PVC (polyvinyl chloride) formula

A PVC resin and formula technology, applied in the field of plastic pipes, can solve problems such as poor impact resistance, and achieve the effect of enhancing impact resistance and strength, suitable for popularization and application, and low ratio.

Inactive Publication Date: 2015-08-19
钱万标
View PDF3 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

PVC pipe has the advantages of acid resistance, alkali resistance, corrosion resistance and high strength, but its impact resistance is relatively poor

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0010] A PVC formula of the present invention is made of the following raw materials in parts by weight: 70 parts of PVC resin, 3 parts of calcium stearate, 4 parts of zinc oxide, 6 parts of hexamethylphosphoric triamide, 1 part of anti-impact agent, chlorinated 2 parts of paraffin, 0.5 parts of additives.

[0011] The auxiliary agent is composed of one or more than two kinds of plasticizer, wetting agent and stabilizer.

Embodiment 2

[0013] A PVC formula of the present invention is made of the following raw materials in parts by weight: 90 parts of PVC resin, 6 parts of calcium stearate, 7 parts of zinc oxide, 8 parts of hexamethylphosphoric triamide, 2 parts of anti-impact agent, chlorinated 3 parts of paraffin, 1.3 parts of additives.

[0014] The auxiliary agent is composed of one or more than two kinds of plasticizer, wetting agent and stabilizer.

Embodiment 3

[0015] Embodiment 3 is the optimal embodiment of the present invention:

[0016] A PVC formula of the present invention is made of the following raw materials in parts by weight: 80 parts of PVC resin, 4.7 parts of calcium stearate, 5 parts of zinc oxide, 7 parts of hexamethylphosphoric triamide, 1.4 parts of anti-impact agent, chlorinated 2.6 parts of paraffin, 0.8 parts of additives.

[0017] The auxiliary agent is composed of one or more than two kinds of plasticizer, wetting agent and stabilizer.

[0018] To sum up, the PVC pipe produced by using this formula can enhance the impact resistance and strength, and the added hexamethylphosphoric acid triamide can not only greatly improve the oxidation resistance of PVC pipe, but also has a relatively low cost, which is suitable for popularization and application .

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a PVC (polyvinyl chloride) formula, which is prepared from the following raw materials in parts by weight: 70 to 90 parts of PVC resin, 3 to 6 parts of calcium stearate, 4 to 7 parts of zinc oxide, 6 to 8 parts of hexamethylphosphoric triamide, 1 to 2 parts of impact modifier, 2 to 3 parts of chlorcosane, and 0.5 to 1.3 parts of auxiliaries. PVC pipes produced by using the formula have the advantages that the impact resistance property and the strength can be enhanced, through adding the hexamethylphosphoric triamide, the oxidation resistance of the PCV pipes can be greatly improved, and the cost is relatively low. The PVC formula is suitable for popularization and application.

Description

【Technical field】 [0001] The invention relates to the technical field of plastic pipes, in particular to a PVC formula. 【Background technique】 [0002] The main component of PVC pipe is polyvinyl chloride, and other components are added to enhance its heat resistance, toughness, ductility, etc. PVC is deeply loved in the world today, and it is quite a popular and widely used synthetic material. PVC pipe is a mature pipe, mainly used in water supply and drainage projects. PVC pipe has the advantages of acid resistance, alkali resistance, corrosion resistance and high strength, but its impact resistance is relatively poor. 【Content of invention】 [0003] The invention provides a PVC formula, and the PVC pipe produced by using the formula can enhance the impact resistance and strength. [0004] In order to achieve the above object, the technical solution adopted by a PVC formula of the present invention is: a PVC formula made of the following raw materials in parts by weig...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/06C08L91/06C08K13/02C08K5/098C08K3/22C08K5/5399
CPCC08L27/06C08L2203/18C08L91/06C08K13/02C08K5/098C08K2003/2296C08K5/5399
Inventor 钱万标
Owner 钱万标
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap