Fibrillar silicate-reinforced super thermal-insulation heat-preserving paint and preparation method thereof

A thermal insulation, silicate technology, applied in chemical instruments and methods, coatings, silicon compounds, etc., can solve the problems of uneven dispersion of aerogel microspheres, performance degradation of composite materials, large interface thermal resistance, etc. The effect of reducing moisture absorption and breaking, increasing bonding strength and increasing strength

Inactive Publication Date: 2015-11-11
DANGTU COUNTY KEHUI TRADING
View PDF6 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Overhydrophobic silica airgel microspheres are a good thermal insulation material, but due to the large number of non-polar groups on its surface, when it is mixed with a water-based polymer system, its compatibility is poor and the interface thermal resistance is large At the same time, the airgel microspheres are unevenly dispersed and easily agglomerated, resulting in a decrease in the performance of the composite material. Therefore, it is necessary to properly modify the hydrophobic silica airgel microspheres

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0016] A needle-shaped silicate-reinforced super thermal insulation coating, made of the following raw materials in parts by weight (kg): Tetraethyl orthosilicate 36, appropriate amount of hydrochloric acid, appropriate amount of ammonia water, appropriate amount of ethanol, appropriate amount of deionized water, vinyl trimethyl Oxysilane 1.5, dimethyldiethoxysilane 2.8, 3-aminopropyl trihydroxysilane 1, phenolic resin 0.6, nanometer calcium carbonate 0.3, acicular silicate 0.7, E-12 epoxy resin 73, ethyl Diol diglycidyl ether 11, triethanolamine 7.4;

[0017] The preparation method of the acicular silicate-enhanced super thermal insulation coating comprises the following steps:

[0018] (1) Add phenolic resin to 3.5 parts by weight of ethanol, stir until dissolved, then add acicular silicate and nano-calcium carbonate, stir evenly, heat to 75°C, and react for 13 minutes to obtain a mixed material;

[0019] (2) Add tetraethyl orthosilicate: ethanol: water into the container i...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention provides a fibrillar silicate-reinforced super thermal-insulation heat-preserving paint. The paint is prepared from the following raw materials by weight: 34 to 38 parts of ethyl orthosilicate, a proper amount of hydrochloric acid, a proper amount of ammonia water, a proper amount of ethanol, a proper amount of deionized water, 1 to 2 parts of vinyltrimethoxy silane, 2.5 to 3 parts of dimethyldiethoxylsilane, 0.8 to 1.2 parts of 3-aminopropyltrihydroxysilane, 0.5 to 0.8 part of phenolic resin, 0.2 to 0.4 part of nanometer calcium carbonate, 0.6 to 0.9 part of fibrillar silicate, 70 to 75 parts of epoxy resin E-12, 9 to 12 parts of ethylene glycol diglycidylether and 7 to 7.5 parts of triethanolamine. According to the invention, through hydrophobic modification of aerogel, the phenomenon of fragmentation of the aerogel due to moisture absorption is reduced; and through hydrophilic modification, bonding strength between the aerogel and a film forming agent is improved.

Description

technical field [0001] The invention relates to the field of thermal insulation coatings, in particular to an acicular silicate reinforced super thermal insulation coating and a preparation method thereof. Background technique [0002] Silica airgel has nanopores and is a porous solid material with low density, high porosity and super thermal insulation properties. The combination of silica airgel microspheres and film-forming materials for coatings forms a coating with super thermal insulation properties. [0003] Most of the current silica aerogels are prepared by hydrolysis of silicon sources such as tetraethyl orthosilicate by using the sol-gel method. The silica aerogels thus obtained are very easy to absorb moisture and crack when exposed to water, resulting in a nanoporous structure. If it is destroyed, it will affect the performance of airgel. Therefore, in the preparation process, it is usually necessary to carry out necessary hydrophobic modification on silica gel...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D161/06C09D7/12C01B33/155C01B33/157
Inventor 董良清
Owner DANGTU COUNTY KEHUI TRADING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products