Cathode for lead-carbon batteries, production method of cathode and battery made with cathode

A lead-carbon battery and negative electrode technology, applied in lead-acid battery electrodes, battery electrodes, lead-acid batteries, etc., can solve the problems of difficult to convert Pb, reduce surface area, etc., to improve conversion activity, prolong service life, and alleviate the irreversibility of negative electrodes. The effect of sulfation

Active Publication Date: 2015-09-09
骆驼集团蓄电池研究院有限公司
View PDF3 Cites 23 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Ideally, all lead sulfate and lead on the negative electrode undergo a completely reversible conversion during the battery charge-discharge cycle, but from a thermodynamic point of view, PbSO 4 Recr

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Cathode for lead-carbon batteries, production method of cathode and battery made with cathode

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0048] A lead-carbon battery negative electrode comprises the following components in parts by weight:

[0049] 8.5 parts of sulfuric acid,

[0050] 0.5 parts of barium sulfate,

[0051] Norwegian lignin 0.1 part,

[0052] Nylon 0.05 parts,

[0053] 0.2 part of graphene nanobelt,

[0054] 0.01 part of silane coupling agent,

[0055] Lignosulfonate 0.05 part,

[0056] Nano titanium dioxide 0.02 parts,

[0057] Nano silicon dioxide 0.04 part,

[0058] 10 parts pure water,

[0059] 70 parts of lead powder;

[0060]Wherein, the density of the sulfuric acid is 1.38g / mL; the specific surface area of ​​the graphene nanobelt is 180 ~ 300m 2 / g, the average pore diameter is less than 50nm;

[0061] According to the composition formula of above-mentioned lead-carbon battery negative pole, make following preparation:

[0062] (1) Premix barium sulfate, organic expansion agent, graphene nanobelts, short fibers, nano-titanium dioxide and nano-silicon dioxide for 5 minutes;

[0...

Embodiment 2

[0069] A lead-carbon battery negative electrode comprises the following components in parts by weight:

[0070] 9.2 parts of sulfuric acid,

[0071] 1.0 parts of barium sulfate,

[0072] 0.25 parts of humic acid,

[0073] 0.12 part of acrylic fiber,

[0074] 0.4 parts of graphene nanoribbons,

[0075] 0.15 parts of silane coupling agent,

[0076] 0.06 parts of cellulose derivatives,

[0077] Nano titanium dioxide 0.03 part,

[0078] Nano silicon dioxide 0.06 part,

[0079] 13 parts of pure water,

[0080] 76 parts of lead powder;

[0081] Wherein, the density of the sulfuric acid is 1.38g / mL; the specific surface area of ​​the graphene nanobelt is 300 ~ 430m 2 / g, the average pore size is 20nm~35nm;

[0082] According to the composition formula of above-mentioned lead-carbon battery negative pole, make following preparation:

[0083] (1) Premix barium sulfate, organic expansion agent, graphene nanobelts, short fibers, nano-titanium dioxide and nano-silicon dioxide f...

Embodiment 3

[0090] A lead-carbon battery negative electrode comprises the following components in parts by weight:

[0091] 10 parts of sulfuric acid,

[0092] 1.5 parts of barium sulfate,

[0093] 0.4 parts of humic acid,

[0094] 0.2 parts of polyester,

[0095] 5 parts of graphene nanoribbons,

[0096] 0.5 part of silane coupling agent,

[0097] 0.08 part of polycarboxylate,

[0098] Nano titanium dioxide 0.04 parts,

[0099] Nano silicon dioxide 0.08 parts,

[0100] 15 parts of pure water,

[0101] 80 parts of lead powder;

[0102] Wherein, the density of the sulfuric acid is 1.38g / mL; the specific surface area of ​​the graphene nanobelt is 430 ~ 500m 2 / g, the average pore diameter is less than 50nm;

[0103] According to the composition formula of above-mentioned lead-carbon battery negative pole, make following preparation:

[0104] (1) Premix barium sulfate, organic expansion agent, graphene nanobelts, short fibers, nano-titanium dioxide and nano-silicon dioxide for 5 m...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Densityaaaaaaaaaa
Specific surface areaaaaaaaaaaa
Average pore sizeaaaaaaaaaa
Login to view more

Abstract

The invention provides a cathode for lead-carbon batteries, a production method of the cathode and a battery made with the cathode. The cathode comprises, by weight, 8.5 to 10 parts of sulfuric acid, 0.5 to 1.5 parts of barium sulfate, 0.1 to 0.4 part of organic expander, 0.05 to 0.2 part of short fiber, 0.2 to 5 parts of graphene nanoribbon, 0.01 to 0.5 part of silane coupling agent, 0.05 to 0.08 part of dispersant, 10 to 15 parts of pure water, 0.06 to 0.12 part of nano-titanium dioxide and nano-silicon dioxide, and 70 to 80 parts of lead powder. Effective improvement is brought to both dynamic charge acceptance and cycle life of the battery made with the cathode.

Description

technical field [0001] The invention belongs to the technical field of lead-acid storage batteries, and in particular relates to a negative electrode of a lead-carbon battery, a preparation method thereof, and the prepared battery. Background technique [0002] With the development of electric vehicles and power batteries, lead-acid batteries have begun to be used in hybrid vehicles. In order to ensure high charging efficiency and sufficient power output, the batteries are often in a partially charged state. The failure of the battery used in this state is different from the conventional mode, mostly reflected in the irreversible sulfation of the negative electrode. Ideally, all lead sulfate and lead on the negative electrode undergo a completely reversible conversion during the battery charge-discharge cycle, but from a thermodynamic point of view, PbSO 4 Recrystallization will spontaneously reduce the surface area, there will always be a fraction of PbSO 4 Difficult to c...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): H01M4/14H01M4/20H01M4/21H01M4/62H01M10/06
CPCH01M4/14H01M4/20H01M4/21H01M4/62H01M10/06H01M2004/027H01M2220/20Y02E60/10
Inventor 张祖波李新禄夏诗忠张艳艳余萍
Owner 骆驼集团蓄电池研究院有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap