Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

SY15MnNiCrMoVNbTi steel and preparing method of structural component of same

A technology for steel structural parts and forgings, which is applied in the field of preparation of SY15MnNiCrMoVNbTi steel structural parts, can solve the problems that the performance cannot meet higher performance requirements, and achieve the effects of meeting the needs of safe production, reducing replacement frequency and improving work efficiency

Active Publication Date: 2015-11-04
MCC SFRE HEAVY IND EQUIP
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to provide a SY15MnNiCrMoVNbTi steel, which solves the problem that the performance of low-carbon engineering structural steel in the prior art cannot meet higher performance requirements

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0059] Table 3-1 The final component actual value (%) of material embodiment 1 of the present invention

[0060] C

Embodiment 2

[0061] Table 3-2 The final component actual value (%) of material embodiment 2 of the present invention

[0062] C

Embodiment 3

[0063] Table 3-3 The final component actual value (%) of material embodiment 3 of the present invention

[0064] C

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses SY15MnNiCrMoVNbTi steel. The SY15MnNiCrMoVNbTi steel consists of the following components in percents by mass: 0.16-0.20 of C, 0.20-0.50 of Si, 1.40-1.60 of Mn, smaller than or equal to 0.025 of P, smaller than or equal to 0.025 of S, 1.00-1.20 of Cr, 0.40-0.60 of Mo, 1.30-1.50 of Ni, 0.05-0.10 of V, 0.03-0.06 of Nb, 0.02-0.20 of Ti, smaller than or equal to 0.006 of B and the balance of Fe, wherein the sum is 100%. The invention further discloses a preparing method of the structural component of the SY15MnNiCrMoVNbTi steel. The material and the steel structural component reach mechanical performance meeting design requirements through adjusting alloy elements and adopting a reasonable thermal treatment technology, so that the requirement on the work environment in which the steel structural component is positioned is met; and the performance indexes of the steel structural component, such as strength, rigidity, stability, cold and hot processing moldability and weldability, are improved, and the service life of the steel structural component is prolonged.

Description

technical field [0001] The invention belongs to the technical field of the metallurgical industry, relates to a SY15MnNiCrMoVNbTi steel, and also relates to a preparation method of the SY15MnNiCrMoVNbTi steel structure. Background technique [0002] In the metallurgical industry, with the development of metallurgical technology, the lack of mineral resources and the development of steel structural parts from riveting technology to welding technology, a class of weldable low-carbon engineering structural steel has gradually emerged. This type of steel has excellent mechanical properties such as lower carbon content, higher yield point or yield strength, better cold and hot forming and good weldability than ordinary carbon structural steel. This type of steel is mainly used in oil and gas transmission pipelines, deep well oil pipes, automobile steel plates, coal mining machinery, construction machinery and other fields. It has great advantages, especially in large-span or hea...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C38/58C22C38/54C22C38/50C22C33/04C21D8/00
Inventor 杜佳王亚锋朱朋祥陈阳李钊库史雷刚王耀琨
Owner MCC SFRE HEAVY IND EQUIP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com