A kind of low friction coefficient high barrier aluminized film and preparation method thereof

A low friction coefficient, high barrier technology, applied in chemical instruments and methods, synthetic resin layered products, layered products, etc., can solve the problems of heat sealing strength (weak barrier property, etc.), and achieve low friction coefficient, heat sealing strength high effect

Active Publication Date: 2017-06-16
HUBEI DEWEI PACKAGING TECH
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The friction coefficient of the existing aluminized film is still high, and the heat sealing strength (barrier property) is still weak

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of low friction coefficient high barrier aluminized film and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] Such as figure 1 As shown, a low-friction coefficient high-barrier aluminum-coated film is formed by four-layer co-extrusion of a heat-sealing layer 1, a first core layer 2, a second core layer 3, and an aluminum-coated layer 4; The mass percentages of the heat-sealing layer 1, the first core layer 2, the second core layer 3, and the aluminum plating layer 4 are respectively: 21%, 30%, 30%, and 19%;

[0022] The material of the heat-sealing layer is formed by mixing ternary random copolymer polypropylene (PP) resin [ternary random copolymer resin 750M] and a modifier, and the amount of the modifier added is ternary random copolymer 10-15% of the mass of propylene (PP) resin;

[0023] The material of the first core layer adopts polypropylene resin (containing few low-molecular precipitates), and because the precipitates are few, the maintenance of the corona value of the base film and the adhesion of the follow-up aluminum layer have played a better effect;

[0024] Th...

Embodiment 2

[0038] Such as figure 1 As shown, it is basically the same as Example 1, except that: the material of the aluminum layer adopts ethylene-vinyl acetate (EVA) copolymer resin.

[0039] The advantages of similar products in the market are as follows: the invention has good flatness, high gloss, high heat-sealing strength and low coefficient of friction. Uniform aluminum plating, high adhesion, excellent barrier after aluminum plating, high brightness. The heat seal strength of similar products in the market is 8N / 108 degrees, and the product of the present invention is 12N / 104 degrees. The coefficient of friction of similar products in the market is 0.6-0.8, and that of the product of the present invention is 0.3-0.4.

Embodiment 3

[0041] Such as figure 1 As shown, it is basically the same as Example 1, except that the modifier is Exxon FL3980.

[0042] The advantages of similar products in the market are as follows: the invention has good flatness, high gloss, high heat-sealing strength and low coefficient of friction. Uniform aluminum plating, high adhesion, excellent barrier after aluminum plating, high brightness. The heat seal strength of similar products in the market is 8N / 108 degrees, and the product of the present invention is 12N / 104 degrees. The coefficient of friction of similar products in the market is 0.6-0.8, and that of the product of the present invention is 0.3-0.4.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
friction coefficientaaaaaaaaaa
friction coefficientaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the technical field of aluminized films, and discloses a low-friction coefficient high-resistance aluminized film. The aluminized film is characterized by comprising a heat-seal layer, a first core layer, a second core layer and an aluminized layer which are arranged in sequence through four-layer co-extrusion casting the mass percentages of the heat-seal layer, the first core layer, the second core layer and the aluminized layer are 21%, 30%, 30% and 19% respectively; the heat-seal layer is made of ternary random copolymerization polypropylene (PP) resin and a modifying agent; the adding amount of the modifying agent is 10-15% of the mass of the ternary random copolymerization polypropylene (PP) resin; the first core layer is made of polypropylene resin; the second core layer is made of polypropylene resin; the aluminized layer is made of copolymer resin and a reinforcing agent; the adding amount of the reinforcing agent is 2-5% of the mass of the copolymer resin. The aluminized film prepared according to the method is relatively low in friction coefficient, and relatively high in heat-seal strength.

Description

technical field [0001] The invention belongs to the technical field of aluminized film, and in particular relates to a low-friction coefficient high-barrier aluminized film and a preparation method thereof. Background technique [0002] The friction coefficient of the existing aluminized film is still high, and the heat sealing strength (barrier property) is still weak. Contents of the invention [0003] The object of the present invention is to provide a low-friction coefficient high-barrier aluminized film and a preparation method thereof. The aluminized film prepared by the method has a low friction coefficient and high heat-sealing strength. [0004] In order to achieve the above object, the technical solution adopted by the present invention is: a low friction coefficient and high barrier aluminized film, which is characterized in that it consists of a heat-sealing layer, a first core layer, a second core layer, and an aluminized layer. It is formed by co-extruding f...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B32B27/06B32B27/08B32B27/32B32B27/18
Inventor 蔡岩胜蔡扬龙
Owner HUBEI DEWEI PACKAGING TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com