A technology of fatigue crack propagation and metal corrosion, which is used in measuring devices, testing wear resistance, weather resistance/light resistance/corrosion resistance, etc. The effect of changing and avoiding sliding

Inactive Publication Date: 2015-07-22
BEIHANG UNIV
View PDF10 Cites 16 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The crack detection of the sample is the focus of corrosion fatigue research. The crack growth rate is directly related to the fatigue life of the sample. GB/T6398-2000 "Metallic Materials Fatigue Crack Growth Rate Test Method" introduces various measurement methods of the fatigue crack length in detail , including the flex

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Device and method for testing metal corrosion fatigue crack extension
  • Device and method for testing metal corrosion fatigue crack extension
  • Device and method for testing metal corrosion fatigue crack extension

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0033] The present invention will be further described below in conjunction with the accompanying drawings.

[0034] The device for testing metal corrosion fatigue crack growth in the present invention includes a base 1, a sample positioning part 2 and a corrosive medium container 3, such as figure 1 shown.

[0035] The base 1 is formed by integral processing of a corrosion-resistant 316L stainless steel cylinder, which can avoid leakage failures due to stress concentration during the test. The base 1 has a circular table top 101, a fatigue testing machine clamping part 102, and a sample locking part 103, such as figure 2 shown.

[0036] Wherein, the clamping part of the fatigue testing machine is arranged at the center of the lower surface of the circular table 101 for clamping the lower chuck of the fatigue testing machine, and after the fatigue testing machine is clamped, the circular table 101 must be in a horizontal state. The sample locking member 103 is arranged on ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a device and a method for testing metal corrosion fatigue crack extension. The device comprises a pedestal and a corrosive medium accommodation container, wherein a fatigue machine clamping piece is designed on the lower surface of the pedestal and used for clamping the lower chuck of the fatigue machine; a testing specimen locking piece is designed on the upper surface of the pedestal and used for fixing the lower end of a fatigue testing specimen; the upper end of the fatigue testing specimen is clamped by a fatigue machine upper clamp; the alternating load of the fatigue machine can be transferred to the testing specimen through the fatigue machine clamping piece; the corrosive medium accommodation container adopts a cylindrical structure; the bottom end of the cylindrical structure is fixedly mounted on the upper surface of a circular table in the pedestal; the testing specimen locking piece in the pedestal is positioned in the corrosive medium accommodation container. The device is used for testing according to the test fatigue testing parameters until the working section of the fatigue testing specimen is broken; in the process, a microscope is utilized to record and shoot the producing-extending-fracturing process of the crack. The device disclosed by the invention has the advantage of realizing the corrosive fatigue performance test of the metal material in the corrosive medium under the standing state.

Description

technical field [0001] The invention belongs to the field of corrosion fatigue crack damage detection of marine metal structural parts, and specifically relates to a device and method for testing the propagation of metal corrosion fatigue cracks when marine structural parts have corrosion fatigue problems when they are serving in marine environments. Background technique [0002] During the service process, marine metal structural parts are in a state of full immersion in seawater during the entire life cycle. On the one hand, they are eroded by seawater corrosive media, and on the other hand, they are subjected to periodic stress loading, resulting in corrosion fatigue fracture failure. Corrosion fatigue is a type of stress corrosion, and the metal defects caused by corrosion can be used as crack sources and then crack propagation occurs until fracture failure. Fatigue fracture of marine metal structural parts in corrosive environment has become the focus of research, and a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): G01N3/56G01N17/00
Inventor 刘天娇张卫方何晶靖方小亮王红勋陈惠鹏娄伟涛董邦林王邓江
Owner BEIHANG UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap