Manufacturing technology of colorful crystal toughened glass decoration panel having stereoscopic water drop effect

A tempered glass and three-dimensional effect technology, which is applied in decorative arts, printing technology, special decorative structures, etc., can solve the problems of unstable three-dimensional effect pattern quality, achieve flexible changes in shape and size, reduce production costs, and shorten the development cycle.

Inactive Publication Date: 2015-11-04
WUXI KEHONG LABEL
View PDF4 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In order to solve the above technical problems, the present invention provides a color crystal tempered glass decorative panel manufacturing process with three-dimensional effect of water drops, which solves the problem of unstable quality of three-dimensional effect patterns processed on hard materials such as tempered glass by screen printing

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] The invention provides a manufacturing process of a colored crystal tempered glass decorative panel with a three-dimensional effect of water drops, comprising the following steps:

[0018] a. Select the substrate made of tempered glass material and send it to the semi-automatic screen printing machine. According to the pattern shape that needs to be formed, plan the pattern area on the front of the substrate, and print transparent bumps on the pattern area with high-temperature resistant UV varnish, and then Curing by UV light curing machine, the lamp power of UV light curing machine is 80W / CM;

[0019] b. Send the substrate obtained in step a into a screen printing machine, and use water drop ink on the back of the substrate to print the dot layer by screen printing, and then send it into the light wave drying tunnel at a temperature of 170 ° C. 8 minutes drying process;

[0020] c. Send the substrate obtained in step b into a semi-automatic screen printing machine, a...

Embodiment 2

[0022] A manufacturing process of a colored crystal tempered glass decorative panel with a three-dimensional effect of water drops, comprising the following steps:

[0023] a. Select the substrate made of tempered glass material and send it to the semi-automatic screen printing machine. According to the pattern shape that needs to be formed, plan the pattern area on the front of the substrate, and print transparent bumps on the pattern area with high-temperature resistant UV varnish, and then Curing by UV light curing machine, the lamp power of UV light curing machine is 120W / CM;

[0024] b. Send the substrate obtained in step a into a screen printing machine, and use water drop ink on the back of the substrate to print the dot layer by screen printing, and then send it into the light wave drying tunnel at a temperature of 180 ° C. 6 minutes drying process;

[0025] c. Send the substrate obtained in step b into a semi-automatic screen printing machine, and still print a refle...

Embodiment 3

[0027] A manufacturing process of a colored crystal tempered glass decorative panel with a three-dimensional effect of water drops, comprising the following steps:

[0028] a. Select the substrate made of tempered glass material and send it to the semi-automatic screen printing machine. According to the pattern shape that needs to be formed, plan the pattern area on the front of the substrate, and print transparent bumps on the pattern area with high-temperature resistant UV varnish, and then Curing by UV light curing machine, the lamp power of UV light curing machine is 100W / CM;

[0029] b. Send the substrate obtained in step a into a screen printing machine, and use water drop ink on the back of the substrate to print the dot layer by screen printing, and then send it into the light wave drying tunnel at a temperature of 175°C. 7 minutes drying process;

[0030] c. Send the substrate obtained in step b into a semi-automatic screen printing machine, and still print a reflect...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a manufacturing technology of a colorful crystal toughened glass decoration panel having a stereoscopic water drop effect. According to the manufacturing technology disclosed by the invention, the adhesive force on a toughened glass material can be increased by adopting printing ink in a water drop shape, combining a screen printing technology and adding a UV (Ultraviolet) gloss oil bottom sizing agent, the problem of instable machining quality of screen printing on hard materials such as the toughened glass is solved, and the stereoscopic water drop effect can be generated; through a follow-up printing reflecting coating protection layer production technology, the production cost is reduced, and the production efficiency is increased; the manufacturing technology has the advantages that the development period is short, forming by making a manufacturing mold is not needed, individualized production is realized, the shape of products is flexible in size variation, and the appearance is attractive and elegant; the manufacturing technology is suitable for manufacturing decoration panels in the field of household appliances, domestic decoration and advertisement media.

Description

technical field [0001] The invention relates to the technical field of decorative panel manufacturing, in particular to a manufacturing process of a colored crystal tempered glass decorative panel with a three-dimensional effect of water drops. Background technique [0002] In the field of traditional decorative panel manufacturing, the three-dimensional effect is achieved by increasing the thickness of the photosensitive adhesive of the screen plate and thickening the printing ink. Because the photosensitive glue is too thick, it is difficult to expose the screen plate, it is not easy to develop, and the photosensitive glue is easy to fall off during production. [0003] Three-dimensional varnish ink uses the characteristics of good solid performance and strong transparency of the ink itself to achieve a three-dimensional effect. Due to the strong solidity of the ink itself, it is easy to stick to the screen during printing, and the ink will have bubbles, which makes print...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B44C5/04B44C1/16
Inventor 陈建平孙涛钱小玲
Owner WUXI KEHONG LABEL