Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Electric brush for treadmill motor and preparation method thereof

A technology of brushes and raw materials, which is applied in the field of brushes for treadmill motors and its preparation, and in the field of brushes for motors. It can solve the problems of mechanical sparks, high unit pressure of brushes, and poor performance of brushes, etc., and achieve mechanical Excellent processing performance, strong anti-interference, good reversing performance

Active Publication Date: 2017-12-05
SUZHOU DONSUN CARBONWARE CO LTD
View PDF10 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the general brushes have poor performance and poor stability. The unit pressure of the brushes is too high, the resistance is large, and the hardness is high. The wear of the brush is intensified, the unit pressure is too small, the contact is unstable, the commutation performance is poor, and mechanical sparks are prone to occur
Especially poor wear resistance, poor commutation performance, poor anti-interference ability, often unable to meet the various requirements of the motor for the brush

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Electric brush for treadmill motor and preparation method thereof
  • Electric brush for treadmill motor and preparation method thereof
  • Electric brush for treadmill motor and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0070] 1. Prepare materials according to the following weight ratio (kg):

[0071]

[0072] Among them, the additives include molybdenum disulfide and paraffin, and the weight ratio of molybdenum disulfide and paraffin is 1:1.5; the binder is bisphenol A epoxy resin, and its epoxy value is 0.25-0.45; the curing agent is selected from Latent curing agent T-31 curing agent (Changzhou Shanfeng Chemical Co., Ltd.);

[0073] 2) Put the raw materials of natural graphite, artificial graphite, expanded graphite, carbon black, additives, and curing agent in the kneading pot, turn on the heating device of the kneading pot, heat up to 160°C, mix at 160°C for 1.5h, and stop heating. After the material is cooled to ≤40°C, the premix is ​​prepared;

[0074] Heating to remove impurities such as moisture and ash in the raw material to ensure that the moisture content in the raw material is <0.5%.

[0075] 3) Dissolve 24kg of binder epoxy resin in 40kg of acetone and mix well to obtain a ...

Embodiment 2

[0084] 1. Prepare materials according to the following weight ratio (kg):

[0085]

[0086] Among them, the additives include molybdenum disulfide and paraffin, and the weight ratio of molybdenum disulfide and paraffin is 0.5:1; the binder is bisphenol A epoxy resin, and its epoxy value is 0.25-0.35; the curing agent is selected from Latent curing agent T-31 curing agent;

[0087] 2) Put the raw materials of natural graphite, artificial graphite, expanded graphite, carbon black, additives, and curing agent in the kneading pot, turn on the heating device of the kneading pot, heat up to 150°C, and stop heating after mixing at 150°C for 2 hours. The material is cooled to ≤40°C to obtain a premix;

[0088] 3) Dissolve 28kg of adhesive epoxy resin in 45kg of acetone and mix evenly to obtain an adhesive solution;

[0089] 4) Add the binder solution into the premix and stir, mix evenly, stir for 1.5 hours, take out the material after mixing evenly, place it at room temperature (...

Embodiment 3

[0096] 1. Prepare materials according to the following weight ratio (kg):

[0097]

[0098] Among them, the additives include molybdenum disulfide and paraffin, and the weight ratio of molybdenum disulfide and paraffin is 1.5:2; the binder is bisphenol A epoxy resin, and its epoxy value is 0.35-0.45; the curing agent is selected from Latent curing agent adipic acid dihydrazide (Wuxi Liangxi Fine Chemical Co., Ltd.);

[0099] 2) Put the raw materials of natural graphite, artificial graphite, expanded graphite, carbon black, additives, and curing agent in the kneading pot, turn on the heating device of the kneading pot, heat up to 170°C, mix at 170°C for 1.5h, and stop heating. After the material is cooled to ≤40°C, the premix is ​​prepared;

[0100] 3) Dissolve 20kg of binder epoxy resin in 35kg of acetone and mix well to obtain a binder solution;

[0101] 4) Add the binder solution into the premix and stir, mix evenly, stir for 1.0h, take out the material after mixing eve...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The present invention discloses an electric brush for a treadmill motor and a manufacturing method of same. The materials of the electric brush for the motor belong to the field of material science, comprising natural graphite, synthetic graphite, expanded graphite, carbon black, an additive, an adhesive and a curing agent. The electric brush for the treadmill motor disclosed by the present invention is low in noise caused during operation, low in resistance, good in direction switching, powerful in interference resistance and long in service life. More importantly, the electric brush is high in abrasion resistance, low in noise and spark grade, sparkless in empty load, and good in product stability.

Description

technical field [0001] The invention relates to a brush for a motor, in particular to a brush for a treadmill motor and a preparation method thereof, belonging to the field of motors. And it is widely used in the medical industry, fitness equipment industry, sports industry and household treadmill motors. Background technique [0002] A motor brush is a device that transmits energy or signals between the fixed part and the rotating part of a rotating machine such as a motor or generator. Also known as carbon brush. Carbon brushes are generally made of pure carbon and coagulant. They are generally square in shape and are stuck on a metal bracket. There are springs inside to press it tightly on the rotating shaft. part. The carbon brush looks a bit like the rubber strip of a pencil, with wires leading out from the top. There are large and small volumes. Carbon brushes are used on commutators or slip rings as sliding contacts for leading and exporting current, and are wide...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): H01R39/22H01R43/12
CPCH01R39/22H01R43/12
Inventor 吴爱民朱约辉林勇
Owner SUZHOU DONSUN CARBONWARE CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com