Cold roller for rolling stainless steel plates, and preparation method of cold roller
A technology of stainless steel plate and cold rolling roll, applied in the field of cold rolling roll for rolling stainless steel plate and its preparation, can solve the problems of increased use cost, early crack of roll, large deformation resistance, etc. Effects of heat treatment stress
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0014] Example one
[0015] The composition and weight percentage of the cold roll are: C: 0.67%; Si: 0.38%; Mn: 0.63%; Cr: 3.3%; Ni: 0.46%; Mo: 0.23%; S, P≤0.015; the rest It is Fe and inevitable impurity elements. The steps of the preparation method of the cold roll for rolling stainless steel plate include: (1) making the roll blank according to the above chemical composition scheme, and the quality of the roll blank is qualified; (2) performing rough processing and tempering heat treatment on the roll blank; (3) Semi-finish the roll blank according to the requirements of the drawings, fine-grind the roll body and conduct ultrasonic flaw detection; (4) Carry out high-temperature induction hardening on the roll body, the quenching temperature is 940℃; (5) Perform -80 on the quenched roll immediately Cryogenic treatment at ℃; (6) Tempering the cold-treated roll with a tempering holding temperature of 170℃; (7) Final finishing to obtain a finished roll, the surface hardness of t...
Example Embodiment
[0016] Example two
[0017] The composition and weight percentage of the cold roll are: C: 0.72%; Si: 0.55%; Mn: 0.67%; Cr: 3.32%; Ni: 0.53%; Mo: 0.31%; S: 0.009%; P: 0.013%; the rest is Fe and unavoidable impurity elements. The steps of the preparation method of the cold roll for rolling stainless steel plate include: (1) making the roll blank according to the above chemical composition scheme, and the quality of the roll blank is qualified; (2) performing rough processing and tempering heat treatment on the roll blank; (3) Semi-finish the roll blank according to the requirements of the drawings, finely grind the roll body and conduct ultrasonic flaw detection; (4) Carry out high-temperature induction hardening on the roll body, and the quenching temperature is 945℃; (5) Perform immediately -90 on the quenched roll Cryogenic treatment at ℃; (6) Tempering the cold-treated roll with a tempering temperature of 175°C; (7) Final finishing to obtain a finished roll. The surface hardn...
Example Embodiment
[0018] Example three
[0019] The composition and weight percentage of the cold roll are: C: 0.68%; Si: 0.43%; Mn: 0.72%; Cr: 3.45%; Ni: 0.45%; Mo: 0.26%; S: 0.006%; P: 0.015%; the rest is Fe and inevitable impurity elements. The steps of the preparation method of the cold roll for rolling stainless steel plate include: (1) making the roll blank according to the above chemical composition scheme, and the quality of the roll blank is qualified; (2) performing rough processing and tempering heat treatment on the roll blank; (3) Semi-finish the roll blank according to the requirements of the drawings, finely grind the roll body and conduct ultrasonic flaw detection; (4) Carry out high-temperature induction hardening on the roll body, and the quenching temperature is 930℃; (5) Perform -85 immediately on the quenched roll Cryogenic treatment at ℃; (6) Tempering the cold-treated roll with a tempering temperature of 165°C; (7) Final finishing to obtain a finished roll, the surface hard...
PUM
Property | Measurement | Unit |
---|---|---|
Surface hardness | aaaaa | aaaaa |
Surface hardness | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap