Manufacturing method for pressing powder into welded ring

A manufacturing method and powder technology, applied in the field of heterosexual self-wetting welding ring manufacturing, can solve the problems of large workload, low welding efficiency, low welding ring forming rate, etc., and achieve the effect of high utilization rate

Inactive Publication Date: 2015-09-02
优美科科技材料(苏州)有限公司
View PDF6 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, this method has a large workload and low productivity
At the same time, in the welding process, the flux ...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Manufacturing method for pressing powder into welded ring
  • Manufacturing method for pressing powder into welded ring
  • Manufacturing method for pressing powder into welded ring

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0036] The following examples are used to illustrate the present invention, but should not be used to limit the scope of the present invention. The implementation conditions used in the examples can be further adjusted according to the manufacturer's conditions, and the unspecified implementation conditions are usually conventional experimental conditions.

[0037] 1. Manufacture of brass welding ring

[0038] See structure figure 1 and figure 2 , the inner wall of the brass welding ring 1 is connected with an annular protrusion 2, which is arranged in steps with the inner wall of the brass welding ring.

[0039] The manufacturing method of described brass welding ring comprises the steps:

[0040] a) Sieving

[0041] Brass alloy powder (Cu x Zn 100-x , the specific composition is shown in Table 1) Pour into a vibrating sieve for classification, and the undersize is for use; pour the flux powder into a vibrating sieve for classification, and the undersize is for use; po...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a manufacturing method for pressing powder into a welded ring. The method comprises the following steps of 1) sieving; 2) mixing powder; 3) performing thermal treatment and sieving; 4) pressing; 5) sintering. The method is less in processing steps, free from repeated wire drawing and annealing processes, capable of manufacturing the welded ring at a time, high in welding efficiency and production efficiency and high in welded ring yield.

Description

technical field [0001] The invention belongs to the technical field of manufacturing heterosexual self-wetting welding rings, and in particular relates to a method for manufacturing welding rings by pressing powder. Background technique [0002] The traditional welding ring manufacturing method usually includes the following steps: smelting→extrusion→wire drawing→annealing→ring making→post-processing, etc. Due to the large size of the extruded wire, it needs to be repeated many times (7-8 times) Only wire drawing and annealing can reach the specified welding ring size, and then the drawn and annealed wire is welded end to end through the ring making machine to obtain the final specification welding ring. [0003] However, this method has a large workload and low productivity. At the same time, during the welding process, flux needs to be applied manually, and the welding efficiency is low, resulting in a low welding ring forming rate (less than 80%). Contents of the inven...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B22F5/10B22F3/16
Inventor 邓彬李旭陈强李文坚
Owner 优美科科技材料(苏州)有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap