thickness increases, affecting normal use

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Repairing method for damaged polyurethane material
  • Repairing method for damaged polyurethane material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] Synthesize the polyurethane repair agent that chitosan is embedded with oxetane according to the following steps:

[0018] (1) Add 2 g of chitosan into a three-neck flask containing 150 mL of NaOH solution with a concentration of 1 mol / L, stir at 0°C for 30 h to obtain deacetylated chitosan, and refrigerate at 0°C for 48 h.

[0019] (2) Thaw the deacetylated chitosan refrigerated in step (1) and mix it with 150 mL of cooled isopropanol, stir for 1 hour, add 0.15 g of cooled 3-chloromethyl-3-methyloxetane The mass ratio of alkanes, chitosan and 3-chloromethyl-3-methyloxetane is 1:0.075, heat up to 80°C, stir for 12 hours until the reaction is complete, filter, wash with methanol until the mixture is medium properties, dried at 60°C for 12 hours to obtain chitosan monomer embedded with oxetane;

[0020] (3) The chitosan monomer embedded with oxetane obtained in step (2) is dispersed in 120 mL of dimethyl sulfoxide solution, ultrasonically treated at 25° C. for 12 hours, ...

Embodiment 2

[0023] The method for repairing the damaged polyurethane material in this embodiment is to adjust the ultraviolet light irradiation time to 20 minutes, and other operations are the same as in embodiment 1 to realize the self-repairing of the polyurethane material.

Embodiment 3

[0025] The method for repairing the damaged polyurethane material in this embodiment is to adjust the ultraviolet light irradiation time to 40 minutes, and other operations are the same as in embodiment 1 to realize the self-repairing of the polyurethane material.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a repairing method for a damaged polyurethane material. The repairing method is characterized in that a repairing agent for a polyurethane network structure embedded with oxetane chitosan is coated on a damaged part of the polyurethane material, and the damaged polyurethane material is irradiated by ultraviolet light for 20-40 minutes to complete the self-repair of the polyurethane material. The repairing method disclosed by the invention can make up a gap of a polyurethane crack, is relatively high in healing rate and capable of repairing the performances of the material better.

Description

technical field [0001] The invention belongs to the technical field of polyurethane material crack repair research, and in particular relates to a method for realizing the self-repair of damaged polyurethane material under the condition of ultraviolet light irradiation. Background technique [0002] Polyurethane has high strength, wear resistance, tear resistance, good bending performance and excellent processing performance, and its oil resistance and water resistance are extremely excellent. In recent years, as an emerging organic polymer material, it has been widely used in many fields of the national economy because of its excellent performance. The product application fields involve light industry, chemical industry, electronics, textile, medical treatment, construction, building materials, automobile, national defense, aerospace, aviation, etc., and is known as the "fifth largest plastic". [0003] Due to a wide range of applications and different use environments, po...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08J7/12C08J7/04C08G18/73C08G18/48C08G18/64C08B37/08
Inventor 李蕊周天澍陈佳奇王鹏志陈旭
Owner CHANGAN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com